固溶时间对Ti-5553显微组织及拉伸性能的影响
Effect of Solution Time on Microstructures and Mechanical Properties of Ti-5553 Alloy
查看参考文献22篇
|
文摘
|
研究了两相区不同固溶时间对Ti-5553合金显微组织及拉伸性能影响。利用扫描电镜观察显微组织随固溶时间的演化行为,重点分析了初生α相(α_p)比例及长宽比分布随固溶时间的变化规律,利用EBSD技术表征了固溶保温阶段晶界α相及晶内α的晶体取向演化,利用电子万能试验机进行了室温拉伸性能测试。结果表明:随着固溶时间的增加,初生α比例降低,等轴化程度增加,进一步导致拉伸塑性变形过程中位错运动的阻力及合金强度降低;晶界α_p在固溶过程中是以“热切口”的形式发生截断,然而截断部分晶体取向仍保持一致。 |
|
其他语种文摘
|
The effects of varied solution time on the microstructures and tensile properties in α+β phase field of Ti-5553 alloy were studied.The volume fraction and Feret ratio distribution of primary α (α_p) with varied solution time were emphatically analyzed.The microstructures of Ti-5553 alloy were observed by SEM.The orientation evolution of grain boundary primary α and intragranular α phase during solution was characterized by EBSD technique.The tensile properties were tested by an electronic universal testing machine.The results show that the volume fraction of α_p decreases with the extension of solution time;meanwhile,the equiaxation and coarsening of α_p decrease the resistance to dislocation movement,which result in the decrease of strength and the increase of plasticity.The grain boundary α_p is truncated in the form of “hot trench” during solution process;however the truncated grain boundary α_p maintains the same orientation. |
|
来源
|
稀有金属材料与工程
,2020,49(3):985-989 【核心库】
|
|
关键词
|
Ti-5553
;
初生α相
;
显微组织
;
力学性能
|
|
地址
|
1.
东北大学, 辽宁, 沈阳, 110819
2.
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
中国科学院战略性科技先导专项(B类)
|
|
文献收藏号
|
CSCD:6688013
|
参考文献 共
22
共2页
|
|
1.
Kasemer M.
Acta Materialia,2017,136:288
|
CSCD被引
6
次
|
|
|
|
|
2.
赵勇.
新技术新工艺,2016(5):94
|
CSCD被引
2
次
|
|
|
|
|
3.
Li Shujian. Formation, Influence Mechanism and Experimental Characterization of Composite Porosity.
Rare Metal Materials and Engineering,2016,45(9):2282
|
CSCD被引
7
次
|
|
|
|
|
4.
Raupach M R.
Proceedings of the National Academy of Sciences,2007,104(24):10288
|
CSCD被引
43
次
|
|
|
|
|
5.
Boyer R R.
Journal of Materials Engineering and Performance,2005,14(6):681
|
CSCD被引
92
次
|
|
|
|
|
6.
Weiss I.
Materials Science and Engineering A,1998,243(1/2):46
|
CSCD被引
120
次
|
|
|
|
|
7.
Stefansson N.
Metallurgical and Materials Transactions A,2003,34(3):691
|
CSCD被引
64
次
|
|
|
|
|
8.
Banerjee D.
Acta Materialia,2013,61(3):844
|
CSCD被引
324
次
|
|
|
|
|
9.
王琛. 热处理对TC18钛合金组织和力学性能的影响.
金属热处理,2018,43(9):186
|
CSCD被引
6
次
|
|
|
|
|
10.
Semiatin S L.
Metallurgical and Materials Transactions A,2003,34(10):2377
|
CSCD被引
36
次
|
|
|
|
|
11.
王清江. 高温钛合金的现状与前景.
航空材料学报,2014,34(4):1
|
CSCD被引
98
次
|
|
|
|
|
12.
Fan J.
Materials Characterization,2014,96:93
|
CSCD被引
3
次
|
|
|
|
|
13.
Fan J.
Materials & Design,2015,83:499
|
CSCD被引
9
次
|
|
|
|
|
14.
Wain N.
Materials Science and Engineering A,2010,527(29/30):7673
|
CSCD被引
12
次
|
|
|
|
|
15.
Warchomicka F.
Materials Science and Engineering A,2011,528(28):8277
|
CSCD被引
42
次
|
|
|
|
|
16.
Ren L.
Materials Science and Engineering A,2018,711:553
|
CSCD被引
22
次
|
|
|
|
|
17.
Wang S.
Scripta Materialia,2019,170:161
|
CSCD被引
4
次
|
|
|
|
|
18.
Gao X.
Acta Materialia,2017,122:298
|
CSCD被引
23
次
|
|
|
|
|
19.
Huang S.
Journal of Alloys and Compounds,2019,791:575
|
CSCD被引
4
次
|
|
|
|
|
20.
Nag S.
Philosophical Magazine,2009,89(6):535
|
CSCD被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问