淬火温度对Ti-4A1-4.5Mo合金马氏体类型的影响
INFLUENCE OF QUENCHING TEMPERATURE ON MARTENSITE TYPE IN Ti-4A1-4.5Mo ALLOY
查看参考文献15篇
|
文摘
|
对Ti-4A1-4.5Mo合金经不同固溶温度淬火处理后的相组成进行了分析,结果表明,当合金在相变点以上温度淬火后,可以获得hcp结构a~1马氏体; 随固溶温度降低,淬火后斜方a''马氏体出现,并在一定的温度范围内与a~1马氏体共存; 在 800℃淬火,a''马氏体消失,合金由a和β相构成; a''马氏体显著降低β转变组织的硬度.EDS分析表明, Mo含量并不是决定马氏体类型的唯一因素 |
|
其他语种文摘
|
There are many discrepancies in the literatures concerning the martensite constitution in theα+β double phase titanium alloys after quenching,so the Ti-4Al-4.5Mo alloy was selected to analysis further the martensite phase transformation in the alloy. The results show that when the quenching temperature is above the(α+β)/βtransformation temperature (925 0C), the hexagonal martensite(α~1)formed. With the decrease of quenching temperature, another kind of martensite with orthorhombic structure (a") appeared which can coexist with α~1 in a certain temperature range. In the sample quenched at 800℃, the a" disappeared, and the alloy only contains α and β phases. The a'' martensite reduced the hardness of martensite transformed structure remarkably. EDS analysis indicated that the content of βstabilized element (Mo) is not the only factor determining the martensitic type |
|
来源
|
金属学报
,2010,46(9):1061-1065 【核心库】
|
|
DOI
|
10.3724/sp.j.1037.2010.00157
|
|
关键词
|
钛合金
;
淬火
;
马氏体
;
显微硬度
|
|
地址
|
1.
中国科学院金属研究所, 沈阳, 110016
2.
西北有色金属研究院, 西安, 710000
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:4033864
|
参考文献 共
15
共1页
|
|
1.
Davis R.
J Mater Sci,1979,14:712
|
CSCD被引
18
次
|
|
|
|
|
2.
Kharia K K.
Metall Mater Trans.A,2001,32:671
|
CSCD被引
4
次
|
|
|
|
|
3.
Wang Y H.
Mater Sci Eng.A,2009,508:76
|
CSCD被引
20
次
|
|
|
|
|
4.
张岷. Ti-4．4A1—3．8Mo合金的亚稳相变及其对硬度的影响.
材料研究学报,2008,22:68
|
CSCD被引
5
次
|
|
|
|
|
5.
Peng W H.
J Alloys Compd,2010,490:661
|
CSCD被引
1
次
|
|
|
|
|
6.
Leyens C.
Titatniutm and Titatniutm Alloys, Futn, datmentals and Applications,2003:22
|
CSCD被引
1
次
|
|
|
|
|
7.
Lutjering G.
Titanium, Engmeering Materials and Processes,2003:32
|
CSCD被引
1
次
|
|
|
|
|
8.
Yang R.
Acta Metall Mater,1992,40:1553
|
CSCD被引
3
次
|
|
|
|
|
9.
Grujicic M.
Mater Sci Eng.A,1992,151:217
|
CSCD被引
3
次
|
|
|
|
|
10.
Ahmed T.
J Mater Sci,1996,31:4267
|
CSCD被引
8
次
|
|
|
|
|
11.
Kolachev A B.
Titanium, Science and Technology,1973:1569
|
CSCD被引
1
次
|
|
|
|
|
12.
Bagiriatskii I A.
Sov Phys Dokl,1958,3:1014
|
CSCD被引
1
次
|
|
|
|
|
13.
张喜燕.
钛合金及应用,2005:92
|
CSCD被引
1
次
|
|
|
|
|
14.
Moffat D L.
Metall Mater Trans.A,1988,19:1677
|
CSCD被引
12
次
|
|
|
|
|
15.
Inamura T.
Philos Mag,2007,87:3325
|
CSCD被引
9
次
|
|
|
|
|
了解气象卫星更多信息，请访问