NaCl沉积和SO_2污染对镁合金初期大气腐蚀行为的影响
Atmospheric Corrosion Initial Stages of Magnesium Alloy in the Presence of NaCl and SO_2
查看参考文献12篇
|
文摘
|
借助扫描电镜(SEM/EDX)、X射线衍射(XRD)研究了NaCl单个因素对镁合金AZ9lD初期腐蚀行为的影响，并对SO2和NaCl的协同作用进行了探讨．NaCl存在时初期破坏金属表面的保护膜，但后期微溶性腐蚀产物的生成导致腐蚀速率的降低．当NaCl和SO2同时存在时，反应生成的可溶性产物不具有阻碍的作用，同时他们会发生部分溶解生成自由移动的离子，大量难溶物在镁合金表面难以短时间形成，故NaCl和SO_2同时存在引起的腐蚀远大于两者单独存在时引起的腐蚀加和。NaCl和SO_2对镁合金的初期大气腐蚀具有明显的协同作用。 |
|
其他语种文摘
|
The effects of NaCl and SO2 on the initial atmospheric corrosion of AZ91D magnesium alloy were studied with a simulated atmospheric corrosion system. The analyses of surface morphology, corrosion products and rust layer structure were integrated by Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD) to in-vestigate the corrosion performance. The results showed that NaCl accelerated the initial atmospheric corrosion of the alloy. The protective film was destroyed in the initial period, but the corrosion rate slowed down because of the formation of slight soluble corrosion products in the later periods in the presence of NaCl. Soluble corrosion pro-ducts with no inhibitive function developed and partly solved to form the ions of free motion when NaCl and SO2 existed simultaneously. A greal deal of these products were very difficult to grow on the surface in a short time. The combined effect of NaCl and SO2 on the initial atmospheric corrosion was greater than that caused by each single component. |
|
来源
|
北京科技大学学报
,2004,26(5):524-528 【核心库】
|
|
关键词
|
SO_2
;
NaCl
;
初期
;
AZ91镁合金
;
协同作用
|
|
地址
|
北京科技大学材料科学与工程学院腐蚀与防护中心, 北京, 100083
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-053X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家科技基础条件平台建设重点项目
;
国家973计划
|
|
文献收藏号
|
CSCD:1656088
|
参考文献 共
12
共1页
|
|
1.
Qu Q. Influence of NaCl deposition on atmospheric corrosion of A3 steel [J].
J Mater Sci Technol,2002,18(6):552
|
CSCD被引
4
次
|
|
|
|
|
2.
Pacheco A M G. an infrared spectroscopic study [J].
Br Corros J,1990,25(1):579
|
CSCD被引
1
次
|
|
|
|
|
3.
Neufeld A K. The Initial mechanism of corrosion of zinc by sodium chloride particle deposition [J].
Corros Sci,2002,44:555
|
CSCD被引
31
次
|
|
|
|
|
4.
Svensson J E. A Laboratory Study of the Initial Stages of the Atmospheric Corrosion of Zinc in the Presence of NaCl.
Corros Sci,1993,34(5):721
|
CSCD被引
37
次
|
|
|
|
|
5.
朱日彰. c.
金属腐蚀学,1993:209
|
CSCD被引
1
次
|
|
|
|
|
6.
托马晓夫. c.
金属腐蚀及其保护的理论,1964:251
|
CSCD被引
2
次
|
|
|
|
|
7.
Qu Q. Effects of NaCl and SO2 on the initial atmospheric corrosion of zinc [J].
Corrosion,2002,44:2789
|
CSCD被引
3
次
|
|
|
|
|
8.
屈庆. NaCl和SO_2在A3钢初期大气腐蚀中的协同效应.
金属学报,2002,38(10):1062
|
CSCD被引
27
次
|
|
|
|
|
9.
Lindstrom R. The influence of carbon dioxide in the atmospheric corrosion of some magnesium alloys in the presence of NaCl [J].
J Electrochem Soc,2002,149(4):B103
|
CSCD被引
16
次
|
|
|
|
|
10.
Falk T. The influence of CO2and NaCl in the atmospheric corrosion of zinc [J].
J Electrochem Soc,1998,145(9):2993
|
CSCD被引
13
次
|
|
|
|
|
11.
Bengtsson B D. The influence of CO2 on the NaCl-induced atmospheric corrosion of aluminium [J].
J Electrochem Soc,2001,148(4):B127
|
CSCD被引
6
次
|
|
|
|
|
12.
Eriksson P. Initial stages of copper corrosion in humid air containing SO2 and NO2 [J].
J Electrochem Soc,1993,140(1):538
|
CSCD被引
1
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问