镁合金无铬化学转化处理的研究 第一部分——工艺参数的优化及膜层性能的测试
Study on chrome-flee chemical conversion treatment of magnesium alloys Part I-Optimization of technological parameters and investigation of film properties
查看参考文献8篇
|
文摘
|
介绍了一种新型无毒的镁合金无铬化学转化处理方法。正交试验获得的最佳工艺参数为：8g／LNa^＋，0．5g／LcO^-23，0．01g／L辅助成膜剂N，处理时间30min，处理温度30℃。研究了膜层的耐蚀性及其与不同漆膜之间的附着力。结果表明，在优化工艺下获得的膜层具有优良的耐蚀性（耐中性盐雾试验时间〉96h）和漆膜附着力（达到1级）。 |
|
其他语种文摘
|
A novel nontoxic and chrome-free chemical conversion treatment process for Mg and its alloys was presented. The technological parameters were optimized by orthogonal experiments： 8 g/L Na^＋, 0.5 g/LCO^-23, 0.01 g/L auxiliary film-forming agent （code： N）, treatment temperature 30℃ and time 30 min. The properties of conversion film, such as corrosion resistance and adhesion strength to different coatings, were studied. The film obtained under optimal process conditions shows good corrosion resistance as characterized by the failure time in neutral salt spray test （〉96 h） and adhesion strength to coatings （reaching first grade）. |
|
来源
|
电镀与涂饰
,2007,26(5):38-42 【扩展库】
|
|
关键词
|
镁合金
;
无铬化学转化工艺
;
耐蚀性
;
附着力
|
|
地址
|
1.
中科院金属研究所, 辽宁, 沈阳, 110016
2.
武汉材料保护研究所, 湖北, 武汉, 430030
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-227X |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:2889484
|
参考文献 共
8
共1页
|
|
1.
郭敏. 镁合金无铬化学转化工艺研究.
材料保护,2005,38(5):28-30
|
CSCD被引
11
次
|
|
|
|
|
2.
杨熙珍.
金属腐蚀电化学热力学,1991:196
|
CSCD被引
1
次
|
|
|
|
|
3.
LINDSTROM R. Corrosion of magnesium in humid air.
Corrosion Science,2004,46(5):1141-1158
|
CSCD被引
25
次
|
|
|
|
|
4.
MATHIEU S. A corrosion study of the main constituent phases of AZ91 magnesium alloys.
Corrosion Science,2003,45(12):2741-2755
|
CSCD被引
66
次
|
|
|
|
|
5.
陈振华.
镁合金,2004:1-25
|
CSCD被引
24
次
|
|
|
|
|
6.
赵明. 镁合金磷酸盐-高锰酸盐化学转化处理工艺研究.
特种铸造及有色合金,2005,25(6):328-329
|
CSCD被引
17
次
|
|
|
|
|
7.
张建. 215铁红环氧防锈底漆的研制.
材料保护,1999,32(11):28-29
|
CSCD被引
1
次
|
|
|
|
|
8.
刘涛. BH06-10铁红丙烯酸环氧酯预涂底漆的研制.
铁道技术监督,1999(6):24-27
|
CSCD被引
1
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问