文摘
|
对表面纳米化和未经表面纳米化处理的316L不锈钢的样品分别进行点蚀实验和应力腐蚀对比实验，在3．5％（质量分数）NaCl水溶液中分别测出它们的极化曲线。结果表明，316L不锈钢表面纳米化后抗点蚀性能下降，抗应力腐蚀性能提高。对应力腐蚀断口的SEM分析发现，316L不锈钢应力腐蚀断口有明显分区现象，断裂形式为韧性断裂，开裂通道既有穿晶型也有沿晶型。 |
|
其他语种文摘
|
Pitting corrosion and stress corrosion tests have been carried out to the specimens of 316L stainless steel with nanocrystalline surface and non-nanocrystalline surface. Their polarization curves also have been measured in a 3.5 % （mass fraction） NaCl solution. The results show that pitting resistance of 316L stainless steel with nanocrystalline surface is reduced but the stress corrosion resistance is improved. The stress corrosion cracked surfaces of the specimens have been observed with SEM. It is found that the cracked surface of the 316L stainless steels has obviously zoned. The cracking shows a ductile fracture. The cracking path is both of intragranular and intergranular characteristic. |
|
来源
|
材料工程
,2005,0(10):42-46 【核心库】
|
|
关键词
|
316L不锈钢
;
表面纳米化
;
点蚀
;
应力腐蚀
;
断口
|
|
地址
|
1.
沈阳航空工业学院, 辽宁, 沈阳, 110034
2.
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
辽宁省自然科学基金
;
国家自然科学基金项目
|
|
文献收藏号
|
CSCD:2198588
|
|
|
1.
王振波. 低碳钢表面纳米化处理及结构特征[J].
金属学报,2002,38(2):157-160
|
CSCD被引
1
次
|
|
|
|
|
2.
LIU G. Low carbon steel with nanastructured surface layer induced by high-energy shot peening [J].
Scr Mater,2001,44:1791-1795
|
CSCD被引
124
次
|
|
|
|
|
3.
张洪旺. 表面机械研磨诱导AISI 304不锈钢表层纳米化Ⅰ.组织与性能.
金属学报,2003,39(4):342-346
|
CSCD被引
51
次
|
|
|
|
|
4.
李东. SS400钢对接接头表面纳米化及其对疲劳强度的影响.
焊接学报,2002,23(2):18-23
|
CSCD被引
22
次
|
|
|
|
|
5.
张德康. 不锈钢局部腐蚀[M].
不锈钢局部腐蚀,1982:285
|
CSCD被引
2
次
|
|
|
|
|
6.
JOHN. Corrosion of stainless steel[M].
Corrosion of stainless steel,1979:293-336
|
CSCD被引
1
次
|
|
|
|
|
7.
吕爱强. 机械研磨诱导316L不锈钢表层组织的演变.
金属学报,2004,40(9):943-949
|
CSCD被引
18
次
|
|
|
|
|
8.
HOWARD. Metals handbook 8th edition vol 10 failture analysis and prevention[M].
Metals handbook 8th edition vol 10 failture analysis and prevention,1975:986
|
CSCD被引
1
次
|
|
|
了解气象卫星更多信息，请访问