Al对GH4169合金冲击性能的影响
Effect of Al on impact strength of GH4169 alloy
查看参考文献14篇
|
文摘
|
研究了Al对GH4169合金晶界相的析出和冲击性能的影响.结果表明,提高Al含量可抑制晶界δ相的析出,促进晶界Laves相、M_7C_3相和σ相等有害相的析出;随着Al含量的提高,GH4169合金的室温冲击性能明显降低,冲击断口由穿晶型转变为沿晶型.提高Al含量所导致的Laves相等有害脆性相的析出降低了晶界强度,使晶界裂纹更容易萌生和扩展,降低了GH4169合金的冲击韧性. |
|
其他语种文摘
|
The effect of Al on the grain boundary precipitation and impact toughness of GH4169 alloy was investigated.The delta phase precipitation at the grain boundaries is noticeably suppressed due to the increasing Al addition,and some harmful phases including Laves phase,M_7C_3 carbide and sigma phase are formed intergranularly.As a result,the 'U' notch impact energy is largely decreased.The cracks incline to be initiated and propagated at the carbides and other harmful phases precipitated along the grain boundaries,and hence the fracture energy of the alloy with higher Al contents is reduced. |
|
来源
|
材料研究学报
,2008,22(3):230-234 【核心库】
|
|
关键词
|
金属材料
;
GH4169
;
Al
;
M7C3碳化物
;
Laves相
;
σ相
;
沿晶断裂
|
|
地址
|
1.
东北大学材料与冶金学院, 辽宁, 沈阳, 110004
2.
中国科学院金属研究所, 辽宁, 沈阳, 110016
3.
东北特钢集团, 抚顺, 113001
4.
贵州安大航空锻造有限责任公司技术中心, 安顺, 561005
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3093 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:3323499
|
参考文献 共
14
共1页
|
|
1.
R Cozar. Morphology ofγ'andγprecipitates and thermal stability of Inconel 718 type alloys.
Metall. Trans.,1973,4:47
|
CSCD被引
30
次
|
|
|
|
|
2.
J P Collier. The effect of varying Al, Ti and Nb content on the phase stability of Inconel 718.
Metall. Trans.,1988,19:1657
|
CSCD被引
24
次
|
|
|
|
|
3.
J X Dong. Influence of associated and separated precipitation ofγandγ'on structure stability in Inconel 718 and modified alloys.
Acta Metallurgica Sinica(English Letters),1993,6:410
|
CSCD被引
1
次
|
|
|
|
|
4.
J X Dong. Enhancement of thermal structure stability in a Ni-base superalloy.
Scripta Metallurgica,1993,28:1477
|
CSCD被引
3
次
|
|
|
|
|
5.
E Guo. Further studies on thermal stability.
Superalloys 718, 625, 706 and Various Derivatives,1994:721
|
CSCD被引
1
次
|
|
|
|
|
6.
F Q Xu. Thermal stability of modified 718 alloys aged for 2000 hours at 700℃.
Superalloys 718,625,706 and Various Derivatives,1997:503
|
CSCD被引
1
次
|
|
|
|
|
7.
W D Cao. Improving stress ruptrue life of alloy 718 by optimizing Al, Ti, P and B contents.
Superalloys 718, 625, 706 and Various Derivatives,2001:477
|
CSCD被引
3
次
|
|
|
|
|
8.
谢锡善. γ↑"和γ↑’复合析出强化新型镍基高温合金的研究.
金属热处理学报,1997,18(3):37
|
CSCD被引
9
次
|
|
|
|
|
9.
X S Xie. The effect of Nb, Ti, Al on precipitation and strengthening behavior of 718 type superalloys.
Superalloys 718,2005:287
|
CSCD被引
1
次
|
|
|
|
|
10.
《中国航空材料手册》编辑委员会.
中国航空材料手册, 第二卷变形高温合金铸造高温合金,2002
|
CSCD被引
1
次
|
|
|
|
|
11.
付书红.
第十一届中国高温合金年会论文集,2007:151
|
CSCD被引
1
次
|
|
|
|
|
12.
黄乾尧.
高温合金,2000:47
|
CSCD被引
2
次
|
|
|
|
|
13.
A K Jena. Role of alloying elements in the design of Nickel-base superalloys.
Journal of Materials Science,1984,19(10):3121
|
CSCD被引
23
次
|
|
|
|
|
14.
宋洪伟.
磷对IN718合金组织演化和力学性能的影响博士学位论文],1999
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问