锂离子液体作为钢/铜、钢/铝摩擦副润滑剂的摩擦学性能
Tribological Property of Lithium-based Ionic Liquids as Lubricant for Steel/Copper and Steel/Aluminum Contacts
查看参考文献15篇
文摘
|
采用一步法合成了锂离子液体润滑剂[Li(OZO)]TFSI,并选择含有相同阴离子的传统咪唑离子液体1-丁基-3-甲基咪唑双三氟甲烷磺酰亚胺盐(L-F104)作对比,在SRV摩擦磨损试验机上评价了其作为钢/铜、钢/铝润滑剂的润滑性能,用X射线光电子能谱仪(XPS)分析了润滑机理。结果表明:在室温或高温(100 ℃)条件下,[Li(OZO)]TFSI都具有优异的减摩抗磨性能,摩擦过程中在金属摩擦副表面有物理吸附与摩擦化学反应发生,形成了阻止金属间直接接触的保护膜,从而起到了减摩抗磨的效果;且[Li(OZO)]TFSI可以取代L-F104作为两种摩擦副的润滑剂,而其合成过程却比L-F104简单的多。 |
其他语种文摘
|
Lithium-based ionic liquid (IL, [Li(OZO)]TFSI) was synthesized by one step and evaluated as lubricant for steel/copper and steel/aluminum contacts on an Optimol SRV-IV oscillating reciprocating friction and wear tester. The traditional IL 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide (L-F104) was used as a contrast. The X-ray photoelectron spectrometer (XPS) analysis was carried out to explore the lubrication mechanism. The results show that [Li(OZO)]TFSI has excellent friction-reducing and anti-wear properties both at room temperature and at 100 ℃. Physical adsorption and tribochemical reactions occur during the rubbing process with the generation of surface protective films, which prevent the metal-metal contact and further reduce friction and wear. [Li(OZO)]TFSI can substitute for L-F104 to lubricate the two kinds of contacts, and the preparation of the former is simpler than the latter. |
来源
|
中国表面工程
,2013,26(6):100-105 【扩展库】
|
关键词
|
锂离子液体
;
润滑剂
;
减摩
;
抗磨
|
地址
|
中国科学院兰州化学物理研究所, 固体润滑国家重点实验室, 兰州, 730000
|
语种
|
中文 |
文献类型
|
研究性论文 |
ISSN
|
1007-9289 |
学科
|
金属学与金属工艺 |
基金
|
国家自然科学基金
|
文献收藏号
|
CSCD:5024953
|
参考文献 共
15
共1页
|
1.
Ye C F. Room-temperature ionic liquids:a novel versatile lubricant.
Chemical Communications,2001,21:2244-2245
|
被引
76
次
|
|
|
|
2.
刘维民. 烷基咪唑四氟硼酸盐离子液作为润滑剂的摩擦学性能.
摩擦学学报,2001,21(6):482-484
|
被引
43
次
|
|
|
|
3.
于波. 不同基底上离子液体薄膜的制备及其摩擦学性能的研究.
中国表面工程,2005,18(2):31-34
|
被引
1
次
|
|
|
|
4.
赵文杰. 单/双咪唑环阳离子结构对离子液体薄膜微/纳摩擦学性能的影响.
中国表面工程,2012,25(4):112-117
|
被引
4
次
|
|
|
|
5.
Liu X Q. Tribological performance of phosphonium based ionic liquids for an aluminum-on-steel system and opinions on lubrication mechanism.
Wear,2006,261(10):1174-1179
|
被引
21
次
|
|
|
|
6.
Jimenez A E. Imidazoliumionic liquids as additives of the synthetic ester propylene glycol dioleate in aluminium-steel lubrication.
Wear,2008,265(5/6):787-798
|
被引
16
次
|
|
|
|
7.
Yu B. Oil-miscible and non-corrosive phosphonium-based ionic liquids as candidate lubricant additives.
Wear,2012,289:58-64
|
被引
22
次
|
|
|
|
8.
Li D M. Excellent lubrication performance and superior corrosion resistance of vinyl functionalized ionic liquid lubricants at elevated temperature.
Tribology International,2011,44(10):1111-1117
|
被引
4
次
|
|
|
|
9.
Cai M R. Imidazolium ionic liquids as antiwear and antioxidant additive in poly(ethylene glycol)for steel/steel contacts.
ACS Applied Materials &Interfaces,2010,2(3):870-876
|
被引
10
次
|
|
|
|
10.
Song Z H. Lithium based ionic liquids:in-situ formed lubricant additive only by blending.
Tribology Letters,2013,49(1):127-133
|
被引
2
次
|
|
|
|
11.
Chen R J. Novel binary room-temperature complex system based on LiTFSI and 2-Oxazolidinone and its characterization as electrolyte.
Journal of Physical Chemistry C,2007,111(13):5184-5194
|
被引
7
次
|
|
|
|
12.
黄伊辉. 离子液体用作润滑剂的研究进展.
润滑油,2010,25(1):4-11
|
被引
6
次
|
|
|
|
13.
.
NIST X-ray photoelectron Spectroscopy Database,2012
|
被引
5
次
|
|
|
|
14.
Bermudez M D. Study of surface interactions of ionic liquids with aluminium alloys in corrosion and erosion-corrosion processes.
Applied Surface Science,2007,253(17):7295-7302
|
被引
3
次
|
|
|
|
15.
Lu R. Study of tribochemical decomposition of ionic liquids on a nascent steel surface.
Applied Surface Science,2009,255(22):8965-8971
|
被引
1
次
|
|
|
|
|