Ti3SiC2表面渗硅涂层的抗高温氧化性能
Oxidation performance sof silicide coatings on Ti_3SiC_2-based ceramic
查看参考文献10篇
|
文摘
|
采用固体粉末包埋法在Ti3SiC2陶瓷上渗硅，研究了渗硅涂层的抗高温氧化性能，用XRD及SEM／EDS分析了渗硅涂层及其氧化后产物的成分，结构和形貌等。结果表明：渗硅层主要由TiSi2和SiC组成，在空气中氧化时形成了SiO2和TiO2的混合氧化物膜，渗硅样品在1100℃和1200℃下的恒温氧化速度比Ti3SiC2降低了2－3个数量级，1100℃下抗循环氧化性能也优于Ti3SiC2,但由于渗硅层中存在裂纹，循环过程中当裂纹贯穿整个渗硅层时，涂层的氧化速度开始增加，其保护作用逐步退化。在1100℃下空气中循环氧化时，经400次循环后涂层已基本失效。 |
|
其他语种文摘
|
Silicide coating was prepared on Ti_3SiC_2 base ceramic by pack cementation. The microstructure, phases and oxidation resistance of the coating were investigated. The results show that, the silicide coating is mainly composed of TiSi_2 and SiC; one layer of the mixture of SiO_2 and TiO_2 is formed when the coating is oxidized. At 1 100 ℃ and 1 200 ℃, the oxidation rate of silicide coat-ing is 2-3 order lower than that of Ti_3SiC_2. The cyclic oxidation resistance of the coating is much higher than that of Ti_3SiC_2. There are a great number of fine cracks in the outer layer of the coating. When these cracks penetrate whole coating during the cyclic oxida-tion, the oxidation rate begins to increase, which is the main reason for the loss of the protection of coating. |
|
来源
|
中国有色金属学报
,2002,12(4):629-633 【核心库】
|
|
关键词
|
钛碳化硅
;
渗硅
;
高温氧化
;
涂层
|
|
地址
|
中国科学院金属研究所, 沈阳材料科学国家（联合）实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1004-0609 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:1132195
|
参考文献 共
10
共1页
|
|
1.
El-Raghy T.
J Am Ceram Soc,1997,80(2):513-516
|
CSCD被引
18
次
|
|
|
|
|
2.
Racault C.
J Mat Sci,1994,29:3384-3392
|
CSCD被引
1
次
|
|
|
|
|
3.
Gao N F.
J Mater Sci,1999,34:4385-4392
|
CSCD被引
26
次
|
|
|
|
|
4.
Barsoum M W.
J Am Ceram Soc,1996,79(7):1953-1956
|
CSCD被引
147
次
|
|
|
|
|
5.
Broum M W.
J Electrochem Soc,1997,144(7):2508
|
CSCD被引
29
次
|
|
|
|
|
6.
Feng A.
J Mater Res,1999,14(3):925-938
|
CSCD被引
12
次
|
|
|
|
|
7.
Okano T.
Trans Met Soc Jpn.A,1993,14:597
|
CSCD被引
2
次
|
|
|
|
|
8.
El-Raghy T.
J Appl Phys,1998,83(1):112-119
|
CSCD被引
6
次
|
|
|
|
|
9.
Tong X.
J Mat Sci,1995,30:3087-3090
|
CSCD被引
2
次
|
|
|
|
|
10.
Samsonov G V.
The Oxide handbook,1982
|
CSCD被引
3
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问