粉末高温合金FGH96原始颗粒边界及高温原位高周疲劳研究
Prior Particle Boundary of PM FGH96 Superalloy and Its In-situ High-cycle Fatigue at Elevated Temperature

查看参考文献17篇

周静怡 1   刘昌奎 1 *   赵文侠 1   郑真 1   钟燕 2  
文摘 利用扫描电镜原位观察的方法研究了粉末高温合金FGH96中不同级别的原始颗粒边界(PPB)在550℃下对合金高周疲劳力学行为的影响。结果表明:采用等离子旋转电极(PREP)制粉+热等静压(HIP)工艺制备的FGH96合金中PPB主要由大尺寸γ'相和碳化物组成;不同级别的PPB对高周疲劳裂纹萌生和扩展均无显著影响,裂纹萌生于晶粒内部,裂纹扩展受晶界与应力轴角度影响,穿晶或沿晶扩展;在裂纹快速扩展区和瞬断区,PPB级别严重的FGH96合金断口呈现穿晶和沿PPB断裂的形貌。
其他语种文摘 The influence of different grades of prior particle boundary(PPB) in PM FGH96 superalloy during high-cycle fatigue test at 550 ℃ was investigated by the in-situ fatigue test in SEM.The results show that the PPB in P /M FGH96 superalloys by plasma rotating electrode process(PREP) + hot isostatic press(HIP) is constituted of large size γ' and carbide.There are no significant effect on the initiation and propagation of high cycle fatigue crack in different grades of PPB.Crack initiation is initiated in the grain interior,and the propagation is transgranular or intergranular,which is influenced by the angle between the grain boundary and the stress axis.In the fast crack growth zone and the transient zone,the fracture characteristics of serious grade PPB FGH96 superalloy are transgranular and along PPB globular surfaces.
来源 航空材料学报 ,2017,37(5):83-89 【核心库】
DOI 10.11868/j.issn.1005-5053.2016.000130
关键词 粉末高温合金 ; FGH96 ; 原始颗粒边界 ; 原位疲劳
地址

1. 中国航发北京航空材料研究院, 航空材料检测与评价北京市重点实验室;;材料检测与评价航空科技重点实验室, 北京, 100095  

2. 中国燃气涡轮研究院, 成都, 610500

语种 中文
文献类型 研究性论文
ISSN 1005-5053
学科 航空
基金 中国航空科学基金
文献收藏号 CSCD:6097847

参考文献 共 17 共1页

1.  张家锋. FGH96粉末高温合金涡轮盘淬火过程界面换热系数的研究. 航空材料学报,2010,30(1):26-29 CSCD被引 3    
2.  马铁军. 粉末高温合金FGH96线性摩擦焊接头组织与力学性能. 材料工程,2014(10):11-15 CSCD被引 3    
3.  李楠. 激光快速成型FGH96高温合金的显微组织及缺陷分析. 失效分析与预防,2016,11(2):125-128 CSCD被引 1    
4.  Crompton J S. Analysis of second particles in a powder metallurgy HIP nickel-base superalloy. Journal of Materials Science,1986,21(10):3445-3454 CSCD被引 3    
5.  Zhang M J. Effect of heat treatment on the micro-indentation behavior of powder metallurgy nickel based superalloy FGH96. Materials and Design,2013,49(49):705-715 CSCD被引 5    
6.  刘新灵. 粉末高温合金缺陷特性及寿命预测方法研究进展和思考. 材料导报,2013,27(21):92-96 CSCD被引 9    
7.  刘丽玉. 发动机粉末合金高压涡轮盘断裂的原因. 机械工程材料,2014,38(8):108-112 CSCD被引 8    
8.  毛健. 粉末高温合金颗粒界面及断裂研究. 金属学报,1993,29(4):187-191 CSCD被引 8    
9.  Carol M. Prior particle boundary precipitation in Ni-base superalloys. The International Journal of Powder Metallurgy,1989,25(4):301-308 CSCD被引 6    
10.  马文斌. 粉末高温合金FGH96中的原始粉末颗粒边界及其对合金拉伸断裂行为的影响. 粉末冶金材料科学与工程,2013,18(1):1-7 CSCD被引 8    
11.  胡文波. FGH96合金原始颗粒边界(PPB)及其对冲击性能的影响. 粉末冶金技术,2012,30(5):327-333 CSCD被引 5    
12.  张莹. 颗粒间断裂在P/M镍基高温合金低周疲劳断口上的特征. 中国有色金属学报,2013,23(4):987-996 CSCD被引 9    
13.  Ingesten N G. Nature and origin of previous particle boundary precipitates in P/ M superalloys. High Temperature Alloys for Gas Turbines,1982:1013-1027 CSCD被引 2    
14.  Rao G A. Effect of oxygen content of powder on microstructure and mechanical properties of hot isotatically pressed superalloy Inconel 718. Materials Science and Engineering: A,2006,435/436:84-99 CSCD被引 20    
15.  赵军普. 粉末冶金高温合金中的原始颗粒边界(PPB)问题. 粉末冶金工业,2010,20(4):43-49 CSCD被引 21    
16.  魏振伟. GH536镍基高温合金焊接接头力学性能与断裂特征研究. 航空材料学报,2015,35(5):70-74 CSCD被引 4    
17.  Beevers C J. Fatigue crack growth characteristics at low stress in tensities of metals and allays. Metal Sci,1977,91(8):362-367 CSCD被引 1    
引证文献 8

1 刘昌奎 粉末尺寸和氧含量对FGH96合金中PPB形成的影响 兵器材料科学与工程,2018,41(3):33-38
CSCD被引 4

2 刘昌奎 热变形工艺对FGH96高温合金PPB析出相及组织的影响 航空材料学报,2018,38(3):40-45
CSCD被引 8

显示所有8篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号