Bainite Transformation of Low-carbon and Boron-containing Steel under Continuous Cooling
查看参考文献15篇
|
文摘
|
The effects of deformation temperature and strain on bainite transformation of low carbon steel and boron-containing steel were investigated under continuous cooling conditions by means of dilatometric measurement and microstructure observation. The results show that with decreasing the deformation temperature from 1000 to 800 ℃ and increasing strains, bainite start temperature for boron-containing low carbon steel increases, whereas it decreases for low carbon steel under the same condition. The bainite microstructures are easily obtained for boron-containing steel deformed at different temperatures and different strains compared with plain low carbon steel. With increasing the continuous cooling rate, the bainite start temperature under deformed condition is about 20 ℃ higher than that under undeformed condition for boron-containing steel, but it changes slightly when the cooling rate is 20 ℃/s or more. |
|
来源
|
Journal of Iron and Steel Research
, International,2014,21(3):359-363 【核心库】
|
|
DOI
|
10.1016/s1006-706x(14)60055-8
|
|
关键词
|
bainite start temperature
;
boron-containing steel
;
phase transformation
;
bainite
|
|
地址
|
Institute of Metallurgical Resources and Environmental Engineering, Northeastern University, Liaoning Key Laboratory of Metallurgical Resources Circulation Science, Liaoning, Shenyang, 110819
|
|
语种
|
英文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1006-706X |
|
学科
|
冶金工业 |
|
基金
|
国家863计划
|
|
文献收藏号
|
CSCD:5097721
|
参考文献 共
15
共1页
|
|
1.
Ohtani H.
Metall. Mater. Trans. A,1990,21:877-888
|
CSCD被引
18
次
|
|
|
|
|
2.
Yamamoto S.
ISIJ Int,1995,35:1020-1026
|
CSCD被引
9
次
|
|
|
|
|
3.
Djahazi M.
Mater. Sci. Tech,1992,8:628-636
|
CSCD被引
5
次
|
|
|
|
|
4.
Ohmori Y.
Scripta Mater,2002,47:201-206
|
CSCD被引
3
次
|
|
|
|
|
5.
Muddle B C.
Scripta Mater,2002,47:187-192
|
CSCD被引
2
次
|
|
|
|
|
6.
Shang C J.
Acta Metall. Sin,2005,41:471-476
|
CSCD被引
1
次
|
|
|
|
|
7.
Zhao Y T.
Acta Metall. Sin,2006,42:54-58
|
CSCD被引
1
次
|
|
|
|
|
8.
Shang C J.
Acta Metall. Sin,2008,44:287-291
|
CSCD被引
2
次
|
|
|
|
|
9.
Rodrigues P C M.
Mater. Sci. Eng. A,2000,283:136-143
|
CSCD被引
54
次
|
|
|
|
|
10.
Jun H J.
Mater. Sci. Eng. A,2006,422:157-162
|
CSCD被引
50
次
|
|
|
|
|
11.
Liu D.
Acta Metall. Sin,1999,35:816-822
|
CSCD被引
1
次
|
|
|
|
|
12.
Liu D L.
Acta Metall. Sin,1999,35:923-927
|
CSCD被引
1
次
|
|
|
|
|
13.
Garlipp W.
J. Mater. Process. Technol,2001,114:71-74
|
CSCD被引
4
次
|
|
|
|
|
14.
Tsuji N.
ISIJ Int,1997,37:797-806
|
CSCD被引
5
次
|
|
|
|
|
15.
Yin S B.
J. Iron Steel Res. Int,2010,17(2):43-47
|
CSCD被引
5
次
|
|
|
|
|
了解气象卫星更多信息，请访问