DD8单晶镍基高温合金热机械疲劳后γ/γ′界面位错网产生内应力的计算
CALCULATION OF THE INTERNAL STRESSES AT THE γ/γ′ INTERFACE OF DD8 SINGLE CRYSTAL NICKEL BASE SUPERALLOY AFTER THERMOMECHANICAL FATIGUE
查看参考文献17篇
|
文摘
|
计算了DD8单晶镍基高温合金在同相(IP)和反相(OP)热机械疲劳(TMF)后γ/γ′相界面上产生的位错网的内应力.结果表明:IP TMF条件下,γ/γ′相界面上产生的位错网可以释放掉大部分错配应力,同时因位错网的存在导致了γ′沉淀相发生了明显的筏化现象.OP条件下产生的层错未造成基体内应力分布的不同,因此未发生γ′沉淀相的筏化. |
|
其他语种文摘
|
The internal stresses produced by dislocation networks at the 7/7' interfaces in a single crystal nickel-base superalloy DD8 has been studied after in phase (IP) and out of phase (OP) thermo-mechanical fatigue (TMF) testing. The results indicate that one of the roles of the dislocation networks at the 7/7' interfaces is to relax most of the misfit stress under IP TMF, on the other hand, the existence of the dislocation networks results in the directional coarsening of the 7' precipitates. While under the OP TMF, the internal stress in the matrix induced by stacking faults does not vary significantly, the 7' precipitates do not show direction coarsening in OP test. |
|
来源
|
金属学报
,2005,41(3):245-250 【核心库】
|
|
关键词
|
单晶镍基高温合金
;
热机械疲劳
;
位错网,γ/γ′界面
;
内应力
|
|
地址
|
中国科学院金属研究所, 沈阳材料科学国家(联合)实验室, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:2018704
|
参考文献 共
17
共1页
|
|
1.
Weatherly G C. Philos Mag.
Philos Mag,1968,17:801
|
CSCD被引
3
次
|
|
|
|
|
2.
Lesalmonie A. Philos Mag.
Philos Mag,1975,32:937
|
CSCD被引
2
次
|
|
|
|
|
3.
Zhang J H. Metall Trans.
Metall Trans. A,1992,23:1253
|
CSCD被引
12
次
|
|
|
|
|
4.
Zhang J X. Metall Mater Trans.
Metall Mater Trans. A,2002,33:3741
|
CSCD被引
45
次
|
|
|
|
|
5.
Gabrisch H. Philos Mag.
Philos Mag. A,1996,74:229
|
CSCD被引
11
次
|
|
|
|
|
6.
Gabb T P. Mater Sci Eng.
Mater Sci Eng. A,1989,118:59
|
CSCD被引
23
次
|
|
|
|
|
7.
王跃臣. 同位相热机械疲劳形变后γ/γ'相界面上的位错网分析.
金属学报,2003,39:237
|
CSCD被引
2
次
|
|
|
|
|
8.
王跃臣. 单晶镍基高温合金DD8反位相热机械疲劳后的层错.
金属学报,2003,39:150
|
CSCD被引
2
次
|
|
|
|
|
9.
Carry C. Metall Trans.
Metall Trans. A,1979,10:855
|
CSCD被引
2
次
|
|
|
|
|
10.
Scheunemann-Frerker G. Scheunemann-Frerker G.
Philos Mag. A,1993,68:193
|
CSCD被引
2
次
|
|
|
|
|
11.
Probst-Hein M. Acta Mater.
Acta Mater,1999,47:2497
|
CSCD被引
13
次
|
|
|
|
|
12.
Zhou L. Z Metallkd.
Z Metallkd,2002,4:315
|
CSCD被引
4
次
|
|
|
|
|
13.
Zhou L. Mater Sci Eng.
Mater Sci Eng. A,2003,352:300
|
CSCD被引
6
次
|
|
|
|
|
14.
Kraft S. Scr Metall Mater.
Scr Metall Mater,1995,32:411
|
CSCD被引
6
次
|
|
|
|
|
15.
Mardhand N. ASTM STP 942.
ASTM SIP 942,1988:638
|
CSCD被引
1
次
|
|
|
|
|
16.
Carry C. Acta Metall.
Acta Metall,1977,25:767
|
CSCD被引
8
次
|
|
|
|
|
17.
Buffiere J Y. Scr Metall Mater.
Scr Metall Mater,1996,34:349
|
CSCD被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问