纳米TiO2/聚氨酯复合涂层的光催化活性研究
Research of photocatalytic activity of nano-TiO2/polyurethane composite coating
查看参考文献8篇
|
文摘
|
用纳米二氧化钛浓缩浆制成了纳米TiO2/聚氨酯复合涂料.纳米TiO2/聚氨酯复合涂层的TEM观察和光催化实验表明,这种复合涂层中的纳米粒子分散均匀,无团聚体,并且具有良好的光催化活性.随着颜基比的增大,复合涂层的反应速率常数增大,光催化活性提高.在二氧化钛粒径不大于250nm时,复合涂层的反应速率常数和光催化活性在二氧化钛粒径为100nm处有一最大值. |
|
其他语种文摘
|
Nano-Ti02/polyurethane composite coating was prepared by the nano-TiO2 concentrates, TEM inves-tigation and photocatalytic experimental results indicated that the nanoparticles in the composite coating were dispersed uniformly and were not aggregated, and has good photocatalytic activity. With the increase of pigment binder ratio, rate constant and photocatalytic activity of composite coating increase. As nano-TiC>2 size is not greater than 250nm, rate constant and photocatalytic activity of composite coating have a maximum at lOOnm. |
|
来源
|
功能材料
,2005,36(1):129-132 【核心库】
|
|
关键词
|
光催化
;
纳米材料
;
纳米浓缩浆
;
聚氨酯
;
涂料
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-9731 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家973计划
|
|
文献收藏号
|
CSCD:1866090
|
参考文献 共
8
共1页
|
|
1.
Fujishima A. [J].
Nature,1972,238(7):37
|
CSCD被引
2960
次
|
|
|
|
|
2.
Yamazaki-Nishida S. [J].
J Photochem Photobiol A: Chem,1993,70:95
|
CSCD被引
1
次
|
|
|
|
|
3.
Canela M C. [J].
Journal of Photochemistry and Photobiotogy A: Chemistry,1998,112:73
|
CSCD被引
11
次
|
|
|
|
|
4.
胡安正. 纳米TiO_2光催化材料及其应用于环境保护的研究进展.
功能材料,2001,32(6):586
|
CSCD被引
19
次
|
|
|
|
|
5.
刘福春. [P].
中国发明专利:CN1410490A,2001
|
CSCD被引
1
次
|
|
|
|
|
6.
刘福春. [P].
中国发明专利:CN1427052A,2001
|
CSCD被引
1
次
|
|
|
|
|
7.
张梅. [J].
化工新型材料,2000,28(4):11
|
CSCD被引
24
次
|
|
|
|
|
8.
余家国. [J].
中国粉体技术,2000,6(2):7
|
CSCD被引
6
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问