激光-等离子束复合制备热障涂层高温性能试验研究
A Study on Elevate Temperature Characteristics of Laser-plasma Prepared Thermal Barrier Coatings
查看参考文献12篇
|
文摘
|
在GH536高温合金基材上，采用矩形积分透镜，激光重熔等离子喷涂NiCrAlY/8YSZ热障涂层。1050℃的静态氧化试验和热震试验的结果表明：激光重熔可以改善热障涂层的抗氧化性能，能量密度33J·mm~-2的激光重熔试样具有高于等离子喷涂试样的热震寿命，氧化阻力的改善与重熔层致密组织有关。微细网状裂纹释放热震应力的作用具热震寿命提高的主要原因。 |
|
其他语种文摘
|
A CO-2 continuous wave laser with BIZ transmissive beam integrators was used for laser remelting (LR) the surface of plasma sprayed (PS) ZrO-2-8(mass fraction/%) Y-2O-3(8YSZ)/ Ni22Cr10A1Y thermal barrier coatings (TBCs)on GH536 superalloy substrate. The uniform energy distribution of beam with rectangular profiles of 9mm×3mm was obtained. The thermal shock test and static oxidation test were conducted to both PS samples and LR samples at 1050℃.With the different failure criteria,the mechanism of failure was discussed.The results show that oxidation resistance and thermal shock resistance are improved with laser specific energy density input of 33 J·mm~-2 |
|
来源
|
材料工程
,2003,0(2):19-22,26 【核心库】
|
|
关键词
|
热障涂层
;
激光重熔
;
等离子喷涂
;
热震试验
;
静态氧化试验
;
矩形积分透镜
;
陶瓷层
;
金属
|
|
地址
|
1.
中国科学院金属研究所, 沈阳, 110016
2.
高能束流加工技术重点实验室, 高能束流加工技术重点实验室, 北京, 100024
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家科技重点实验室基金
|
|
文献收藏号
|
CSCD:1353952
|
参考文献 共
12
共1页
|
|
1.
H L Tsai.
Mater Sci Eng A,1994,177:227-232
|
CSCD被引
4
次
|
|
|
|
|
2.
H L Tsai.
Surf Coat Techol,1995,71:53-59
|
CSCD被引
3
次
|
|
|
|
|
3.
H L Tsai.
J Mater Eng Perform,1995,4:689-696
|
CSCD被引
5
次
|
|
|
|
|
4.
R Sivacumar.
Surface Engineering,1988,4(2):127-140
|
CSCD被引
1
次
|
|
|
|
|
5.
I Zaplatyunsy.
Thin Sold Films,1982,95:273-284
|
CSCD被引
1
次
|
|
|
|
|
6.
Chang K C.
Surf Coat Technol,1998,102:197-204
|
CSCD被引
7
次
|
|
|
|
|
7.
L Lelait.
J Mater Sci,1992,27:5-12
|
CSCD被引
8
次
|
|
|
|
|
8.
K M Jasim.
Mater Sci Technol,1992,8:83-91
|
CSCD被引
4
次
|
|
|
|
|
9.
M Leoni.
Surf Coat Technol,1998,108/109:107-113
|
CSCD被引
24
次
|
|
|
|
|
10.
S V Joshi.
Surface Engineering,1995,11(3):233-239
|
CSCD被引
3
次
|
|
|
|
|
11.
Wu B C.
J Am Ceram Soc,1989,72(2):212-218
|
CSCD被引
18
次
|
|
|
|
|
12.
R A Miller.
J Am Ceram Soc,1984,67(8):517-521
|
CSCD被引
19
次
|
|
|
|
|
了解气象卫星更多信息，请访问