喷丸表面完整性对K4169合金高温疲劳性能的影响
Effect of surface integrity induced by shot peening on high-temperature fatigue property of K4169 alloy
查看参考文献19篇
|
文摘
|
采用表面粗糙度仪、X射线残余应力测试仪和显微硬度计分别对试样表面粗糙度、表面残余应力分布和硬度梯度等表面完整性参数进行表征,研究不同表面完整性状态对K4169合金缺口旋弯试样高温疲劳寿命的影响规律。结果表明:相比未喷丸试样,喷丸试样在632 ℃、450 MPa条件下的中值疲劳寿命提高了10.2~43.9倍;喷丸后疲劳源数量降至单个,疲劳源萌生位置由表面转移至次表层。喷丸试样表面形成了高幅值的表面残余压应力(-941~-1023 MPa),并产生了一定深度的硬化层(0.10~0.32 mm),较大的喷丸强度获得了较大的硬化层深度;喷丸消除了试样表面加工刀痕,并显著降低了表面应力集中系数;喷丸改善了试样表面完整性,是疲劳寿命提升的主要原因。 |
|
其他语种文摘
|
The surface roughness, residual stress and micro-hardness of K4169 alloy specimens were characterized by roughness tester, X-ray diffraction(XRD)stress tester and micro-hardness tester. The results indicate that median fatigue lives of the specimens increased by 10.2-43.9 times after SP treatments compared with untreated specimens. Furthermore, the number of fatigue source decreased to only one and the site of fatigue source transferred from the surface to the subsurface. The harden layer with the depth of 0.10-0.32 mm and the surface residual stress of -941--1023 MPa are obtained. The depth of harden layer increased with the increasing of peening intensity. The grooves obtained from the grinding disappeared and the surface stress concentration intensity decreased largely after SP. The improvement of fatigue life is mainly ascribed to the enhancement of surface integrity induced by SP. |
|
来源
|
航空材料学报
,2023,43(3):42-48 【核心库】
|
|
DOI
|
10.11868/j.issn.1005-5053.2022.000205
|
|
关键词
|
喷丸
;
高温合金
;
疲劳
;
表面完整性
|
|
地址
|
1.
中国航空发动机集团有限公司, 北京, 100097
2.
中国航发北京航空材料研究院, 航空材料先进腐蚀与防护航空科技重点实验室, 北京, 100095
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-5053 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家重大科学与技术专项
;
国家自然科学基金面上项目
;
中国航发创新平台项目
|
|
文献收藏号
|
CSCD:7495485
|
参考文献 共
19
共1页
|
|
1.
Zhang X H. Study on the relation between surface integrity and contact fatigue of carburized gears.
International Journal of Fatigue,2022,165:107203
|
CSCD被引
9
次
|
|
|
|
|
2.
Holmberg J. Surface integrity investigations for prediction of fatigue properties after machining of alloy 718.
International Journal of Fatigue,2021,144:106059
|
CSCD被引
2
次
|
|
|
|
|
3.
Field M. A review of measuring methods for surface integrity.
Ann CIRP,1972,21:219-238
|
CSCD被引
4
次
|
|
|
|
|
4.
Yao C F. Influence of high-speed milling parameter on 3D surface topography and fatigue behavior of TB6 titanium alloy.
Transactions of Nonferrous Metals Society of China,2013,23(3):650-660
|
CSCD被引
19
次
|
|
|
|
|
5.
Prabhakaran S. Laser shock peening without coating induced residual stress distribution, wettability characteristics and enhanced pitting corrosion resistance of austenitic stainless steel.
Applied Surface Science,2018,428:17-30
|
CSCD被引
9
次
|
|
|
|
|
6.
Nagarajan B. Effect of deep cold rolling on mechanical properties and microstructure of nickel-based superalloys.
Materials Science and Engineering:A,2018,728:196-207
|
CSCD被引
3
次
|
|
|
|
|
7.
Bhaumik S K. Fatigue failure of aircraft components.
Engineering Failure Analysis,2008,15(6):675-694
|
CSCD被引
11
次
|
|
|
|
|
8.
谭喜平. K4169镍基高温合金薄壁机匣的热疲劳行为.
特种铸造及有色合金,2018,38(8):880-883
|
CSCD被引
6
次
|
|
|
|
|
9.
Foss B J. Analysis of shot-peening and residual stress relaxation in the nickelbased superalloy RR1000.
Acta Materialia,2013,61(7):2548-2559
|
CSCD被引
15
次
|
|
|
|
|
10.
Bache M R. Environment and time dependent effects on the fatigue response of an advanced nickel based superalloy.
International Journal of Fatigue,2009,31(11):1719-1723
|
CSCD被引
5
次
|
|
|
|
|
11.
Wu D. Surface characterization and fatigue evaluation in GH4169 superalloy:comparing results after finish turning; shot peening and surface polishing treatments.
International Journal of Fatigue,2018,113:222-235
|
CSCD被引
14
次
|
|
|
|
|
12.
Wang J C. Investigations of the effects of combination treatments on the fretting fatigue resistance of GH4169 superalloy at an elevated temperature.
Surface and Coatings Technology,2021,1255758(426):1-11
|
CSCD被引
1
次
|
|
|
|
|
13.
李妍佳. 不同热处理工艺对K4169高温合金组织和力学性能的影响.
航空材料学报,2021,41(4):119-127
|
CSCD被引
3
次
|
|
|
|
|
14.
唐中杰. 镍基高温合金K4169中夹杂物的特征及形成机理.
中国有色金属学报,2015,25(9):2403-2413
|
CSCD被引
14
次
|
|
|
|
|
15.
Lin L. Grain refinement of superalloy K4169 by addition of refiners: cast structure and refinement mechanisms.
Materials Science & Engineering A,2005,394(1/2):1-8
|
CSCD被引
21
次
|
|
|
|
|
16.
罗学昆. 激光冲击/喷丸复合强化对K4169铸造合金的表面完整性和疲劳性能的影响.
航空制造技术,2022,65(11):57-62
|
CSCD被引
4
次
|
|
|
|
|
17.
Li J K. An analysis of stress concentrations caused by shot peening and its application in predicting fatigue strength.
Fatigue & Fracture of Engineering Materials & Structures,1992,15(12):1271-1279
|
CSCD被引
12
次
|
|
|
|
|
18.
Kumar D. Microstructural characteristics and strengthening mechanisms in a polycrystalline Ni-based superalloy under deep cold rolling.
Materials Science and Engineering: A,2019,753:285-299
|
CSCD被引
3
次
|
|
|
|
|
19.
Xu Z. The influence of shot peening on the fatigue response of Ti-6Al-4V surfaces subject to different machining processes.
International Journal of Fatigue,2018,111:196-207
|
CSCD被引
10
次
|
|
|
|
|
了解气象卫星更多信息，请访问