Cu含量对2219铝合金锻件及其焊接接头组织与性能的影响
Effect of Cu Content on Microstructure and Properties of 2219 Aluminum Alloy Forgings and Its Welded Joints
查看参考文献17篇
|
文摘
|
采用力学拉伸实验、焊接实验、电化学阻抗谱(EIS) 、循环阳极极化曲线(Tafel)以及金相和扫描电镜(SEM)等分析测试方法,研究Cu含量对2219铝合金锻件组织与性能的影响。结果表明:降低Cu含量,有利于减少2219铝合金基体内的残余结晶相,并有效抑制在合金焊接过程中粗大Al_2Cu相的析出,使基材和焊件的伸长率显著提高,强度略有下降; Cu在铝基体中形成Al_2Cu相诱导合金发生局部腐蚀,使材料的耐腐蚀性能变差,降低Cu含量能够减小合金的腐蚀倾向,改善合金的耐腐蚀性能。 |
|
其他语种文摘
|
The influence of Cu content on microstructure and properties of 2219 aluminum alloy was investigated by using tensile tests, welding tests,electrochemical impedance spectroscopy (EIS),cyclic anodic polarization curves (Tafel) combined with optical microscopy (OM) and scanning electron microscopy analysis (SEM). The results indicate that the residual crystal phase in the matrix of 2219 aluminum alloy is reduced with the decrease of Cu content which contributed to effectively suppress the precipitation of Al_2Cu coarse phase during the welding process. Furthermore,with the decrease of Cu content,elongation of the alloy is significantly increased, while the tensile strength and yield strength is slightly decreased. At the same time,Al_2Cu phase formed in the matrix induces localized corrosion which causes the deterioration of corrosion resistance in the alloy,while the corrosion tendency of the alloy can be reduced by the decrease of Cu content and the corrosion resistance of the alloy is improved. |
|
来源
|
航空材料学报
,2017,37(3):1-8 【核心库】
|
|
DOI
|
10.11868/j.issn.1005-5053.2016.000226
|
|
关键词
|
2219铝合金
;
Cu含量
;
Al_2Cu相
;
腐蚀
;
焊接
|
|
地址
|
1.
中南大学轻合金研究院, 有色金属先进结构材料与制造协同创新中心, 长沙, 410083
2.
中南大学轻合金研究院, 有色金属先进结构材料与制造协同创新中心;;粉末冶金国家重点实验室, 长沙, 410083
3.
中南大学, 有色金属先进结构材料与制造协同创新中心;;粉末冶金国家重点实验室, 长沙, 410083
4.
北京宇航系统工程研究所, 北京, 100076
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-5053 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金重大项目
;
江苏省科技成果转化计划
;
国家自然科学基金委员会—中国航天科技集团公司航天先进制造技术研究联合基金资助项目
;
国家重点研发计划
|
|
文献收藏号
|
CSCD:6005810
|
参考文献 共
17
共1页
|
|
1.
Immarigeon J P. Lightweight materials for aircraft applications.
Materials Characterization,1995,35(1):41-67
|
CSCD被引
53
次
|
|
|
|
|
2.
刘欣. 重型运载火箭关键制造技术发展展望.
航天制造技术,2013,1(1):1-6
|
CSCD被引
36
次
|
|
|
|
|
3.
Narayana G V. Fracture behavior of aluminum alloy 2219-T87 welds plates.
Science and Technology of Welding and Joining,2004,9(2):121-130
|
CSCD被引
22
次
|
|
|
|
|
4.
姚君山. 航天贮箱结构材料及其焊接技术的发展.
航天制造技术,2002,1(5):17-22
|
CSCD被引
15
次
|
|
|
|
|
5.
Grilli R. Localized corrosion of a 2219 aluminum alloy exposed to a 3.5% NaCl solution.
Corrosion Science,2010,52(9):2855-2866
|
CSCD被引
27
次
|
|
|
|
|
6.
Li Q. Fracture behavior of double-pass TIG welded 2219-T8 aluminum alloy joints under transverse tensile test.
Transactions of Nonferrous Metals Society of China,2015,25(6):1794-1803
|
CSCD被引
5
次
|
|
|
|
|
7.
An L H. Effect of pre-deformation on microstructure and mechanical properties of 2219 aluminum alloy sheet by thermomechanical treatment.
The Chinese Journal of Nonferrous Metals,2012,22(2):370-375
|
CSCD被引
1
次
|
|
|
|
|
8.
刘燕.
贮箱用2219铝合金热处理工艺的研究,2013:17-52
|
CSCD被引
1
次
|
|
|
|
|
9.
何跃.
高强Al-Cu合金2219及其焊接接头的局部腐蚀敏感性研究,2005:36-66
|
CSCD被引
1
次
|
|
|
|
|
10.
杜辉.
时效对2219铝合金VPTIG焊接结构性能影响研究,2012:19-42
|
CSCD被引
1
次
|
|
|
|
|
11.
张聃. 2219铝合金及其焊接接头电化学腐蚀行为.
电焊机,2013,43(10):14-17
|
CSCD被引
3
次
|
|
|
|
|
12.
孙擎擎. 时效制度对挤压Al-6.2Zn-2.3Mg-2.3Cu铝合金电化学腐蚀性能的影响.
中国有色金属学报,2015,25(4):866-874
|
CSCD被引
16
次
|
|
|
|
|
13.
Reddy G M. Influence of welding techniques on microstructure and pitting corrosion behavior of 1441 grade Al-Li alloy gas tungsten arc welds.
British Corrosion Journal,2001,36(4):304-309
|
CSCD被引
1
次
|
|
|
|
|
14.
孙擎擎. 大气污染物对7B50铝合金电化学腐蚀性能的影响.
中国有色金属学报,2015,25(3):575-581
|
CSCD被引
11
次
|
|
|
|
|
15.
李学朝.
铝合金材料组织与金相图谱,2010:201-203
|
CSCD被引
3
次
|
|
|
|
|
16.
吴龙飞.
2219铝合金TIG焊接性研究,2007:32-40
|
CSCD被引
1
次
|
|
|
|
|
17.
陈建. 高强铝合金焊接接头SCC机理的探讨.
焊接学报,1990,11(2):91-98
|
CSCD被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问