超高压凝固条件下Mg-6zn-3Y合金的晶体形态及相演变
CRYSTAL MORPHOLOGIES AND THE PHASES IN THE Mg-6Zn-3Y ALLOY SOLIDIFIED UNDER SUPER-HIGH PRESSURE
查看参考文献23篇
|
文摘
|
利用扫描电镜(SEM)并配合能谱(EDS)分析研究了超高压凝固Mg-6Zn-3Y合金的晶体形态和相演变.实验结果表明:随着凝固压力的增大,α-Mg晶体的形态发生了粗大树枝晶→超细树枝晶→胞状晶转变,即晶体的生长方式逐渐由树枝晶生长→胞状生长过渡.GPa级超高压下凝固极大地提高了Zn在基体中的溶解度,使之成为过饱和固溶体,并随着凝固压力的增大促使Zn的分布趋于均匀化.Mg-6Zn-3Y合金在2 GPa超高压凝固条件下形成了新相Y固溶体,室温组织由4相组成;在6 GPa超高压凝固条件下大量粒状相均匀弥散地分布在基体上,Mg-6Zn-3Y合金的硬度显著提高. |
|
其他语种文摘
|
The solidification microstructure of Mg-6Zn 3Y alloy under super-high pressure was investigated by SEM and EDS.The results show that solidification microstructure of Mg-6Zn-3Y alloy under super high pressure(GPa level) could be evidently refined and was further refined with the increase of solidification pressure.Solubility of Zn in the alloy reached up to 1.64%under 4 GPa pressure which was increased by 44%than that under the atmosphere condition.Y is insoluble in the matrix,which resulted in a new phase riched in Y and granular phases which were dispersed in the matrix.The morphology of crystal changes follow:bulky branch crystal→superfine branch crystal→cellular crystal,and the growth of crystal changed from branch growth to cellular growth. |
|
来源
|
金属学报
,2011,47(12):1550-1554 【核心库】
|
|
DOI
|
10.3724/sp.j.1037.2011.00395
|
|
关键词
|
Mg-6Zn-3Y合金
;
超高压凝固
;
晶体形态
;
Y固溶体
;
粒状相
|
|
地址
|
1.
东北大学材料与冶金学院, 沈阳, 110819
2.
燕山大学材料科学与工程学院, 秦皇岛, 066004
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
基金
|
河北省自然科学基金
;
辽宁省自然科学基金
|
|
文献收藏号
|
CSCD:4429638
|
参考文献 共
23
共2页
|
|
1.
曲迎东. 高压作用下合金凝固的研究进展.
铸造,2005,54:539
|
CSCD被引
18
次
|
|
|
|
|
2.
Kumar M.
Physica. B,1995,212:391
|
CSCD被引
7
次
|
|
|
|
|
3.
张锦升（译）.
金属和合金在压力下结晶,1987:23
|
CSCD被引
4
次
|
|
|
|
|
4.
弭光宝. 压力对Al-Si和Mg-Al合金平衡相图作用的残余键结构分析.
中国有色金属学报,2009,12:2074
|
CSCD被引
6
次
|
|
|
|
|
5.
Ebihara T.
J Magn Magn Mater,2004,272/276:e83
|
CSCD被引
3
次
|
|
|
|
|
6.
Wang Z X.
J Alloys Compd,2010,492:529
|
CSCD被引
6
次
|
|
|
|
|
7.
于溪凤.
材料研究学报,2000,14(增刊):141
|
CSCD被引
14
次
|
|
|
|
|
8.
张国志. 超高压凝固Al-Si合金的非平衡组织.
金属学报,1999,35:285
|
CSCD被引
27
次
|
|
|
|
|
9.
Yu X F.
J Mater Sci,1999,34:4149
|
CSCD被引
14
次
|
|
|
|
|
10.
李荣德. 高压凝固ZA43合金的非平衡组织.
特种铸造及有色合金,2003(6):16
|
CSCD被引
10
次
|
|
|
|
|
11.
Wu R I.
J Mater Sci Technol. A,2001,301:12
|
CSCD被引
1
次
|
|
|
|
|
12.
Yao W J.
Mater Sci Eng. A,2003,344:10
|
CSCD被引
6
次
|
|
|
|
|
13.
陈忠伟. 凝固压力对A357合金凝固组织及含Fe相的影响.
铸造,2009,58:887
|
CSCD被引
2
次
|
|
|
|
|
14.
Xu R.
Mater Letts,2006,60:783
|
CSCD被引
16
次
|
|
|
|
|
15.
Kaibyshev F M R.
Mater Sci Eng. A,2003,342:169
|
CSCD被引
4
次
|
|
|
|
|
16.
包艳青. 压力对Zn-22AI合金晶体结构及微观组织的影响.
铸造,2011,60:533
|
CSCD被引
3
次
|
|
|
|
|
17.
刘楚明.
镁合金相图集,2007:334
|
CSCD被引
3
次
|
|
|
|
|
18.
Zhou H T.
Mater Sci Eng. A,2007,445/446:1
|
CSCD被引
16
次
|
|
|
|
|
19.
Yasuo F.
J Phys: Condens Mater,2002,12:10727
|
CSCD被引
1
次
|
|
|
|
|
20.
王振玲.
博士学位论文,2007
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问