Roasting and leaching behaviors of vanadium and chromium in calcification roasting-acid leaching of high-chromium vanadium slag
查看参考文献22篇
|
文摘
|
Calcification roasting-acid leaching of high-chromium vanadium slag (HCVS) was conducted to elucidate the roasting and leaching behaviors of vanadium and chromium. The effects of the purity of CaO, molar ratio between CaO and V_2O_5 (n(CaO)/n(V_2O_5)), roasting temperature, holding time, and the heating rate used in the oxidation-calcification processes were investigated. The roasting process and mechanism were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), and thermogravimetry-differential scanning calorimetry (TG-DSC). The results show that most of vanadium reacted with CaO to generate calcium vanadates and transferred into the leaching liquid, whereas almost all of the chromium remained in the leaching residue in the form of (Fe_(0.6)Cr_(0.4))_2O_3. Variation trends of the vanadium and chromium leaching ratios were always opposite because of the competitive reactions of oxidation and calcification between vanadium and chromium with CaO. Moreover, CaO was more likely to combine with vanadium, as further confirmed by thermodynamic analysis. When the HCVS with CaO added in an n(CaO)/n(V_2O_5) ratio of 0.5 was roasted in an air atmosphere at a heating rate of 10oC/min from room temperature to 950°C and maintained at this temperature for 60 min, the leaching ratios of vanadium and chromium reached 91.14% and 0.49%, respectively; thus, efficient extraction of vanadium from HCVS was achieved and the leaching residue could be used as a new raw material for the extraction of chromium. Furthermore, the oxidation and calcification reactions of the spinel phases occurred at 592 and 630°C for n(CaO)/n(V_2O_5) ratios of 0.5 and 5, respectively. |
|
来源
|
International Journal of Minerals
, Metallurgy and Materials,2018,25(5):515-526 【核心库】
|
|
DOI
|
10.1007/s12613-018-1598-3
|
|
关键词
|
high-chromium vanadium slag
;
calcification roasting
;
roasting behaviors
;
leaching behaviors
;
vanadium extraction
|
|
地址
|
1.
School of Metallurgy, Northeastern University, Shenyang, 110819
2.
Liaoning Key Laboratory for Recycling Science of Metallurgical Resources, Liaoning Key Laboratory for Recycling Science of Metallurgical Resources, Shenyang, 110819
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1674-4799 |
|
学科
|
冶金工业 |
|
基金
|
国家自然科学基金
;
国家973计划
;
the Fundamental Funds for the Central Universities
|
|
文献收藏号
|
CSCD:6242210
|
参考文献 共
22
共2页
|
|
1.
Moskalyk R R. Processing of vanadium: a review.
Miner. Eng,2003,16(9):793
|
CSCD被引
138
次
|
|
|
|
|
2.
Dhal B. Chemical and microbial remediation of hexavalent chromium from contaminated soil and mining/metallurgical solid waste: a review.
J. Hazard. Mater,2013,250/251:272
|
CSCD被引
112
次
|
|
|
|
|
3.
Liu B. A novel method to extract vanadium and chromium from vanadium slag using molten NaOH-NaNO_3 binary system.
AIChE J,2013,59(2):541
|
CSCD被引
32
次
|
|
|
|
|
4.
Li X S. Oxidation process of low-grade vanadium slag in presence of Na_2CO_3.
Trans. Nonferrous Met. Soc. China,2011,21(8):1860
|
CSCD被引
29
次
|
|
|
|
|
5.
Katz S A. The toxicology of chromium with respect to its chemical speciation: a review.
J. Appl. Toxicol,1993,13(3):217
|
CSCD被引
16
次
|
|
|
|
|
6.
Zhang X F. Effects of microwave and conventional blank roasting on oxidation behavior, microstructure and surface morphology of vanadium slag with high chromium content.
J. Alloys Compd,2016,686:356
|
CSCD被引
7
次
|
|
|
|
|
7.
Li M. Effective extraction of vanadium and chromium from high chromium content vanadium slag by sodium roasting and water leaching.
Mater. Sci. Forum,2016,863:144
|
CSCD被引
5
次
|
|
|
|
|
8.
Li H Y. Asynchronous extraction of vanadium and chromium from vanadium slag by stepwise sodium roasting-water leaching.
Hydrometallurgy,2015,156:124
|
CSCD被引
24
次
|
|
|
|
|
9.
Van Vuuren C P J. The oxidation of FeV204 by oxygen in a sodium carbonate mixture.
Miner. Eng,2001,14(7):803
|
CSCD被引
7
次
|
|
|
|
|
10.
Wang Z H. Research and prospect on extraction of vanadium from vanadium slag by liquid oxidation technologies.
Trans. Nonferrous Met. Soc. China,2014,24(5):1273
|
CSCD被引
19
次
|
|
|
|
|
11.
Wang H G. Leaching behaviour of chromium during vanadium extraction from vanadium slag.
Miner. Process. Extr. Metall. Rev,2015,124(3):127
|
CSCD被引
3
次
|
|
|
|
|
12.
Olmez T. The optimization of Cr(VI) reduction and removal by electrocoagulation using response surface methodology.
J. Hazard. Mater,2009,162(2/3):1371
|
CSCD被引
15
次
|
|
|
|
|
13.
Robert B. Separation of chromium from vanadium by extraction of perchromic acid with ethyl acetate.
Anal. Chem,1951,23(8):1110
|
CSCD被引
1
次
|
|
|
|
|
14.
Fan Y Y. Separation and recovery of chromium and vanadium from vanadium-containing chromate solution by ion exchange.
Hydrometallurgy,2013,136:31
|
CSCD被引
14
次
|
|
|
|
|
15.
Cao P. Research on vanadium slag roasted with calcium salt.
Iron Steel Vanadium Titanium,2012,33(1):30
|
CSCD被引
2
次
|
|
|
|
|
16.
Slobodin B V. A thermoanalytical study of the interaction of vanadiumoxide(V) with calcium oxide and calcium carbonate.
J. Therm. Anal,1979,15(2):197
|
CSCD被引
1
次
|
|
|
|
|
17.
Zhang J H. Oxidation kinetics of vanadium slag roasting in the presence of calcium oxide.
Miner. Process. Extr. Metall. Rev,2017,38(5):1
|
CSCD被引
1
次
|
|
|
|
|
18.
Zhang X. Nucleation and growth kinetics of spinel crystals in vanadium slag.
Ironmaking Steelmaking,2013,39(2):147
|
CSCD被引
1
次
|
|
|
|
|
19.
Diao J. Growth mechanisms of spinel crystals in vanadium slag under different heat treatment conditions.
CrystEngComm,2015,17(38):7300
|
CSCD被引
2
次
|
|
|
|
|
20.
Miretzky P. Cr(VI) and Cr(III) removal from aqueous solution by raw and modified lignocellulosic materials: A review.
J. Hazard. Mater,2010,180(1/3):1
|
CSCD被引
60
次
|
|
|
|
|
了解气象卫星更多信息，请访问