La_(0.6)Nd_(0.4)Ni_(4.8)Mn_(0.2)M_(0.1)（M=Cu，Zr）合金的贮氢性能研究
Study on Hydrogen Storage Properties of La_(0.6)Nd_(0.4)Ni_(4.8)Mn_(0.2)M_(0.1)（M=Cu,Zr） Alloys
查看参考文献21篇
|
文摘
|
系统研究了非化学计量比合金La_(0.6)Nd_(0．4)Ni_(4．8)Mn_(0．2)M_(0．1)（M=Cu，Zr）的贮氢性能。结果表明，添加Cu能提高合金的平台压力，减轻滞后效应；而添加Zr能够有效提高合金的动力学性能和抗粉化性能，降低平台压力。但Cu和Zr的添加使贮氢容量有所降低。研究表明，XRD（111）主峰半高宽FWHM值及晶格常数a／c值与合金的滞后因子有相同的变化趋势，平台压力、吸氢焓变与晶胞参数α有很好的线性关系。 |
|
其他语种文摘
|
Hydrogen storage properties of the nonstoichiometric alloys of La_(0.6)Nd_(0.4)Ni_(4.8)Mn_(0.2)M_(0.1)（M=Cu,Zr） have been systematically investigated. Experimental results showed that Cu addition increased the plateau pressure and alleviated the hysteresis while Zr addition effectively improved the absorption kinetics, enhanced the pulverization resistant capability and lowered the plateau pressure. However, additions of Cu and Zr addition impaired the hydrogen storage capacity of the alloys. It was found that the hysteresis factors was correlated with FWHM of （111） peak and α/c value of the alloys, and both the plateau pressure and enthalpy had good linear relations With the lattice parameter α. |
|
来源
|
稀有金属材料与工程
,2008,37(4):599-603 【核心库】
|
|
关键词
|
贮氢合金
;
非化学计量比
;
压力
;
成分等温线
;
动力学
;
抗粉化性能
|
|
地址
|
中国科学院金属研究所, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家863计划
|
|
文献收藏号
|
CSCD:3273272
|
参考文献 共
21
共2页
|
|
1.
Ron M.
Journal of the Less-Common Metals,1991,172/174:1138
|
CSCD被引
2
次
|
|
|
|
|
2.
胡子龙.
贮氢合金,2002:91
|
CSCD被引
2
次
|
|
|
|
|
3.
Kohno T.
Journal of Alloys and Compounds,2004,363:249
|
CSCD被引
16
次
|
|
|
|
|
4.
Wang Xinhua.
Trans Nonferrous Met Soc China,1998,8(1):56
|
CSCD被引
2
次
|
|
|
|
|
5.
新华.
稀有金属材料与工程,2001,30(5):353
|
CSCD被引
1
次
|
|
|
|
|
6.
Suzuki Y.
Journal of Alloys and Compounds,2002,488:330-332
|
CSCD被引
1
次
|
|
|
|
|
7.
大角泰章.
金属氢化物的性质与应用,1991
|
CSCD被引
5
次
|
|
|
|
|
8.
Hahne E.
International Journal of Hydrogen Energy,1998,23:107
|
CSCD被引
8
次
|
|
|
|
|
9.
Wang J Kim.
International Journal of Hydrogen Energy,2001,26:609
|
CSCD被引
1
次
|
|
|
|
|
10.
廖彬. 镀覆处理对LaNiAl合金贮氢性能影响.
功能材料,2001,32(2):167
|
CSCD被引
3
次
|
|
|
|
|
11.
Kim K J.
International Journal of Refrigeration,1997,20:339
|
CSCD被引
1
次
|
|
|
|
|
12.
程宏辉. 新型贮氢材料性能测试装置及其应用.
稀有金属材料与工程,2007,36(1):78
|
CSCD被引
2
次
|
|
|
|
|
13.
Yu X B.
International Journal of Hydrogen Energy,2004,29:1377
|
CSCD被引
12
次
|
|
|
|
|
14.
Lundin C E.
Journal of the Less Common Metals,1977,56:19
|
CSCD被引
37
次
|
|
|
|
|
15.
Valoen L O.
Journal of Alloys and Compounds,2000,306:235
|
CSCD被引
13
次
|
|
|
|
|
16.
Sandrock G.
Proc of the 12th International Energy Conversion Engineering Conference(IECEC),1977:951
|
CSCD被引
1
次
|
|
|
|
|
17.
Krishna Kumar M.
International Journal of Hydrogen Energy,2007,32(12):1890
|
CSCD被引
4
次
|
|
|
|
|
18.
赵爽. LaNi_（5-x）-M_x合金氢化物贮氢性能的计算与预报.
金属学报,1999,35:65
|
CSCD被引
11
次
|
|
|
|
|
19.
Lin Qin.
Journal of Alloys and Compounds,2003,351:91
|
CSCD被引
5
次
|
|
|
|
|
20.
余学斌. Cr含量对TiMn_(1.2-x)CrxV_(0.25)Fe_(0.05)合金吸/放氢性能的影响.
金属学报,2004,40:527
|
CSCD被引
6
次
|
|
|
|
|
了解气象卫星更多信息，请访问