试样疲劳性能尺度效应的概率控制体积方法
PROBABILISTIC CONTROL VOLUME METHOD FOR THE SIZE EFFECT OF SPECIMEN FATIGUE PERFORMANCE
查看参考文献31篇
|
文摘
|
试样尺度、缺口和加载方式通常对材料的疲劳性能具有重要影响.因此,发展关联试样尺度、缺口和加载方式对疲劳强度影响的方法对于从材料疲劳性能到结构件疲劳性能的预测具有重要意义.首先,采用旋转弯曲加载和轴向加载方式对不同几何形状EA4T车轴钢试样进行了疲劳实验.实验结果表明,由于试样尺度的增加,轴向加载下狗骨形试样的疲劳强度明显低于沙漏形试样;相同寿命下,缺口显著降低试样的疲劳强度.疲劳断口扫描电镜观测结果表明,疲劳裂纹均起源于试样表面.沙漏形试样和狗骨形试样疲劳断口大多只有一个裂纹源,而缺口试样疲劳断口均具有多裂纹源特征.然后,采用概率控制体积方法研究了试样尺度、缺口和加载方式对疲劳强度的影响,并与临界距离和应变能密度方法进行了比较.结果表明,概率控制体积方法能够更好地关联试样尺度、缺口和加载方式对EA4T车轴钢疲劳强度的影响.最后,提出一种基于控制体积的结构件疲劳强度预测方法,并用于具有不连续高应力区域车轴钢试样的疲劳强度预测,预测结果与实验结果吻合. |
|
其他语种文摘
|
The effects of specimen size, notch and loading type usually have important influence on the fatigue properties of metallic materials. Therefore, it is vital to modelling the effects of specimen size, notch and loading type on the fatigue strength, which is of great importance for predicting the fatigue property of the structural parts from that of the materials. In this work, rotating bending and axial loading fatigue tests are first performed on the specimens of an EA4T axle steel with different shapes. Experimental results indicate that the fatigue strength of the dogbone specimen is lower than that of the hourglass specimen due to the increase of the specimen size, and the notch reduces the fatigue strength of the specimen in terms of the nominal stress due to the large stress gradient at the notch root. The fracture surface observation by the scanning electron microscope indicates that all the tested specimens fail from the surface of the specimen. For hourglass and dogbone specimens, most of the fracture surfaces only have single crack initiation site, while for the notched specimen all the fracture surfaces have the characteristic of multiple crack initiation sites. Then, the probabilistic control volume method is used for correlating the effects of specimen size, notch and loading type on the fatigue strength of the EA4T steel, which is also compared with the critical distance method and the strain energy density method. It is indicated that the probabilistic control volume method gives better predictions for correlating the effects of specimen size, notch and loading type on the fatigue strength of the EA4T steel. Finally, a method based on the control volume is proposed for predicting the fatigue strength of structural parts, and is used for the specimens of axle steel with discontinuous highly stressed regions. The predicted results are in agreement with the experimental data. |
|
来源
|
力学学报
,2019,51(5):1363-1371 【核心库】
|
|
DOI
|
10.6052/0459-1879-19-118
|
|
关键词
|
EA4T车轴钢
;
尺度效应
;
缺口效应
;
加载方式
;
疲劳强度
;
控制体积方法
|
|
地址
|
1.
中车青岛四方机车车辆股份有限公司工程实验室, 山东, 青岛, 266111
2.
中国科学院力学研究所, 非线性力学国家重点实验室, 北京, 100190
3.
中国科学院大学工程科学学院, 北京, 100049
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0459-1879 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
中国科学院战略性先导科技专项
;
中国铁路总公司科技研究开发计划课题
|
|
文献收藏号
|
CSCD:6580939
|
参考文献 共
31
共2页
|
|
1.
高江平. 三剪应力统一强度理论研究.
力学学报,2017,49(6):1322-1334
|
CSCD被引
15
次
|
|
|
|
|
2.
万征. 一种横观各向同性强度准则及变换应力空间.
力学学报,2018,50(5):1168-1184
|
CSCD被引
5
次
|
|
|
|
|
3.
Xu W. Failure criterion of titanium alloy irregular sheet specimens for vibration-based bending fatigue testing.
Engineering Fracture Mechanics,2018,195:44-56
|
CSCD被引
5
次
|
|
|
|
|
4.
文龙飞. 动载下裂纹应力强度因子计算的改进型扩展有限元法.
力学学报,2018,50(3):599-610
|
CSCD被引
15
次
|
|
|
|
|
5.
Furuya Y. Specimen size e ects on gigacycle fatigue properties of high-strength steel under ultrasonic fatigue testing.
Scripta Materialia,2008,58:1014-1017
|
CSCD被引
5
次
|
|
|
|
|
6.
Shirani M. Fatigue life distribution and size e ect in ductile cast iron for wind turbine components.
Engineering Failure Analysis,2011,18:12-24
|
CSCD被引
10
次
|
|
|
|
|
7.
Beretta S. Probabilistic fatigue assessment for railway axles and derivation of a simple format for damage calculations.
International Journal of Fatigue,2016,86:13-23
|
CSCD被引
8
次
|
|
|
|
|
8.
Chen S. Fatigue strengths of the 54SiCr6 steel under di erent cyclic loading conditions.
Acta Metallurgica Sinica,2009,45:428-433
|
CSCD被引
1
次
|
|
|
|
|
9.
Nakajima M. E ect of loading condition on very high cycle fatigue behavior in a high strength steel.
International Journal of Fatigue,2010,32:475-480
|
CSCD被引
7
次
|
|
|
|
|
10.
Hu Y. E ects of loading frequency and loading type on high-cycle and very-high-cycle fatigue of a high-strength steel.
Materials,2018,11:1456
|
CSCD被引
7
次
|
|
|
|
|
11.
Lanning D B. On the use of critical distance theories for the prediction of the high cycle fatigue limit stress in notched Ti-6Al-4V.
International Journal of Fatigue,2005,27:45-57
|
CSCD被引
15
次
|
|
|
|
|
12.
Akiniwa Y. Notch e ect on fatigue strength reduction of bearing steel in the very high cycle regime.
International Journal of Fatigue,2006,28:1555-1565
|
CSCD被引
16
次
|
|
|
|
|
13.
Sun C. E ects of specimen size on fatigue life of metallic materials in high-cycle and very-high-cycle fatigue regimes.
Fatigue & Fracture of Engineering Materials &Structures,2016,39:770-779
|
CSCD被引
3
次
|
|
|
|
|
14.
Wang R. A combined critical distance and highlystressed-volume model to evaluate the statistical size e ect of the stress concentrator on low cycle fatigue of TA19 plate.
International Journal of Fatigue,2017,95:8-17
|
CSCD被引
6
次
|
|
|
|
|
15.
Leitner M. Statistical size e ect on multiaxial fatigue strength of notched steel components.
International Journal of Fatigue,2017,104:322-333
|
CSCD被引
3
次
|
|
|
|
|
16.
Sun C. A method for evaluating the e ects of specimen geometry and loading condition on fatigue life of metallic materials.
Materials Research Express,2019,6:046536
|
CSCD被引
2
次
|
|
|
|
|
17.
Neuber H.
Theory of Notch Stresses: Principles for Exact Calculation of Strength with Reference to Structural Form and Material. 2nd Ed,1958
|
CSCD被引
4
次
|
|
|
|
|
18.
Peterson R E. Notch sensitivity.
Metal Fatigue,1959:293-306
|
CSCD被引
11
次
|
|
|
|
|
19.
Kuguel R A. A relation between theoretical stress concentration factor and fatigue notch factor deduced from the concept of highly stressed volume.
ASTM Proc,1961,61:732-748
|
CSCD被引
2
次
|
|
|
|
|
20.
Murakami Y. Mechanism of fatigue failure in ultralong life regime.
Fatigue & Fracture of Engineering Materials & Structures,2002,25:735-746
|
CSCD被引
46
次
|
|
|
|
|
了解气象卫星更多信息，请访问