在湿H2S环境中金属腐蚀行为和机理研究概述
A REVIEW ON CORROSION BEHAVIOR AND MECHANISM OF METALS IN WET H2S
查看参考文献42篇
|
文摘
|
概述了金属在湿H2S环境中的腐蚀破坏类型、腐蚀机理、实验研究方法和影响因素,探讨了湿H2S的定义,提出:在区分溶液H2S和薄液H2S腐蚀的基础上,加强湿H2S环境下腐蚀机理、高温高压湿H2S条件下的腐蚀开裂行为和机理、阳极溶解和HIC的相互关系的研究;发展和规范湿H2S环境下设备腐蚀破坏的检测方法和相关的工业标准,开展H2S环境下寿命预测和安全评估技术工作;完善室内模拟湿H2S环境下腐蚀实验技术. |
|
其他语种文摘
|
The types, mechanisms, research methods and influence factors of corrosion and cracking of metals in wet hydrogen sulfide were summarized in the paper. The definition of wet hydrogen sulfide was also discussed. Further researches were proposed as follows: understanding corrosion mechanisms in wet hydrogen sulfide, corrosion and cracking in high temperature and high pressure hydrogen sulfide and the relations between anodic SCC and HIC; developing methods for detecting H2S induced corrosion damage of facilities in wet hydrogen sulfide and the relevant industrial standards; carrying out works on lifetime prediction and safety evaluation and establishing test techniques to simulate sulfide hydrogen corrosion indoor. |
|
来源
|
腐蚀科学与防护技术
,2005,17(2):107-111 【核心库】
|
|
关键词
|
湿H2S
;
应力腐蚀开裂
;
阳极溶解
;
氢致开裂
|
|
地址
|
北京科技大学腐蚀与防护中心, 北京市腐蚀、磨蚀与表面技术开放实验室, 北京, 100083
|
|
语种
|
中文 |
|
文献类型
|
综述型 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
基金
|
中国石油化工集团公司项目
;
国家973计划
|
|
文献收藏号
|
CSCD:1927024
|
参考文献 共
42
共3页
|
|
1.
王维宗. 液化石油气球罐的硫化物应力腐蚀破裂[J].
腐蚀与防护,1983,22(3):15
|
CSCD被引
1
次
|
|
|
|
|
2.
应道宴. 液化石油气球罐的硫化物应力腐蚀破裂[J].
腐蚀与防护,1983(2):22
|
CSCD被引
1
次
|
|
|
|
|
3.
于英姿. 输气管道的硫化物应力腐蚀分析[J].
油气储运,2000,19(8):37
|
CSCD被引
3
次
|
|
|
|
|
4.
柳曾典. 湿硫化氢环境用低合金高强度钢[J].
石油化工设备技术,1998,19(5):57
|
CSCD被引
3
次
|
|
|
|
|
5.
American Petroleum Institute. American Petroleum Institute.
Technical Data Book, Phase Equilibrium in System Containing Water,1966:7
|
CSCD被引
1
次
|
|
|
|
|
6.
Y M Mu. Applying process modeling to screen refining equipment for wet hydrogen sulfide service[J].
Corrosion,1998,54(2):167
|
CSCD被引
1
次
|
|
|
|
|
7.
. Canadian Standards Association CSA- Z662 - 94.
Canadian Standards Association CSA- Z662 - 94, Oil and Gas Pipelines
|
CSCD被引
1
次
|
|
|
|
|
8.
. European Federation of Corrosion Publication.
A Working Party Report on Guidelines on Material requirements for Carbon and Low Alloy Steels for H2S - Containing Environments in Oil and Gas Production,1995:10
|
CSCD被引
1
次
|
|
|
|
|
9.
王荣贵. 化工装置中钢在湿硫化氢环境下的腐蚀机理与设备选材[J].
化肥设计,2002,40:5
|
CSCD被引
3
次
|
|
|
|
|
10.
陈石卿(译). ВасиленкоИИ.
钢的应力腐蚀开裂,1983:185
|
CSCD被引
1
次
|
|
|
|
|
11.
Tromans D. Stress corrosion cracking of ASTM A516 steel in hot caustic sulfide solutionspotential and weld effects[J].
Corrosion,1986,42(2):63
|
CSCD被引
3
次
|
|
|
|
|
12.
Kindlein W. The characterization of the sulphide stress corrosion susceptibility of high- strength low- alloy steels in standardized solutions[J].
Corrosion Science,1993,34(8):1243
|
CSCD被引
5
次
|
|
|
|
|
13.
Riecke E M. The effect of phosphorus on hydrogen uptake by iron in acidic suplphate and sulphide solutions[J].
Corrosion Science,1987,27(10):1027
|
CSCD被引
3
次
|
|
|
|
|
14.
Greer J B. Factors affecting the sulfide stress cracking performance of high strength steels [J].
Materials performance,1975,14(3):11
|
CSCD被引
3
次
|
|
|
|
|
15.
褚武扬. 钢中氢致开裂机理[J].
金属学报,1981,17:10
|
CSCD被引
11
次
|
|
|
|
|
16.
Li J C M. Computer simulation of dislocations emitted from a crack[J].
Scripta Metal,1986,20:1477
|
CSCD被引
9
次
|
|
|
|
|
17.
Lu H. Hydrogen - enhanced dislocation emission.
Science in China. Series E (in English),1997,40:530
|
CSCD被引
10
次
|
|
|
|
|
18.
褚武扬. 断裂与环境断裂[M].
断裂与环境断裂,2000:221
|
CSCD被引
1
次
|
|
|
|
|
19.
H Huang. Cold work effects on sulfide stress cracking of pipeline steel exposed to sour environments [J].
Corrosion Science,1993,34(1):61
|
CSCD被引
2
次
|
|
|
|
|
20.
左禹. 1Cr18Ni9Ti不锈钢在硫化氢水溶液中的台阶状应力腐蚀破裂[J].
北京化工学院学报,1994,21(4):58
|
CSCD被引
6
次
|
|
|
|
|
了解气象卫星更多信息，请访问