喷射态7075合金回归再时效中预时效的研究
PRE-AGING OF RETROGRESSION AND RE-AGING OF SPRAY FORMED 7075 ALLOY
查看参考文献25篇
|
文摘
|
采用拉伸测试、TEM和电导率测试等方法, 研究回归再时效(RRA)处理中预时效处理对喷射成形7075合金组织及性能的影响. 结果表明, 采用120 ℃, 16 h 的欠时效预处理比120 ℃, 24 h 峰值时效预处理和120 ℃, 32 h 过时效预处理更有利于在回归处理过程中合金晶内析出相的回溶, 比120 ℃, 8 h 的早期预时效处理更有助于晶界相在再时效处理后断续分布. 120 ℃, 16 h 预时效处理的合金经RRA处理后, 其抗拉强度和屈服强度分别为782和726 MPa, 均高于T6峰值时效和常规回归再时效水平; 电导率为22.7 MS/m, 晶界析出相断续分布, 合金抗腐蚀性能优良. |
|
其他语种文摘
|
Retrogression and re-aging (RRA) treatments are divided into pre-aging, retrogression and re-aging. Although peak aging was used as the pre-aging of RRA treatment in the past, some different opinions were reported in recent years. The effects of pre-aging of RRA treatment on microstructure, mechanical properties and conductivity of spray formed 7075 aluminum alloy were investigated by TEM, tensile and conductivity test. The results show that the mechanical properties and conductivity of spray formed 7075 alloy could be improved by the under aging at 120 ℃ for 16 h as the pre-aging of RRA treatment. The properties of the 7xxx series aluminum alloys depend on matrix precipitates (MPt), grain boundary precipitates (GBPs) and precipitate free zones (PFZs). The tiny MPt can increase the tensile strength. The connected GBPs and narrow PFZs will lower the conductivity and the elongation of the alloy. The under aging is more beneficial for the re-dissolution of the MPts at retrogression treatment at 200 ℃ for 10 min, and is more conducive to interrupt distributions of the GBPs than the early aging after RRA treatment. With the under aging as the pre-aging treatment, the growth of the MPts was actively suppressed and the GBPs at grain boundaries are continuous. During retrogression treatment, the MPts were re- dissolved absolutely and the GBPs were transformed from a chain to dissociation. After re-aging treatment, lots of tiny dispersive MPts precipitated out again in matrix, the GBPs were totally separated and the PFZ were widened. After pre-aging at 120 ℃ for 16 h and RRA treatment, the tensile strength and yield strength of the alloy are 782 and 726 MPa, respectively, which are higher than that after peak aging treatment or conventional RRA treatment, the conductivity of the 7075 alloy is excellent with 22.7 MS/m. |
|
来源
|
金属学报
,2014,50(7):863-870 【核心库】
|
|
DOI
|
10.3724/sp.j.1037.2013.00756
|
|
关键词
|
7075铝合金
;
喷射成形,回归再时效
;
预时效
;
析出相
|
|
地址
|
沈阳工业大学材料科学与工程学院, 沈阳, 110870
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家教育部霍英东教育基金
;
辽宁省创新团队项目
|
|
文献收藏号
|
CSCD:5188510
|
参考文献 共
25
共2页
|
|
1.
王艳秋. 7075铝合金微弧氧化涂层的组织结构与耐蚀耐磨性能.
金属学报,2011,47:455
|
CSCD被引
31
次
|
|
|
|
|
2.
Marlaud T.
Acta Mater,2010,58:248
|
CSCD被引
75
次
|
|
|
|
|
3.
Marlaud T.
Acta Mater,2010,58:4814
|
CSCD被引
74
次
|
|
|
|
|
4.
George S L.
J Mater Sci,2012,47:4716
|
CSCD被引
7
次
|
|
|
|
|
5.
Su R M.
Appl Mech Mater,2012,217:1835
|
CSCD被引
3
次
|
|
|
|
|
6.
Jeyakumar M.
Mater Manuf Proc,2010,25:777
|
CSCD被引
6
次
|
|
|
|
|
7.
Silva G.
J Mater Eng Perform,2013,22:210
|
CSCD被引
9
次
|
|
|
|
|
8.
Ricker R E.
Metall Mater Trans. A,2013,44:1353
|
CSCD被引
8
次
|
|
|
|
|
9.
宁爱林. 铝合金回归再时效状态的超峰时效强度行为分析.
金属学报,2006,42:1253
|
CSCD被引
9
次
|
|
|
|
|
10.
Fooladfar H.
J Mater Eng Perform,2010,19:852
|
CSCD被引
5
次
|
|
|
|
|
11.
Arnold E M.
J Mater Eng Perform,2012,21:2480
|
CSCD被引
3
次
|
|
|
|
|
12.
Cina B M.
US Pat, 3856584,1974
|
CSCD被引
1
次
|
|
|
|
|
13.
李荣德. 喷射成形7075合金回归再时效处理的组织和抗应力腐蚀性能.
机械工程学报,2013,49(20):22
|
CSCD被引
4
次
|
|
|
|
|
14.
Su R M.
Adv Mater Res,2013,774:872
|
CSCD被引
2
次
|
|
|
|
|
15.
Peng G.
Mater Sci Eng. A,2011,528:4014
|
CSCD被引
36
次
|
|
|
|
|
16.
Reda Y.
Mater Sci Eng. A,2008,485:468
|
CSCD被引
38
次
|
|
|
|
|
17.
Ohnishi T.
Mater Trans JIM,1989,30:601
|
CSCD被引
21
次
|
|
|
|
|
18.
Higashi K.
US Pat, 4713216,1987
|
CSCD被引
1
次
|
|
|
|
|
19.
Lin J.
US Pat, 5108520,1992
|
CSCD被引
1
次
|
|
|
|
|
20.
韩小磊. 7150铝合金三级过时效热处理制度.
中国有色金属学报,2012,22:3006
|
CSCD被引
7
次
|
|
|
|
|
了解气象卫星更多信息，请访问