文摘
|
在试验合金中,1600℃熔体处理对凝固后组织和性能产生显著影响。经1600℃熔体处理后,合金样品二次枝晶间距显著降低,元素偏析情况得到有效改善,凝固过程析出的TCP相数量明显减少,热处理后γ″析出相也更加细小均匀。熔体处理对合金室温和700℃拉伸强度影响不大,但却显著提高合金的拉伸塑性和700℃/620MPa持久性能。在1600℃熔体处理10min时,合金的综合力学性能最佳;延长熔体处理时间至15min时,合金力学性能呈下降趋势。 |
|
其他语种文摘
|
Effect of melt treatment on the microstructure and mechanical properties of a modified inconel 718C alloy was studied in this paper. The results show that, microstructure of finer dendrite, lower segregation and less amount of Laves phase is obtained after melt treatment. Also, smaller γ" phases with more uniform distribution are precipitating in the specimen via melt treatment. Melt treatment shows no obvious effect on the 25℃ and 700℃ tensile strength, while it evidently improves the tensile plasticity and the stress-rupture property. Specimens via melt treatment at 1600℃ for 10 minutes exhibit best mechanical properties. Extended melt treatment after 10 minutes degrades the mechanical properties. |
|
来源
|
铸造
,2007,56(3):248-250,254 【核心库】
|
|
关键词
|
高温合金
;
熔体处理
;
偏析
;
力学性能
|
|
地址
|
1.
南京理工大学材料科学与工程系, 江苏, 南京, 210094
2.
沈阳中科三耐新材料有限公司, 辽宁, 沈阳, 110179
3.
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4977 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家863计划
|
|
文献收藏号
|
CSCD:2719597
|
|
|
1.
陈光. 熔体过热历史对Ni基高温合金定向凝固界面形态的影响.
金属学报,2001,37(5):488-492
|
CSCD被引
9
次
|
|
|
|
|
2.
陈光.
熔体热历史对定向凝固界面稳定性的影响[博士论文],1999
|
CSCD被引
1
次
|
|
|
|
|
3.
копотухинзъ. Bлияниестроенияи CBOйCTB MеTaллического pacплaBaHA клΙчестBо OTлиBOK.
CTAлъ,1992(7):21-28
|
CSCD被引
1
次
|
|
|
|
|
4.
桂忠楼. 镍基高温合金BTOPT工艺的发展.
航空制造工程,1995(4):12-14
|
CSCD被引
21
次
|
|
|
|
|
5.
SIMS C T.
Superalloy Ⅱ,1st,1987
|
CSCD被引
1
次
|
|
|
|
|
6.
KOLOTUKHIN E V. Structure of molten commercial neckel-base alloys.
Russian Metallurgy,1989(2):6-9,15
|
CSCD被引
1
次
|
|
|
|
|
7.
胡赓祥.
金属学,1980
|
CSCD被引
84
次
|
|
|
|
|
8.
KURZ W.
Fundamentals of Solidification,1986
|
CSCD被引
16
次
|
|
|
了解气象卫星更多信息，请访问