表面超声滚压处理对高速列车车轴钢疲劳性能的影响
Effects of Surface Ultrasonic Rolling Processing on Fatigue Properties of Axle Steel Used on High Speed Train

任学冲 ¹ ^* 陈利钦 ² 刘鑫贵 ³ 项彬 ³ 林国标 ²

文摘	对EA4T型高速列车车轴钢棒状旋转弯曲疲劳试样实验段磨削加工后进行了表面超声滚压处理。观察了处理前后试样的表面形貌及表层微观组织,测量了处理前后试样的表面粗糙度、表层硬度及表层残余应力。利用旋转弯曲疲劳实验得到处理前后试样的疲劳极限。结果表明:表面超声滚压处理后,试样的疲劳极限由352MPa提高到401MPa。疲劳极限的提高主要由于表面超声滚压处理后试样表面粗糙度降低、表层强度及残余压应力增加。
其他语种文摘	The rotating bar bending fatigue testing specimens made from EA4T high speed axle were grinded. Some of the grinded specimens were surface ultrasonic rolling processed (SURP). The microstructures in surface layer and surface morphologies of the grinded specimens and the SURP specimens were observed. Micro-hardness and residual stress in surface layer and surface roughness of the grinded specimens and the SURP specimens were measured. Fatigue limits of the grinded specimens and the SURP specimens were tested using rotational bending testing method. The results show that fatigue limits of the grinded specimens and the SURP specimens are 352MPa and 401MPa respectively.The increase of fatigue limit of the SURP specimens is mainly due to the decrease of surface roughness and the increase of strength and residual compressive stress in surface layer.
来源	材料工程 ,2015,43(12):1-5 【核心库】
DOI	10.11868/j.issn.1001-4381.2015.12.001
关键词	车轴钢 ; 表面超声滚压处理 ; 疲劳极限 ; 表面粗糙度 ; 残余应力
地址	1. 北京科技大学国家材料服役安全科学中心, 北京, 100083 2. 北京科技大学材料科学与工程学院, 北京, 100083 3. 中国铁道科学研究院金属与化学研究所, 北京, 100081
语种	中文
文献类型	研究性论文
ISSN	1001-4381
学科	金属学与金属工艺
基金	国家自然科学基金资助项目 ; 北京高等学校青年英才计划资助项目
文献收藏号	CSCD:5592136