利用固相反应法在硅片上制备硅酸锌发光薄膜及表征
Photoluminescent Zinc Silicate Films Prepared on Silicon Wafer by Solid-Phase Reaction
查看参考文献17篇
|
文摘
|
采用与硅集成工艺相兼容的固相反应方法在硅衬底上制备了未经掺杂及掺锰的硅酸锌薄膜.XRD测试和UV-Vis吸收谱测试证明在高于880℃的温度下热处理,可以获得结晶状态很好的硅酸锌薄膜.光致发光光谱分析表明,未掺杂的薄膜在紫外波段有较弱的发射,而掺锰的硅酸锌薄膜在可见光波段有很强的光致发射.由于硅酸锌薄膜在高温下非常稳定,可以与硅集成电路工艺兼容,而且发光强度高,因此在制作硅基光电集成器件方面有非常大的应用前景. |
|
其他语种文摘
|
Undoped and Mn-doped zinc silicate (Zn2Si04) thin films on silicon substrate are prepared by solid-phase reaction method. The results of the samples are characterized by XRD and UV-Vis absorption,which show that willemite Zn_2SiO_4 thin films are formed after the annealing above 880 ℃. Undoped zinc silicate film shows a weak UV emission while Mn-doped willemite shows intense photoluminescence in visible region. It is suggested that zinc silicate films are used in silicon based optoelectronic devices due to their stability and high efficiency. |
|
来源
|
半导体学报
,2004,25(7):794-797 【核心库】
|
|
关键词
|
硅酸锌
;
硅基光电
;
光致发光谱
;
固相反应
|
|
地址
|
浙江大学, 硅材料国家重点实验室, 杭州, 310027
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0253-4177 |
|
学科
|
物理学 |
|
基金
|
国家973计划
;
国家自然科学基金
|
|
文献收藏号
|
CSCD:1
|
参考文献 共
17
共1页
|
|
1.
Du Chunxia. Electrolu-minescence studies of Er and SiO co-doped Si layers prepared by molecular beam epitaxy.
Opt Mater,2000,14:259
|
CSCD被引
1
次
|
|
|
|
|
2.
Gaburro Z. Electroluminescence in MOS structures with Si/SiO2 nanometric multilayers.
Solid State Commun,2000,114:33
|
CSCD被引
4
次
|
|
|
|
|
3.
Svrcek V. Photoluminescence properties of sol-gel derived SiO2 layers doped with porous silicon.
Mater Sci Eng C,2002,19:233
|
CSCD被引
1
次
|
|
|
|
|
4.
王蓟. 硅基发光材料研究进展.
微纳电子技术,2002,8:18
|
CSCD被引
1
次
|
|
|
|
|
5.
徐飞. （Si,Er）双注入热氧化SiO_2/Si薄膜的表面结构及1.54μm光发射.
半导体学报,2001,22(10):1258
|
CSCD被引
1
次
|
|
|
|
|
6.
Zhang Q Y. Influence of annealing atmosphere and temperature on photoluminescence of Tb3+ or Eu3+ activated zinc silicate thin film phosphors via sol-gel method.
Chem Phys Lett,2002,351:163
|
CSCD被引
10
次
|
|
|
|
|
7.
Zhang H X. Luminescence of Eu3+ and Tb3+ doped Zn2SiO4 nanometer powder phosphors.
Mater Chem Phys,2001,68:31
|
CSCD被引
10
次
|
|
|
|
|
8.
Ahmadi T S. Mn) in aqueous medium.
Mater Res Bull,2000,35:1869
|
CSCD被引
3
次
|
|
|
|
|
9.
尤洪鹏. Zn_2SiO_4∶Mn的VUV和UV光谱特性.
发光学报,2000,21(4):349
|
CSCD被引
3
次
|
|
|
|
|
10.
Zhang H X. Zn2SiO4 films on SiO2/Si.
Thin Solid Films,2000,370:50
|
CSCD被引
8
次
|
|
|
|
|
11.
Kang Y C. Mn phosphor particles prepared by spray pyrolysis using a filter expansion aerosol generator.
Mater Res Bull,2000,35:1143
|
CSCD被引
8
次
|
|
|
|
|
12.
Sohn K S. Mn phosphors.
Mater Lett,1999,41:303
|
CSCD被引
2
次
|
|
|
|
|
13.
Krug V A. Excitonic Mechanism of Energy Transfer in Zinc Orthosilicate.
Chinese Journal of Luminescence,1990,11(4):264
|
CSCD被引
1
次
|
|
|
|
|
14.
Van der Kolk E. Optimised co-activated willemite phosphors for application in plasma display panels.
J Lumin,2000,87/89:1246
|
CSCD被引
3
次
|
|
|
|
|
15.
谢平波. Zn↓2SiO↓4:Mn纳米微晶薄膜的溶胶-凝胶法制备及其光致发光性质研究.
中国科学技术大学学报,1997,27(4):389
|
CSCD被引
5
次
|
|
|
|
|
16.
张迈生. Sol-Gel法和微波法合成亚纳米级Zn_2SiO_4:Mn~（2＋）高效绿色荧光体.
无机材料学报,1999,14(3):479
|
CSCD被引
7
次
|
|
|
|
|
17.
Taghavinia N. emergence of yellow luminescence.
J Cryst Growth,2002,237/239:869
|
CSCD被引
2
次
|
|
|
|
|
了解气象卫星更多信息，请访问