A231变形镁合金锰系转化膜溶液中锰消耗对膜性能的影响
Effect of Mn~2+ Consumption in Phosphate Conversion Solution on Performance of Phosphorized Films on A231 Magnesium Alloy Surface
查看参考文献7篇
|
文摘
|
应用化学分析方法对镁合金转化膜溶液中锰离子的浓度进行分析,使用电化学工作站和SEM对膜层的耐蚀性、形貌和成分进行表征.结果表明:随着处理面积的增加,锰离子浓度线性减少,耐蚀性变化范围不大;当处理面积达到100 dm~2/L后,膜层表面微观裂纹变得较宽 |
|
其他语种文摘
|
Chemical analysis method was used to determine the Mn2+ consumption due to phosphorization of A231 Mg alloy in a magnesium phosphate conversion solution. Then electrochemical test and SEM were employed to examined the corrosion resistance and the morphology of the conversion films. Results showed that with the increase amount of treated surface area, the concentration of Mn~2+ decreased linearly but the corrosion resistance of the phosphorized films did not change obviously;however, when the amount of treated surface area exceed 100 dm~2/L, micro cracks in the coating became wide |
|
来源
|
腐蚀科学与防护技术
,2010,22(5):377-379 【核心库】
|
|
关键词
|
锰离子
;
镁合金
;
转化膜处理液
;
耐蚀性
|
|
地址
|
1.
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
2.
重庆理工大学材料科学与工程学院, 重庆, 400050
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
;
重庆市科技攻关项目
|
|
文献收藏号
|
CSCD:4037866
|
参考文献 共
7
共1页
|
|
1.
周学华. 镁合金化学转化膜.
腐蚀与防护,2004,25(11):468
|
CSCD被引
24
次
|
|
|
|
|
2.
周婉秋. 镁合金的腐蚀行为与表面防护方法.
材料保护,2002,35(7):1
|
CSCD被引
52
次
|
|
|
|
|
3.
Gray J E. Protective coatings on magnesium and its alloys.
J. Alloys Compd,2002,336:88
|
CSCD被引
482
次
|
|
|
|
|
4.
刘锋. 钙对镁合金表面锰系转化膜的影响.
中国有色金属学报,2008,18(10):1825
|
CSCD被引
7
次
|
|
|
|
|
5.
徐红娣.
常用电镀溶液的分析(第三版),1993:394
|
CSCD被引
1
次
|
|
|
|
|
6.
Zhao M. Growth of multi-elements complex coating on A291D magnesium alloy through conversion treatment.
J. Alloys Compd,2007,427:310
|
CSCD被引
10
次
|
|
|
|
|
7.
鲁维国. 磷化促进剂.
表面技术,2002,31(6):12
|
CSCD被引
5
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问