DD421单晶高温合金在无SO_x气氛下的低温热腐蚀硫化行为
Sulfidation behavior in low-temperature hot corrosion of single crystal superalloy DD421 without SO_x atmosphere
查看参考文献24篇
|
文摘
|
采用涂盐法研究表面涂覆有90%(质量分数,下同)Na_2SO_4+10%NaCl混合盐(750℃熔融态)和纯Na_2SO_4盐(750℃固态)的第二代镍基单晶高温合金DD421在750℃大气环境下(无SO_x气氛)的热腐蚀行为。结果表明:在熔融混合盐腐蚀介质中,硫化反应主要由液相熔融盐侵蚀所导致。热腐蚀100h后合金腐蚀产物主要为典型的简单氧化物(Al_2O_3,Cr_2O_3,TiO_2)以及Ni/Cr/Ti的硫化物。而在纯Na_2SO_4固态盐热腐蚀实验中,热腐蚀100h后合金腐蚀产物与混合盐实验中的产物基本相同,但其腐蚀层厚度相对更薄,硫化物尺寸相对更大。结合热力学和微观组织分析,本研究明确了在无SO_x气氛的腐蚀环境下合金元素能够与固态Na_2SO_4盐发生硫化反应。 |
|
其他语种文摘
|
The hot corrosion behavior of the second generation nickel base single crystal superalloy DD421 coated with 90%(mass fraction)Na_2SO_4+10%NaCl(molten at 750℃)and pure Na_2SO_4(solid state at 750 ℃)was investigated by salt coating method in 750 ℃ atmosphere (without SO_x atmosphere).The results show that in the corrosion medium of molten mixed salt,the sulfidation reaction is mainly caused by the corrosion of liquid molten salt.After 100h of hot corrosion,the main corrosion products are typical simple oxides(Al_2O_3,Cr_2O_3,TiO_2)and Ni/Cr/Ti sulfides.However,in the pure Na_2SO_4 solid salt hot corrosion experiment,the corrosion products of the alloy after 100h of hot corrosion are basically the same as those in the mixed salt test,but the thickness of the corrosion layer is relatively thinner and the size of sulfide is relatively larger.Combined with thermodynamics and microstructure analysis,it is clear that the alloy elements can react with solid Na_2SO_4 salt in the corrosion environment without SO_xatmosphere. |
|
来源
|
材料工程
,2021,49(6):109-115 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2020.000335
|
|
关键词
|
高温合金
;
热腐蚀
;
硫化
;
固态反应
|
|
地址
|
1.
中国科学技术大学材料科学与工程学院, 合肥, 230026
2.
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家重大科技专项
|
|
文献收藏号
|
CSCD:6997251
|
参考文献 共
24
共2页
|
|
1.
Eliaz N. Hot corrosion in gas turbine components.
Engineering Failure Analysis,2002,9(1):31-43
|
CSCD被引
55
次
|
|
|
|
|
2.
张莹. 一种新型钴基高温合金在900℃熔融NaCl中的热腐蚀行为.
材料工程,2018,46(8):134-139
|
CSCD被引
2
次
|
|
|
|
|
3.
李萍. 涂覆Na_2SO_4-25%NaCl盐膜的Super304H的热腐蚀行为.
材料工程,2016,44(2):69-74
|
CSCD被引
8
次
|
|
|
|
|
4.
Bourhis Y. Na_2SO_4-and NaCl~-induced hot corrosion of six nickel-base superalloys.
Oxidation of Metals,1975,9(6):507-528
|
CSCD被引
12
次
|
|
|
|
|
5.
Deb D. A comparative study of oxidation and hot corrosion of a cast nickel base superalloy in different corrosive environments.
Materials Letters,1996,29(1/3):19-23
|
CSCD被引
13
次
|
|
|
|
|
6.
Gurrappa I. Hot corrosion behavior of CM 247LC alloy in Na_2SO_4and NaCl environments.
Oxidation of Metals,1999,51(5/6):353-382
|
CSCD被引
12
次
|
|
|
|
|
7.
Weng F. The influence of Nb on hot corrosion behavior of Ni-based superalloy at 800℃in a mixture of Na_2SO_4-NaCl.
Journal of Materials Research,2014,29(21):2596-2603
|
CSCD被引
5
次
|
|
|
|
|
8.
Kamal S. Hot corrosion behavior of superalloy in different corrosive environments.
Journal of Minerals and Materials Characterization and Engineering,2015,3:26-36
|
CSCD被引
2
次
|
|
|
|
|
9.
Chiang K T. Low temperature hot corrosion.
High Temperature Corrosion.Proceedings of the International Conference,1983:519-530
|
CSCD被引
1
次
|
|
|
|
|
10.
Luthra K L. Low-temperature hot corrosion of cobalt-base alloys:Ⅰmorphology of the reaction-product.
Metallurgical and Materials Transactions A,1982,13(10):1843-1852
|
CSCD被引
13
次
|
|
|
|
|
11.
Luthra K L. Low-temperature hot corrosion of cobalt-base alloys:Ⅱreaction-mechanism.
Metallurgical and Materials Transactions A,1982,13(10):1853-1864
|
CSCD被引
6
次
|
|
|
|
|
12.
Pettit F. Hot corrosion of metals and alloys.
Oxidation of Metals,2011,76(1/2):1-21
|
CSCD被引
12
次
|
|
|
|
|
13.
Sumner J. TypeⅡhot corrosion:kinetics studies of CMSX-4.
Oxidation of Metals,2013,80(5/6):553-563
|
CSCD被引
1
次
|
|
|
|
|
14.
Lortrakul P. Investigation of the mechanisms of Type-Ⅱhot corrosion of superalloy CMSX-4.
Corrosion Science,2014,80:408-415
|
CSCD被引
9
次
|
|
|
|
|
15.
Kai W. Sulfidation behavior of Inconel 738superalloy at 500-900℃.
Oxidation of Metals,2001,56(1/2):51-71
|
CSCD被引
6
次
|
|
|
|
|
16.
Zhang W J. Revisit the typeⅡcorrosion mechanism.
Metallurgical and Materials Transactions A,2018,49(9):4362-4372
|
CSCD被引
2
次
|
|
|
|
|
17.
徐仰涛. 钽含量对Co-Al-W合金强化相和高温氧化行为的影响.
中国有色金属学报,2016,26(2):302-309
|
CSCD被引
4
次
|
|
|
|
|
18.
赵双群. 新型镍基高温合金在950℃和1000℃的氧化行为.
稀有金属材料与工程,2005,34(2):208-211
|
CSCD被引
40
次
|
|
|
|
|
19.
Cook L.
Phase diagrams for ceramists:volⅦ,1989:118
|
CSCD被引
1
次
|
|
|
|
|
20.
Goebel J A. Na_2SO_4-induced accelerated oxidation(hot corrosion)of nickel.
Metallurgical Transactions,1970,1(7):1943-1954
|
CSCD被引
26
次
|
|
|
|
|
了解气象卫星更多信息，请访问