表面疏水性纳米TiO2颗粒的制备及光催化性能
The synthesis of hydrophobic nano-TiO2 powder and its photocatalytic property
查看参考文献17篇
|
文摘
|
在70℃水解钛酸四丁酯(TBOT)时加入十二烷基硫酸钠(SDS),无需热处理就能得到准球形锐钛矿结构的纳米TiO2.这种TiO2粉具有强疏水性,漂浮于水溶液的表面,可通过过滤手段与溶液分离.应用透射电子显微镜和X射线衍射仪对TiO2粉进行了形貌观察和晶体结构的测定.研究了反应体系pH值的变化对TiO2粉结构的影响.FT-IR光谱证明在酸性条件下SDS分子吸附于TiO2颗粒的表面.颗粒尺寸增大引起Rama峰、紫外吸收峰的红移,表现出量子尺寸效应.在对罗丹明B的光催化降解反应中,表面吸附SDS的TiO2粉显示出很强的光催化活性,在50 min内催化降解了100%罗丹明B. |
|
其他语种文摘
|
Sodium dodecylsulfate (SDS) was used to control the hydrolysis of tetrabutyl titanate (TBOT) and modify the surface of TiO2 particles. Hydrophobic anatase-TiO2 particles shaped in pseudo-spherical were directly obtained without heat treatment. The TiO2 particles have distinct hydrophobic property, which can float on the surface of aqueous solution and are more easily separated from aqueous solution. The morphology, structure and optic characters of these T1O2 particles were confirmed by means of TEM, XRD, FT-IR, Raman and UV-Vis spectrum. The effect of pH values on the structure of hydrolytic products was also investigated. The FT-IR spectrum showed there were organic molecules on the surface of TiO2 particles synthesized at acid condition. The quantum size effect was observed as the Raman and UV-Vis spectra shifting toward long-wave with increasing the particle size. In the photo-catalytic reaction, the Rhodanmine B was degraded 100% in 50 min by the TiO2 modified by SDS. |
|
来源
|
材料研究学报
,2005,19(2):131-138 【核心库】
|
|
关键词
|
无机非金属材料
;
纳米TiO2
;
锐钛矿
;
疏水性
;
SDS
;
光催化
|
|
地址
|
1.
东北大学
2.
中国科学院金属研究所
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-3093 |
|
学科
|
冶金工业 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:1954473
|
参考文献 共
17
共1页
|
|
1.
沈伟韧. TiO？2光催化反应及其在废水处理中的应用.
化学进展,1998,10(4):349
|
CSCD被引
171
次
|
|
|
|
|
2.
Fujishima A.
Journal of Photochemistry and Photobiology C: Photochemistry Reviews,2000,1:1
|
CSCD被引
596
次
|
|
|
|
|
3.
J M Herrmann.
Catalysis Today,1999,53:115
|
CSCD被引
96
次
|
|
|
|
|
4.
R W Matthers.
Water Res.,1991,25(10):1169
|
CSCD被引
1
次
|
|
|
|
|
5.
G Rothenberger.
J. Am. Chem. Soc.,1985,107:8054
|
CSCD被引
24
次
|
|
|
|
|
6.
R W Matthews.
J. Catal.,1988,113:549
|
CSCD被引
10
次
|
|
|
|
|
7.
赵国玺. 表面活性剂物理化学(修订版)(北京.
表面活性剂物理化学(修订版),1999
|
CSCD被引
1
次
|
|
|
|
|
8.
YUAN Qingzhong. Separation and Purification Technology.
Separation and Purification Technology,2000,21:9
|
CSCD被引
3
次
|
|
|
|
|
9.
Yuan Qingzhong.
Separation and Purification Technology,2001,24:309
|
CSCD被引
8
次
|
|
|
|
|
10.
苏文悦. TiO_2光催化剂的光谱研究.
光谱学与光谱分析,2001,21(1):32
|
CSCD被引
15
次
|
|
|
|
|
11.
张立德. 纳米材料和纳米结构(北京.
纳米材料和纳米结构,2002
|
CSCD被引
64
次
|
|
|
|
|
12.
Bersani D.
Appl. Phys. Lett.,1998,72(1):73
|
CSCD被引
22
次
|
|
|
|
|
13.
余锡宾. TiO_2超微粒子的量子尺寸效应与光吸收特性.
催化学报,1999,20(6):613
|
CSCD被引
15
次
|
|
|
|
|
14.
L Brus.
J. Phys. Chem.,1986,90:2555
|
CSCD被引
113
次
|
|
|
|
|
15.
Sugimoto T.
Journal of Colloid and Interface Science,2003,259:53
|
CSCD被引
15
次
|
|
|
|
|
16.
陈小斌. 表面活性剂对TiO-2水悬浮体稳定及流变性质的影响.
高等学校化学学报,1998,19(3):457
|
CSCD被引
5
次
|
|
|
|
|
17.
张霞. 低温制备锐钛矿结构的纳米TiO_2.
材料科学与工程学报,2004,22(3):328
|
CSCD被引
8
次
|
|
|
|
|
了解气象卫星更多信息，请访问