不同热氧环境对T800碳纤维/环氧树脂复合材料力学性能的影响
Effects of different thermal-oxidative environments on mechanical properties of T800carbon fiber/epoxy resin composites
查看参考文献16篇
|
文摘
|
不同热氧环境(70,130,190℃)对碳纤维复合材料的性能有着重要的影响。分析了不同热氧环境下T800碳纤维/环氧树脂复合材料的失重特性,并对比了老化前后的表面形貌、红外光谱、动态力学性能和层间剪切性能。结果表明:在热氧老化初始阶段,质损率急速上升,老化温度越高质量损失越快;试样表面形貌随热氧温度的升高其破坏程度逐渐加剧,在190℃老化后,纤维表面树脂脱落严重,纤维与纤维之间出现裂缝空隙,无树脂填充,在此老化温度下,试样发生了不可逆化学变化;试样的玻璃化转变温度会随老化温度的升高而变大,但内耗呈现先降低后增大再降低的趋势,在70, 130,190℃热氧老化后试样剪切强度分别提高6.0%,13.7%和2.1%。相关实验结果和实验现象可为后续研究新型国产T800碳纤维/环氧复合材料提供数据参考。 |
|
其他语种文摘
|
Different thermal-oxidative environments(70,130℃and 190℃)have important effects on the properties of carbon fiber composites.The mass loss characteristics of T800carbon fiber/epoxy resin composites under different thermal-oxidative environments were analyzed,and the surface morphology,infrared spectra,dynamic mechanical properties and interlaminar shear properties of T800carbon fiber/epoxy resin composites before and after aging were compared.The results show that in the initial stage of thermal-oxidative aging,the mass loss rate is increased rapidly,and the higher the aging temperature,the faster the mass loss.The extent of damage sample surface morphology is gradually increased with the increasing of thermal-oxidative temperature,after aging at 190℃,the resin on the fiber surface falls off seriously,the cracks and gaps appear between the fibers,and there is no resin filling,at this aging temperature,the sample has an irreversible chemical change.The glass transition temperature of the sample is increased with the increase of aging temperature,but the internal friction is decreased at first,then increased and then decreased.After thermal-oxidative aging at 70,130℃and 190℃,the shear strength of the samples is increased by 6.0%,13.7% and 2.1%,respectively.The relevant test results and phenomena can provide data reference for the follow-up study of the new domestic T800carbon fiber/epoxy composites. |
|
来源
|
材料工程
,2022,50(4):156-161 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2021.000678
|
|
关键词
|
不同热氧环境
;
T800碳纤维/环氧树脂复合材料
;
表面形貌
;
红外光谱
;
力学性能
|
|
地址
|
1.
航空工业成都飞机工业(集团)有限责任公司, 成都, 610091
2.
沈阳航空航天大学机电工程学院, 沈阳, 110136
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
一般工业技术 |
|
文献收藏号
|
CSCD:7208416
|
参考文献 共
16
共1页
|
|
1.
Salvetti M. Analytical model of the dynamic behavior of CFRP plates subjected to lowvelocity impacts.
Composites:Part B,2018,142:47-55
|
CSCD被引
5
次
|
|
|
|
|
2.
Liao B. Finite element analysis of dynamic progressive failure properties of GLARE hybrid laminates under low-velocity impact.
Journal of Composite Materials,2018,52(10):1317-1330
|
CSCD被引
1
次
|
|
|
|
|
3.
陈祥宝. 先进树脂基复合材料的发展.
航空材料学报,2000,20(1):46-54
|
CSCD被引
48
次
|
|
|
|
|
4.
Kubota Y. Long-term thermal stability of carbon fibre-reinforced addition-type polyimide composite in terms of compressive strength.
Advanced Composite Materials,2019,28(2):115-133
|
CSCD被引
1
次
|
|
|
|
|
5.
马少华. 湿热-高温循环老化对碳纤维增强双马树脂基复合材料界面性能的影响.
高分子材料科学与工程,2018,34(3):54-59
|
CSCD被引
5
次
|
|
|
|
|
6.
过梅丽. 先进聚合物基复合材料的老化研究Ⅰ热氧老化.
航空学报,2000,21(增刊1):62-65
|
CSCD被引
28
次
|
|
|
|
|
7.
郭丹丹. 热氧老化对三维四向编织碳/环氧复合材料压缩性能的影响.
山东纺织科技,2014(5):7-11
|
CSCD被引
1
次
|
|
|
|
|
8.
Akay M. Evaluation of thermal ageing of a carbon fibre reinforced bismalemide.
Composites Science and Technology,2008,68(15/16):3081-3086
|
CSCD被引
7
次
|
|
|
|
|
9.
Shivakumar K N. Effect of thermal fatigue on tensile and flexural properties of carbon/cyanate ester pultruded composite.
Journal of Reinforced Plastics and Composites,2009,28(6):675-689
|
CSCD被引
2
次
|
|
|
|
|
10.
马少华. 热氧老化对碳纤维双马树脂基复合材料性能的影响.
材料工程,2017,45(12):50-57
|
CSCD被引
11
次
|
|
|
|
|
11.
Xu L. Effects of hygrothermal and thermal-oxidative ageing on the open-hole properties of T800/high-temperature epoxy resin composites with different hole shapes.
High Performance Polymers,2020,32:306-315
|
CSCD被引
4
次
|
|
|
|
|
12.
Chen J S. Processing and properties of carbon fiber-reinforced PMR type polyimide composites.
High Performance Polymers,2006,18(3):377-396
|
CSCD被引
4
次
|
|
|
|
|
13.
Ray B C. Temperature effect during humid ageing on interfaces of glass and carbon fibers reinforced epoxy composites.
Journal of Colloid and Interface Science,2006,298:111-117
|
CSCD被引
42
次
|
|
|
|
|
14.
樊威. 热氧老化对碳纤维织物增强聚合物基复合材料弯曲性能的影响.
复合材料学报,2015,32(5):1260-1270
|
CSCD被引
15
次
|
|
|
|
|
15.
Xu L. Effects of aging process and testing temperature on the open-hole compressive properties of a carbon fiber composite.
High Performance Polymers,2020,32:693-701
|
CSCD被引
2
次
|
|
|
|
|
16.
许良. 热氧老化对炭纤维/双马树脂复合材料力学性能的影响.
固体火箭技术,2017,40(6):770-775
|
CSCD被引
2
次
|
|
|
|
|