[110]取向镍基单晶合金在蠕变过程中的组织演变
Microstructure Evolution in a Nickel-base Single Crystal Superalloy with [110] Orientation during Creep Process
查看参考文献11篇
|
文摘
|
研究了一种[110]取向的镍基单晶高温合金在1 040℃、150 MPa和850℃、500 MPa条件下的蠕变性能、蠕变过程中γ'相的形貌演变以及γ'相的筏化机理,并对拉断后试样的纵向截面进行了SEM形貌观察.结果表明:在1 040℃、150 MPa条件下,沿[110]取向施加应力拉伸时,合金中γ'相形成了与应力轴成45°角的层片状筏化组织;距断口不同位置处γ'相的粗化程度存在明显差异;而在850℃、500 MPa条件下,拉伸蠕变后合金中γ'相没有发生明显的粗化现象. |
|
其他语种文摘
|
The tensile creep tests were conducted on a Ni-base single crystal superalloy with [110] orientation under the conditions of 1 040 ℃/150 MPa and 850 ℃/500 MPa, respectively. The creep properties and the microstructure evolution during the creep process were investigated. The longitudinal section morphology of the tensile fracture was observed by SEM. The results show that the γ' phase of the Ni-base single crystal superalloy with [110] orientation formed the lamellar-type raft structure with inclined 45?with the stress axis under the condition of 1 040 ℃/150 MPa. There was evident difference in the degree of γ' phase coarsening at different distances away from the fractured surface. However, the γ' phase was not coarsened obviously under the condition of 850 ℃/500 MPa. |
|
来源
|
机械工程材料
,2009,33(6):6-9 【核心库】
|
|
关键词
|
镍基单晶高温合金
;
拉伸蠕变
;
γ'相
;
筏化组织
|
|
地址
|
1.
沈阳理工大学材料科学与工程学院, 辽宁, 沈阳, 110168
2.
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1000-3738 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:3538376
|
参考文献 共
11
共1页
|
|
1.
水丽. 预压缩处理对镍基单晶高温合金蠕变变形机制的影响.
金属学报,2007,43(1):47-52
|
CSCD被引
4
次
|
|
|
|
|
2.
TAKAO M. Creep behavior of Ni-base single crystal superalloys with various γ' volume fraction.
Acta Metal,2004(52):3737-3744
|
CSCD被引
1
次
|
|
|
|
|
3.
PEARSON D D. Stress coarsening of γ' and its influence on creep properties of a single crystal superalloy.
Superalloys 1984,1984:513-522
|
CSCD被引
4
次
|
|
|
|
|
4.
SHAH D M. Orientation dependence of creep behavior of single crystal γ' (Ni_3Al).
Scripta Metall,1983,17:997-1002
|
CSCD被引
4
次
|
|
|
|
|
5.
刘金来. 一种镍基单晶高温合金高温持久性能的各向异性.
金属学报,2001,37(12):1233-1237
|
CSCD被引
19
次
|
|
|
|
|
6.
任英磊. 热处理制度对一种单晶镍基高温合金γ′相形貌演化的影响.
机械工程材料,2001,25(4):7-10
|
CSCD被引
12
次
|
|
|
|
|
7.
MACKAY R A. The influence of orientation on the stress rupture properties of nickel-basc superalloy single crystals.
Metallurgical and Materials A,1982,13(10):1947-1454
|
CSCD被引
1
次
|
|
|
|
|
8.
刘金来. 晶体取向对镍基单晶高温合金铸态组织和偏析的影响.
中国有色金属学报,2002,12(4):764-768
|
CSCD被引
4
次
|
|
|
|
|
9.
ZHOU L. Three-dimensional finite element analysis of stresses and energy density distributions around γ' before coarsening loaded in the[110] direetion in Ni-based superalloy mater.
Materials Science and Engineering A,2003,352(1/2):300-307
|
CSCD被引
6
次
|
|
|
|
|
10.
田素贵. 单晶Ni基合金高温蠕变期间γ'定向粗化驱动力的有限元分析.
金属学报,2000,36(5):465-471
|
CSCD被引
12
次
|
|
|
|
|
11.
田素贵. 一种单晶镍基合金蠕变初期的位借组态.
金属学报,1998,34(2):123-126
|
CSCD被引
7
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问