激光熔覆FeCrNiCoCuAl_x高熵合金涂层的耐腐蚀与抗冲蚀性能
Corrosion and slurry erosion properties of FeCrNiCoCuAl_x high-entropy alloy coatings prepared by laser cladding
查看参考文献28篇
|
文摘
|
采用激光熔覆技术在Q345钢表面制备FeCrNiCoCuAl_x(x=0,1,2,3)高熵合金涂层。通过XRD,SEM及冲蚀磨损等实验方法研究高熵合金涂层的组织结构与性能。结果表明:随着Al含量的增加,高熵合金涂层由简单结构的FCC和BCC混合固溶体逐渐转变成全部的BCC结构,涂层的硬度也随之增大,最高可达580HV。在3.5%NaCl溶液中,涂层的腐蚀电流密度随着Al含量的增加先降低后提高,且当x=1时涂层具有最好的耐蚀性。冲蚀磨损实验表明,当冲蚀角度由90°减小到30°时,冲蚀磨损量不降反升,表现出韧性材料的冲蚀特征。涂层的抗冲蚀性能随着Al含量的增加而增强,且冲蚀磨损机制由锻造挤压转变为以微切削和犁削为主。 |
|
其他语种文摘
|
FeCrNiCoCuAl_x(x=0,1,2,3)high-entropy alloy(HEA)coatings were prepared on Q345 steel by laser cladding.The effects of Al content on microstructure and properties of FeCrNiCoCuAl_x HEA coatings were studied by XRD,SEM and erosion wear tests.The results show that the HEA coatings are mainly composed by simple FCC and BCC solid-solution phases.With the increase of Al addition,the microstructure is evolved gradually from FCC to BCC.And the hardness of the HEA coatings improves significantly and the maximum value is 580HV.In 3.5%NaCl solution,the corrosion current density of FeCrNiCoCuAl_x HEA coatings decreases firstly and then increases with the increase of Al addition.And the HEA coating has the best corrosion resistance at x =1. Meanwhile,the mass loss rate of HEA coating decreases in the erosion test when the impact angle is changed from 90°to 30°,exhibiting an erosion characteristic of ductile materials.The slurry erosion properties of the HEA coating increase with the increase of Al content,and the erosion wear mechanism is evolved from forging extrusion to ploughing and micro-cutting. |
|
来源
|
材料工程
,2019,47(11):141-147 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2018.000065
|
|
关键词
|
激光熔覆
;
高熵合金
;
组织结构
;
耐蚀性
;
冲蚀磨损
|
|
地址
|
1.
河海大学机电工程学院, 江苏, 常州, 213022
2.
河海大学, 疏浚技术教育部工程研究中心, 江苏, 常州, 213022
3.
河海大学力学与材料学院, 南京, 210098
4.
常熟浦发第二热电能源有限公司, 江苏, 苏州, 215513
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金面上项目
;
中央高校基本科研业务费专项资金
;
江苏省普通高校学术学位研究生创新计划项目
|
|
文献收藏号
|
CSCD:6616651
|
参考文献 共
28
共2页
|
|
1.
Singh S. Decomposition in multi-component AlCoCrCuFeNi high-entropy alloy.
Acta Materialia,2011,59:182-190
|
CSCD被引
66
次
|
|
|
|
|
2.
Zhang Y. Microstructures and properties of high-entropy alloys.
Progress in Materials Science,2014,61:1-93
|
CSCD被引
671
次
|
|
|
|
|
3.
梁秀兵. 高熵合金新材料的研究进展.
材料工程,2009(12):75-79
|
CSCD被引
39
次
|
|
|
|
|
4.
高家诚. 高熵合金研究的新进展.
功能材料,2008,39(7):1059-1061
|
CSCD被引
20
次
|
|
|
|
|
5.
Wu W H. Industrial development of highentropy alloys.
European Journal of Control,2006,31(6):737-747
|
CSCD被引
2
次
|
|
|
|
|
6.
刘宁. 激光熔覆技术制备高熵合金涂层的研究进展.
材料导报,2014,28(3):133-134
|
CSCD被引
10
次
|
|
|
|
|
7.
Zhang H. Microstructural control and properties of 6FeNiCoSiCrAlTi high-entropy alloy coating prepared by laser cladding.
Applied Surface Science,2011,257:2259-2263
|
CSCD被引
49
次
|
|
|
|
|
8.
马明星. 激光制备Al_xCoCrNiMo高熵合金涂层的研究.
应用激光,2010,30(6):433-437
|
CSCD被引
22
次
|
|
|
|
|
9.
黄祖凤. WC颗粒对激光熔覆FeCoCrNiCu高熵合金涂层组织与硬度的影响.
中国表面工程,2013,26(1):13-19
|
CSCD被引
29
次
|
|
|
|
|
10.
刘永长. 激光熔覆技术的研究现状.
粉末冶金技术,1998,16(3):209-212
|
CSCD被引
12
次
|
|
|
|
|
11.
张晖. 激光熔覆BCC结构高硬度高断裂韧性高熵合金涂层.
第十次全国热处理大会论文集,2011:676-679
|
CSCD被引
1
次
|
|
|
|
|
12.
翁子清. 退火对激光熔覆FeCrNiCoMn高熵合金涂层组织与性能的影响.
中国激光,2014,41(3):59-64
|
CSCD被引
15
次
|
|
|
|
|
13.
Yeh J W. Nanostructured high-entropy alloys with multiple principal elements:novel alloy design concepts and outcomes.
Advanced Engineering Materials,2004,6(5):299-303
|
CSCD被引
1460
次
|
|
|
|
|
14.
Zhuang Y X. Effect of elemental interaction on microstructure and mechanical properties of Fe-CoNiCuAl alloys.
Materials Science & Engineering:A,2012,556:395-399
|
CSCD被引
11
次
|
|
|
|
|
15.
Raghavan R. Analysis of phase formation in multi-component alloys.
Journal of Alloys and Compounds,2012,544:152-158
|
CSCD被引
9
次
|
|
|
|
|
16.
Pi J H. Thermodynamic analysis for microstructure of high-entropy alloys.
Rare Metal Materials and Engineering,2013,42(2):232-237
|
CSCD被引
8
次
|
|
|
|
|
17.
安旭龙. 碳化钨对激光熔覆高熵合金的影响.
强激光与粒子束,2014,26(12):129001
|
CSCD被引
8
次
|
|
|
|
|
18.
邱星武. 激光熔覆法制Al_2CrFeCo_xCuNiTi高熵合金涂层的组织与性能.
粉末冶金材料科学与工程,2013,18(5):735-740
|
CSCD被引
27
次
|
|
|
|
|
19.
王艳苹.
AlCrFeCoNiCu系多主元合金及其复合材料的组织与性能,2009
|
CSCD被引
7
次
|
|
|
|
|
20.
Fleischer R L. Statistics of stabilities of ternary elements in intermetallic compounds.
Journal of Material Science Letter,1988,7(5):525-526
|
CSCD被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问