固溶参数对镍基高温合金K439B显微组织及力学性能的影响
Effect of solution parameters on microstructures and mechanical properties of K439B nickel-based superalloy
查看参考文献18篇
|
文摘
|
采用金相显微镜和场发射扫描电子显微镜(FE-SEM)研究不同固溶温度(1140,1160 ℃及1180 ℃)及固溶冷却方式(AC,FC-900 ℃+AC,FC)等热处理参数对K439B合金显微组织及力学性能的影响。结果表明:提高固溶温度后合金的光学组织及γ'相形貌接近,晶界宽度略有增加。当以AC方式冷却时,γ'相均匀分布,尺寸为50.7 nm;以FC-900 ℃+AC方式冷却时,枝晶间及晶界附近析出250~510 nm的粗大γ '相,γ '相呈双态形貌;以FC方式冷却时,粗大γ '相的含量增多,且晶界颗粒状M_(23)C_6碳化物含量有所提高。降低冷却速率后K439B合金的815 ℃/379 MPa持久寿命得到较大改善,不同固溶参数对热处理K439B合金的室温拉伸性能影响较小。 |
|
其他语种文摘
|
The effect of different solution temperatures(1140, 1160 ℃ and 1180 ℃)and cooling conditions(AC, FC-900 ℃ +AC,FC)on the microstructures and mechanical properties of K439B alloy were investigated using metallographic microscopy and field emission scanning electron microscopy(FE-SEM). The results show that the optical microstructures and morphology of γ' precipitates are similar and the width of grain boundary slightly increases after increasing the solution temperature. When cooled with AC, γ' precipitates are uniformly distributed and the average size is 50.7 nm; when cooled with FC-900 ℃+AC, the larger γ' precipitates of 250-510 nm are precipitated at the interdendritic area region and near the grain boundary, exhibiting a bimodal γ' microstructure; when cooled with FC, the volume fraction of larger γ' precipitates increases and the content of granular M_(23)C_6 carbides at grain boundary improves. The stress rupture life of K439B alloy at 815 ℃/379 MPa is enhanced after reducing the cooling rate, while different solution parameters have little effect on the room-temperature tensile property. |
|
来源
|
材料工程
,2024,52(4):120-126 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2022.001021
|
|
关键词
|
镍基高温合金
;
K439B
;
固溶参数
;
显微组织
;
力学性能
|
|
地址
|
1.
西安理工大学材料科学与工程学院, 西安, 710048
2.
中国航发北京航空材料研究院, 先进高温结构材料国防科技重点实验室, 北京, 100095
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家重大科技专项
;
先进高温结构材料重点实验室基金
;
中国航空发动机集团科技创新平台项目
|
|
文献收藏号
|
CSCD:7702985
|
参考文献 共
18
共1页
|
|
1.
Schwant R. New materials enable unprecedented improvement in turbine performance.
Advanced Materials and Processes,2013,171(1):18-22
|
CSCD被引
6
次
|
|
|
|
|
2.
郭建亭.
高温合金材料学,2008:1-4
|
CSCD被引
4
次
|
|
|
|
|
3.
Detrois M. Advancing development and application of superalloys.
Journal of Metals,2020,72(5):1783-1784
|
CSCD被引
2
次
|
|
|
|
|
4.
Tang L T. Precipitation sequences in rapidly solidified Allvac 718Plus alloy during solution treatment.
Journal of Materials Science and Technology,2022,128:180-194
|
CSCD被引
1
次
|
|
|
|
|
5.
Ou M Q. Effect of Solution Annealing on Microstructure and Mechanical Properties of a Ni-Cr-W-Fe Alloy.
Journal of Materials Science and Technology,2017,33(11):1300-1307
|
CSCD被引
5
次
|
|
|
|
|
6.
Franco-Correa J C. Effect of conventional heat treatments on the microstructure and microhardness of IN718 obtained by wrought and additive manufacturing.
Journal of Materials Engineering and Performance,2021,30:7035-7045
|
CSCD被引
2
次
|
|
|
|
|
7.
夏鹏成. 固溶温度对DZ951镍基高温合金组织和持久性能的影响.
材料工程,2009(9):1-4
|
CSCD被引
2
次
|
|
|
|
|
8.
Singh A R P. Influence of cooling rate on the development of multiple generations of γ ' precipitates in a commercial nickel base superalloy.
Materials Characterization,2011,62(9):878-886
|
CSCD被引
24
次
|
|
|
|
|
9.
Deng W K. Prediction of yield strength in a polycrystalline nickel base superalloy during interrupt cooling.
Scripta Materialia,2020,183:139-143
|
CSCD被引
2
次
|
|
|
|
|
10.
Anderson M. δ phase precipitation in Inconel 718 and associated mechanical properties.
Materials Science and Engineering: A,2017,679:48-55
|
CSCD被引
26
次
|
|
|
|
|
11.
Anbarasan N. Effect of heat treatment on the microstructure and mechanical properties of Inconel 718.
Materials Today Proceedings,2018,5(2):7716-7724
|
CSCD被引
2
次
|
|
|
|
|
12.
陈晶阳. 铸造镍基高温合金K439b的组织及典型性能.
金属热处理,2023,48(1):100-104
|
CSCD被引
6
次
|
|
|
|
|
13.
基什金S T. 铸造镍基高温合金中的碳化物强化.
航空材料学报,1991,11(2):1-8
|
CSCD被引
4
次
|
|
|
|
|
14.
张明军. 固溶冷速对CHS-104合金显微组织和高温力学性能的影响.
热加工工艺,2013,42(10):216-219
|
CSCD被引
4
次
|
|
|
|
|
15.
吴凯. 固溶冷却速度和前处理对新型镍基粉末高温合金组织与显微硬度的影响.
稀有金属材料与工程,2012,41(4):685-691
|
CSCD被引
7
次
|
|
|
|
|
16.
胥国华. 固溶冷却速度对GH4586合金组织及850℃拉伸性能的影响.
材料热处理学报,2006,27(2):47-49
|
CSCD被引
11
次
|
|
|
|
|
17.
Qin X Z. Effects of long-term thermal exposure on the microstructure and properties of a cast Nibase superalloy.
Metallurgical and Materials Transactions A,2007,38:3014-3022
|
CSCD被引
32
次
|
|
|
|
|
18.
孙文. 铸造镍基高温合金中初生MC碳化物的退化过程和机理.
金属学报,2016,52(4):455-462
|
CSCD被引
13
次
|
|
|
|
|
了解气象卫星更多信息，请访问