超音速微粒轰击对TC11钛合金组织和疲劳性能的影响
Effect of supersonic fine particle bombardment on microstructure and fatigue properties of TC11titanium alloy
查看参考文献23篇
|
文摘
|
采用超音速微粒轰击(SFPB)技术对层片组织的TC11钛合金进行表面纳米化处理,对比研究了表面纳米化处理前、后TC11钛合金的室温高周疲劳行为;借助光学显微镜(OM)、扫描电镜(SEM)、透射电镜(TEM)和X射线衍射仪(XRD)对比分析了高周疲劳断口及断口附近的微观组织形貌。结果表明:经SFPB处理后在钛合金表层产生了30~ 50μm厚的纳米层,纳米晶尺寸在5~15nm左右;疲劳性能得到明显提高,在相同应力级别下的疲劳寿命提高了约8~ 10倍,疲劳条带宽度变窄,且随着加载级别的降低,疲劳寿命提高的倍数逐渐增加;SFPB前、后疲劳断口均由疲劳源区、裂纹扩展区、瞬断区三部分组成,但SFPB处理后的疲劳源由处理前的表层移至次表层;SFPB处理态试样疲劳加载后表层组织仍为纳米量级,但次表层组织中出现大量的形变孪晶、位错缠结以及少量的形变诱导马氏体组织。 |
|
其他语种文摘
|
The high cycle fatigue behavior of TC11titanium alloy with lamellar structure before and after surface nanocrystallization was studied by supersonic fine particle bombardment(SFPB).The microstructure of the high cycle fatigue fracture and its vicinity were compared and analyzed by means of optical microscope(OM),scanning electron microscope(SEM),transmission electron microscope(TEM)and X-ray diffraction(XRD).The results show that there are 30-50μm thick nanolayers on the surface of titanium alloy after SFPB treatment,and the size of nanocrystalline is about 5-15nm. The fatigue performance is improved obviously and the fatigue life is increased about 8-10times under the same stress level,the fatigue striation width becomes narrow,and the multiple of fatigue life increases gradually with the decrease of loading level.The fatigue fracture surface before and after SFPB treatment consists of the fatigue source zone,the crack propagation zone and the instantaneous fracture zone,but the fatigue source after SFPB treatment moves from the surface layer before treatment to the subsurface.After fatigue loading,the surface microstructure of SFPB treated specimens is still in nanometer scale,but there are a lot of deformation twins,dislocation tangles and a small amount of deformation-induced martensite in the subsurface microstructure. |
|
来源
|
材料工程
,2021,49(5):137-143 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2020.000435
|
|
关键词
|
超音速微粒轰击
;
TC11钛合金
;
表面纳米化
;
高周疲劳
;
微观组织
|
|
地址
|
1.
河南科技大学材料科学与工程学院, 河南, 洛阳, 471023
2.
有色金属新材料与先进加工技术省部共建协同创新中心, 有色金属新材料与先进加工技术河南省省部共建协同创新中心, 河南, 洛阳, 471023
3.
西北核技术研究所, 激光与物质相互作用国家重点实验室, 西安, 710024
4.
中国船舶重工集团公司第七二五研究所, 河南, 洛阳, 471023
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金资助项目
;
河南省高校科技创新人才支持计划项目
;
河南省外国专家与引智项目
;
河南科技大学科技创新团队资助项目
|
|
文献收藏号
|
CSCD:6973172
|
参考文献 共
23
共2页
|
|
1.
刘全明. 钛合金在航空航天及武器装备领域的应用与发展.
钢铁研究学报,2015,27(3):1-4
|
CSCD被引
62
次
|
|
|
|
|
2.
Kikuchi S. Formation of a hydroxyapatite layer on Ti-29Nb-13Ta-4.6Zr and enhancement of four-point bending fatigue characteristics by fine particle peening.
International Journal of Lightweight Materials and Manufacture,2019,2(3):227-234
|
CSCD被引
1
次
|
|
|
|
|
3.
Xiong J H. Microstructure and mechanical properties of Ti6321alloy welded joint by GTAW.
Materials Science and Engineering:A,2015,640:419-423
|
CSCD被引
16
次
|
|
|
|
|
4.
Ao N. The effect of residual stress and gradient nanostructure on the fretting fatigue behavior of plasma electrolytic oxidation coated Ti-6Al-4Valloy.
Journal of Alloys and Compounds,2019,811:1-11
|
CSCD被引
1
次
|
|
|
|
|
5.
许良. TB6钛合金疲劳小裂纹扩展行为.
材料工程,2019,47(11):171-177
|
CSCD被引
3
次
|
|
|
|
|
6.
Zheng H Z. Effect of shot peening on microstructure, nanocrystallization and microhardness of Ti-10V-2Fe-3Al alloy surface.
Journal of Iron and Steel Research International,2019,26(1):52-58
|
CSCD被引
5
次
|
|
|
|
|
7.
王筱冬. 研磨光整处理Ti-6Al-4V钛合金表面组织及疲劳性能.
机械制造与自动化,2019,48(4):30-31
|
CSCD被引
2
次
|
|
|
|
|
8.
蔡振.
表面超声滚压Ti-6Al-4V合金多尺度疲劳裂纹扩展行为的影响,2017
|
CSCD被引
1
次
|
|
|
|
|
9.
张恭轩. TC17钛合金激光冲击强化实验研究.
表面技术,2018,47(3):96-100
|
CSCD被引
5
次
|
|
|
|
|
10.
Chen Y X. Effect of shot peening on fatigue performance of Ti_2AlNb intermetallic alloy.
International Journal of Fatigue,2019,57:53-57
|
CSCD被引
11
次
|
|
|
|
|
11.
Liu C S. Improving fatigue performance of Ti-6Al-4V alloy via ultrasonic surface rolling process.
Journal of Materials Science and Technology,2019,35:1555-1562
|
CSCD被引
9
次
|
|
|
|
|
12.
巴德玛. 超音速微粒轰击38CrSi钢表面纳米化的研究.
材料工程,2006(12):3-7
|
CSCD被引
10
次
|
|
|
|
|
13.
李慧敏. 钛合金表层机械处理的纳米化组织、力学性能与机理研究进展.
中国有色金属学报,2015,25(3):642-651
|
CSCD被引
3
次
|
|
|
|
|
14.
范梅香. TC11钛合金室温高周疲劳断口及微观组织.
河南科技大学学报(自然科学版),2019,40(1):6-11
|
CSCD被引
5
次
|
|
|
|
|
15.
Zhang X C. Improvement of fatigue life of Ti-6Al-4Valloy by laser shock peening.
Materials Science and Engineering:A,2010,527(15):3411-3415
|
CSCD被引
36
次
|
|
|
|
|
16.
Nie X F. Effect study and application to improve high cycle fatigue resistance of TC11titanium alloy by laser shock peening with multiple impacts.
Surface and Coatings Technology,2014,253:68-75
|
CSCD被引
22
次
|
|
|
|
|
17.
温爱玲. 高能喷丸时间对TC4疲劳性能的影响.
热加工工艺,2009,38(14):127-129
|
CSCD被引
5
次
|
|
|
|
|
18.
赵坤. TC17钛合金自表面纳米化机制及组织演化.
稀有金属材料与工程,2013,42(10):2048-2052
|
CSCD被引
7
次
|
|
|
|
|
19.
欧阳德来. TB6钛合金热变形诱导马氏体转变.
中国有色金属学报,2010,20(12):2307-2012
|
CSCD被引
9
次
|
|
|
|
|
20.
林翠.
钛合金选用与设计,2014:100-152
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问