Li_(3-2x)B_(1-x)N_xO_3 (x=0.1, 0.2, 0.3)锂离子固体电解质的制备和性能
Preparation and Characterization of Li_(3-2x)B_(1-x)N_xO_3 (x=0.1, 0.2, 0.3) Solid Electrolytes
查看参考文献17篇
|
文摘
|
以硝酸锂、碳酸锂、氧化硼为原料,采用固相法制备得到了Li_(3-2x)B_(1-x)N_xO_3 (x=0.1, 0.2, 0.3)锂离子固体电解质,通过无压烧结制备得到固体电解质片,并通过X射线衍射(XRD)、扫描电子显微镜(SEM)、电化学交流阻抗(EIS)对Li_(3-2x)B_(1-x)N_xO_3固态电解质进行了表征。结果表明:当x=0.2时,采用无压烧结在600 ℃烧结10 h制备得到的固体电解质片致密度最高,达到理论密度的90.07%,室温锂离子总电导率也最大,为6.37×10~(-6) S/cm,此时激活能值最小,为0.48 eV。 |
|
其他语种文摘
|
The Li_(3-2x)B_(1-x)N_xO_3 (x=0.1, 0.2, 0.3) compound with pure phase were prepared by solid phase method with lithium nitrate, lithium carbonate and boron oxide as the raw materials. The Li_(3-2x)B_(1-x)N_xO_3 precursor powders were sintered via pressureless sintering, and the Li_(3-2x)B_(1-x)N_xO_3 solid electrolytes were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS). The results show that the Li_(2.6)B_(0.8)N_(0.2)O_3 sintered at 600 °C for 10 h by the pressureless sintering shows the highest density, reaching 90.07% of theoretical density, the highest total conductivity of 6.37×10~(-6) S/cm, and the lowest activation energy 0.48 eV at 250~390 K. |
|
来源
|
稀有金属材料与工程
,2018,47(12):3835-3838 【核心库】
|
|
关键词
|
固相法
;
固体电解质
;
锂离子电导率
|
|
地址
|
1.
中国科学院西安光学精密机械研究所, 瞬态光学与光子技术国家重点实验室, 陕西, 西安, 710119
2.
中国科学院大学, 北京, 100049
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
电工技术 |
|
基金
|
陕西省工业科技攻关项目
|
|
文献收藏号
|
CSCD:6397944
|
参考文献 共
17
共1页
|
|
1.
Shin R H.
Solid State Ionics,2017,301:10
|
CSCD被引
6
次
|
|
|
|
|
2.
Takada K.
Acta Mater,2013,61(3):759
|
CSCD被引
40
次
|
|
|
|
|
3.
Tatsumisago M.
J Asian Ceram Soc,2013,1(1):17
|
CSCD被引
20
次
|
|
|
|
|
4.
刘美景. 溶胶-凝胶法制备NASICON型Li_(1.15)Y_(0.15)Zr_(1.85)(PO_4)_3固态电解质.
硅酸盐学报,2015,43(3):276
|
CSCD被引
2
次
|
|
|
|
|
5.
Chiang Y M.
Science,2010,330(6010):1485
|
CSCD被引
47
次
|
|
|
|
|
6.
Hong H Y P.
Mat Res Bull,1978,13(2):117
|
CSCD被引
20
次
|
|
|
|
|
7.
Mei A.
Electrochimica Acta,2010,55(8):2958
|
CSCD被引
10
次
|
|
|
|
|
8.
Thangadurai V.
Chem Mater,2004,16:2998
|
CSCD被引
8
次
|
|
|
|
|
9.
Goodenough J B.
Mat Res Bull,1976,11(2):203
|
CSCD被引
87
次
|
|
|
|
|
10.
He M.
Journal of Solid State Chemistry,2005,178(3):680
|
CSCD被引
1
次
|
|
|
|
|
11.
Ohta S.
Journal of Power Sources,2013,238:53
|
CSCD被引
30
次
|
|
|
|
|
12.
Tatsumisago M.
Journal of Power Sources,2014,270:603
|
CSCD被引
3
次
|
|
|
|
|
13.
Kim J M.
Journal of Power Sources,2009,189(1):211
|
CSCD被引
7
次
|
|
|
|
|
14.
Chan H W.
Electrochimica Acta,2006,51(18):3645
|
CSCD被引
5
次
|
|
|
|
|
15.
Lim S N.
Electrochimica Acta,2014,136:1
|
CSCD被引
10
次
|
|
|
|
|
16.
Chan H W.
Surface & Coatings Technology,2004,188/189:116
|
CSCD被引
3
次
|
|
|
|
|
17.
Sahan H.
Solid State Ionics,2008,178(35/36):1837
|
CSCD被引
13
次
|
|
|
|
|
了解气象卫星更多信息，请访问