粉末高温合金FGH96原始颗粒边界及高温原位高周疲劳研究
Prior Particle Boundary of PM FGH96 Superalloy and Its In-situ High-cycle Fatigue at Elevated Temperature
查看参考文献17篇
|
文摘
|
利用扫描电镜原位观察的方法研究了粉末高温合金FGH96中不同级别的原始颗粒边界(PPB)在550℃下对合金高周疲劳力学行为的影响。结果表明:采用等离子旋转电极(PREP)制粉+热等静压(HIP)工艺制备的FGH96合金中PPB主要由大尺寸γ'相和碳化物组成;不同级别的PPB对高周疲劳裂纹萌生和扩展均无显著影响,裂纹萌生于晶粒内部,裂纹扩展受晶界与应力轴角度影响,穿晶或沿晶扩展;在裂纹快速扩展区和瞬断区,PPB级别严重的FGH96合金断口呈现穿晶和沿PPB断裂的形貌。 |
|
其他语种文摘
|
The influence of different grades of prior particle boundary(PPB) in PM FGH96 superalloy during high-cycle fatigue test at 550 ℃ was investigated by the in-situ fatigue test in SEM.The results show that the PPB in P /M FGH96 superalloys by plasma rotating electrode process(PREP) + hot isostatic press(HIP) is constituted of large size γ' and carbide.There are no significant effect on the initiation and propagation of high cycle fatigue crack in different grades of PPB.Crack initiation is initiated in the grain interior,and the propagation is transgranular or intergranular,which is influenced by the angle between the grain boundary and the stress axis.In the fast crack growth zone and the transient zone,the fracture characteristics of serious grade PPB FGH96 superalloy are transgranular and along PPB globular surfaces. |
|
来源
|
航空材料学报
,2017,37(5):83-89 【核心库】
|
|
DOI
|
10.11868/j.issn.1005-5053.2016.000130
|
|
关键词
|
粉末高温合金
;
FGH96
;
原始颗粒边界
;
原位疲劳
|
|
地址
|
1.
中国航发北京航空材料研究院, 航空材料检测与评价北京市重点实验室;;材料检测与评价航空科技重点实验室, 北京, 100095
2.
中国燃气涡轮研究院, 成都, 610500
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-5053 |
|
学科
|
航空 |
|
基金
|
中国航空科学基金
|
|
文献收藏号
|
CSCD:6097847
|
参考文献 共
17
共1页
|
|
1.
张家锋. FGH96粉末高温合金涡轮盘淬火过程界面换热系数的研究.
航空材料学报,2010,30(1):26-29
|
CSCD被引
3
次
|
|
|
|
|
2.
马铁军. 粉末高温合金FGH96线性摩擦焊接头组织与力学性能.
材料工程,2014(10):11-15
|
CSCD被引
3
次
|
|
|
|
|
3.
李楠. 激光快速成型FGH96高温合金的显微组织及缺陷分析.
失效分析与预防,2016,11(2):125-128
|
CSCD被引
1
次
|
|
|
|
|
4.
Crompton J S. Analysis of second particles in a powder metallurgy HIP nickel-base superalloy.
Journal of Materials Science,1986,21(10):3445-3454
|
CSCD被引
3
次
|
|
|
|
|
5.
Zhang M J. Effect of heat treatment on the micro-indentation behavior of powder metallurgy nickel based superalloy FGH96.
Materials and Design,2013,49(49):705-715
|
CSCD被引
5
次
|
|
|
|
|
6.
刘新灵. 粉末高温合金缺陷特性及寿命预测方法研究进展和思考.
材料导报,2013,27(21):92-96
|
CSCD被引
10
次
|
|
|
|
|
7.
刘丽玉. 发动机粉末合金高压涡轮盘断裂的原因.
机械工程材料,2014,38(8):108-112
|
CSCD被引
8
次
|
|
|
|
|
8.
毛健. 粉末高温合金颗粒界面及断裂研究.
金属学报,1993,29(4):187-191
|
CSCD被引
8
次
|
|
|
|
|
9.
Carol M. Prior particle boundary precipitation in Ni-base superalloys.
The International Journal of Powder Metallurgy,1989,25(4):301-308
|
CSCD被引
6
次
|
|
|
|
|
10.
马文斌. 粉末高温合金FGH96中的原始粉末颗粒边界及其对合金拉伸断裂行为的影响.
粉末冶金材料科学与工程,2013,18(1):1-7
|
CSCD被引
8
次
|
|
|
|
|
11.
胡文波. FGH96合金原始颗粒边界(PPB)及其对冲击性能的影响.
粉末冶金技术,2012,30(5):327-333
|
CSCD被引
5
次
|
|
|
|
|
12.
张莹. 颗粒间断裂在P/M镍基高温合金低周疲劳断口上的特征.
中国有色金属学报,2013,23(4):987-996
|
CSCD被引
9
次
|
|
|
|
|
13.
Ingesten N G. Nature and origin of previous particle boundary precipitates in P/ M superalloys.
High Temperature Alloys for Gas Turbines,1982:1013-1027
|
CSCD被引
2
次
|
|
|
|
|
14.
Rao G A. Effect of oxygen content of powder on microstructure and mechanical properties of hot isotatically pressed superalloy Inconel 718.
Materials Science and Engineering: A,2006,435/436:84-99
|
CSCD被引
21
次
|
|
|
|
|
15.
赵军普. 粉末冶金高温合金中的原始颗粒边界(PPB)问题.
粉末冶金工业,2010,20(4):43-49
|
CSCD被引
21
次
|
|
|
|
|
16.
魏振伟. GH536镍基高温合金焊接接头力学性能与断裂特征研究.
航空材料学报,2015,35(5):70-74
|
CSCD被引
4
次
|
|
|
|
|
17.
Beevers C J. Fatigue crack growth characteristics at low stress in tensities of metals and allays.
Metal Sci,1977,91(8):362-367
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问