阳离子光敏抗菌型水凝胶的制备及性能表征
Preparation and property characterization of cationic photoantimicrobial hydrogel
查看参考文献21篇
|
文摘
|
利用蒙脱土(MMT)分别吸附3种阳离子光敏剂(meso-四(1-甲基吡啶嗡-4-基)卟吩对甲苯磺酸盐(TMPyP)、 meso-四(N-甲基-4-吡啶)卟吩四氯化锌(Zn-TMPyP)、亚甲基蓝(MB)),然后均匀分散在聚乙烯醇-苯乙烯基吡啶盐缩合物(PVA-SbQ)的水溶液中,通过紫外光交联法制备出相应的光敏MMT/PS水凝胶。借助透射电子显微镜(TEM)对MMT和MMT/PS形貌结构进行分析,利用扫描电子显微镜(SEM)、热重分析仪(TGA)对3种光敏水凝胶的内部形貌、热学性能进行分析,研究其溶胀性能及对金黄色葡萄球菌的抗菌效果。结果表明:3种光敏MMT/PS水凝胶均具有良好的溶胀性能。抗菌结果显示,三者对金黄色葡萄球菌均具有一定的杀灭效果,其中负载Zn-TMPyP的水凝胶在光照条件下对金黄色葡萄球菌的杀菌率达到98.49%。 |
|
其他语种文摘
|
Montmorillonite(MMT)was utilized to absorb three types of cationic photosensitizers, namely,meso-tetra(4-N-methylpyridyl)porphyrine tetratosylate (TMPyP),Zn(Ⅱ)meso-tetra (N-methyl-4-pyridyl)porphine tetrachloride(Zn-TMPyP)and methylene blue(MB),the as-obtained mixtures were then evenly dispersed in aqueous polyvinyl alcohol-styrylpyridine salt condensate (PVA-SbQ)solution,corresponding photoactive MMT/PS hydrogels were prepared by the assay of UV cross-linking eventually.Transmission electron microscopy(TEM)was employed to analyse morphology of MMT and one as-prepared MMT/PS hydrogel.Scanning electron microscopy(SEM)and thermogravimetric analysis(TGA)were applied to analyse the internal morphology and thermal properties of the as-prepared hydrogels.Finally,swelling properties and antibacterial effect against staphylococcus aureus(S.aureus)were investigated.The results show that three photoactive MMT/PS hydrogels are successfully prepared with good swelling properties.The as-prepared hydrogels exhibit inactivation against S.aureus to some extent,furthermore,the hydrogel which immobilizes Zn-TMPyP reveals best inactivation efficacy,with a sterilization rate of 98.49%. |
|
来源
|
材料工程
,2019,47(2):56-61 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2017.000588
|
|
关键词
|
蒙脱土
;
水凝胶
;
光敏抗菌
;
金黄色葡萄球菌
|
|
地址
|
江南大学, 生态纺织教育部重点实验室, 江苏, 无锡, 214122
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
化学工业 |
|
基金
|
2018年江苏省研究生科研创新计划项目
;
国家自然科学基金国家杰出青年科学基金
;
中央高校基本科研业务费专项资金
|
|
文献收藏号
|
CSCD:6449866
|
参考文献 共
21
共2页
|
|
1.
郑辉东. 负载纳米银EVA复合发泡材料的制备及其抗菌性能.
材料工程,2016,44(7):107-112
|
CSCD被引
7
次
|
|
|
|
|
2.
高党鸽. 原位制备季铵盐聚合物/纳米ZnO复合抗菌剂.
材料工程,2015,43(6):38-45
|
CSCD被引
4
次
|
|
|
|
|
3.
吕生华. 氧化石墨烯/壳聚糖生物复合材料的制备及应用研究进展.
材料工程,2016,44(10):119-128
|
CSCD被引
6
次
|
|
|
|
|
4.
Wainwright M. Photodynamic antimicrobial chemotherapy(PACT).
J Antimicrob Chemother,1998,42(1):13-28
|
CSCD被引
26
次
|
|
|
|
|
5.
Spagnul C. Immobilized photosensitizers for antimicrobial applications.
J Photochem Photobiol B-Biol,2015,150:11-30
|
CSCD被引
7
次
|
|
|
|
|
6.
Schlachet I. Protoporphyrin IX-modified chitosan-g-oligo(NiPAAm)polymeric micelles:from physical stabilization to permeability characterizationin vitro.
Biomater Sci,2017,5(1):128-140
|
CSCD被引
2
次
|
|
|
|
|
7.
Alves E. Potential applications of porphyrins in photodynamic inactivation beyond the medical scope.
J Photochem Photobiol C-Photochem Rev,2015,22:34-57
|
CSCD被引
5
次
|
|
|
|
|
8.
Cavallaro A. Responsive and "smart" antibacterial surfaces:common approaches and new developments(review).
Biointerphases,2014,9(2):10-19
|
CSCD被引
2
次
|
|
|
|
|
9.
Bujdak J. Interaction of methylene blue with reduced charge montmorillonite.
J Phys Chem B,1997,101(44):9065-9068
|
CSCD被引
4
次
|
|
|
|
|
10.
Bettanin F. Aggregation of photosensitizers:the role of dispersion and solvation on dimer formation energetics.
Theoretical Chemistry Accounts,2015,134(12):11-23
|
CSCD被引
1
次
|
|
|
|
|
11.
Zhang H F. Aligned two-and three-dimensional structures by directional freezing of polymers and nanoparticles.
Nat Mater,2005,4(10):787-793
|
CSCD被引
16
次
|
|
|
|
|
12.
Wu J. Assembly of chitin nanofibers into porous biomimetic structures via freeze drying.
ACS Macro Lett,2014,3(2):185-190
|
CSCD被引
3
次
|
|
|
|
|
13.
Cui J. Synthesis and characterization of cross-linked SbQ/montmorillonite composites.
Polymer Materials Science &Engineering,2015,31(7):159-162
|
CSCD被引
1
次
|
|
|
|
|
14.
Rotomskis R. Phototransformations of sensitizers 1.significance of the nature of the sensitizer in the photobleaching process and photoproduct formation in aqueous solution.
J Photochem Photobiol B-Biol,1997,39:167-171
|
CSCD被引
3
次
|
|
|
|
|
15.
Horvath O. Photophysics and photochemistry of kinetically labile,water-soluble porphyrin complexes.
Coordination Chemistry Reviews,2006,250(13/14):1792-1803
|
CSCD被引
3
次
|
|
|
|
|
16.
许凤兰. 纳米羟基磷灰石/聚乙烯醇复合水凝胶的溶胀性.
材料工程,2005(7):15-18
|
CSCD被引
7
次
|
|
|
|
|
17.
崔晓彤. 不同接触尺度下PVA/HA复合水凝胶的滑动摩擦行为.
材料工程,2016,44(5):59-64
|
CSCD被引
2
次
|
|
|
|
|
18.
Gomez I. Thermal degradation study of PVA derivative with pendant phenylthionecarbamate groups by DSC/TGA and GC/MS.
Polym Degrad Stabil,2015,112:132-136
|
CSCD被引
2
次
|
|
|
|
|
19.
Xu J. Properties of hyaluronan/PVA-SbQ composite films processed by casting.
Polymers & Polymer Composites,2013,21(1):55-60
|
CSCD被引
3
次
|
|
|
|
|
20.
Redmond R W. A compilation of singlet oxygen yields from biologically relevant molecules.
Photochem Photobiol,1999,70(4):391-475
|
CSCD被引
16
次
|
|
|
|
|
了解气象卫星更多信息，请访问