Distinct dendritic α phase emerging on the surface of primary α phase in a compressed near-α titanium alloy

查看参考文献32篇

Liu Z 1,2   Zhao Z B 1 *   Liu J R 1 *   Wang Q J 1   Yang R 1,2  
文摘 The characteristic of the surface morphology of primary α phase was studied in a deformed near-a titanium alloy. Dendritic α phase emerged on the surfaces of primary α phase when the alloy was air-cooled in α+β phase field after deformation. The dendritic a grain has the same orientation with its original primary α grain. The formation of the dendritic α phase could be explained by interface instability in epitaxial growth process of the primary α phase. The dislocations induced by deformation could facilitate the formation of dendritic α phase leading to the dendritic α phase and more obvious with the increase of strain. The growth of dendritic α phase was finally limited by the nucleation of second α phase with cooling.
来源 Journal of Materials Science & Technology ,2018,34(4):666-669 【核心库】
DOI 10.1016/j.jmst.2017.10.011
关键词 Epitaxial growth ; Dendritic α phase ; Microstructure ; Interface instability ; Hot deformation
地址

1. Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016  

2. School of Materials Science and Engineering, University of Science and Technology of China, Hefei, 230000

语种 英文
文献类型 研究性论文
ISSN 1005-0302
学科 金属学与金属工艺
文献收藏号 CSCD:6219165

参考文献 共 32 共2页

1.  Gao X. Acta Mater,2017,122:298-309 CSCD被引 24 次    
2.  Zhao Z B. Acta Mater,2017,126:372-382 CSCD被引 32 次    
3.  Banerjee D. Acta Mater,2013,61:844-879 CSCD被引 319 次    
4.  Lutjering G. Titanium,2007 CSCD被引 56 次    
5.  Semiatin S L. Metall. Mater. Trans. A,2007,38:910-921 CSCD被引 13 次    
6.  Zherebtsov S. Acta Mater,2011,59:4138-4150 CSCD被引 65 次    
7.  Dong H. Sci. Technol,2015,31:962-968 CSCD被引 1 次    
8.  Wang G Q. Effect of Base Material on Microstructure and Texture Evolution of a Ti–6Al–4V Electron-Beam Welded Joint. Acta Metall. Sin. (Engl. Lett.),2017,30:499-504 CSCD被引 6 次    
9.  Yang M. Quantitative Phase Field Simulation of α Particle Dissolution in Ti-6A1-4V Alloys Below β Transus Temperature. Acta Metall. Sin. (Engl. Lett.),2017,30:745-752 CSCD被引 3 次    
10.  Froes F. Titanium: Physical Metallurgy, Processing, and Applications,2015 CSCD被引 1 次    
11.  Semiatin S L. Metall. Mater. Trans. A,2003,34:2377-2386 CSCD被引 36 次    
12.  Zhao Z B. J. Alloys Compd,2017,712:179-184 CSCD被引 11 次    
13.  Sun Z. Mater. Charact,2016,118:167-174 CSCD被引 2 次    
14.  Sun Z. J. Alloys Compd,2016,689:693-701 CSCD被引 2 次    
15.  Lonardelli I. Acta Mater,2007,55:5718-5727 CSCD被引 20 次    
16.  Obasi G C. Acta Mater,2012,60:1048-1058 CSCD被引 21 次    
17.  Obasi G C. Acta Mater,2012,60:7169-7182 CSCD被引 5 次    
18.  Appolaire B. Acta Mater,2005,53:3001-3011 CSCD被引 24 次    
19.  Sun Z. Acta Mater,2013,61:2057-2064 CSCD被引 9 次    
20.  Kirkaldy J S. Scr. Metall,1980,14:739-744 CSCD被引 1 次    
引证文献 5 篇

1 刘巧沐 β 锻造Ti17钛合金的组织和织构及其对室温拉伸性能的影响 材料热处理学报,2018,39(5):60-65
CSCD被引 1 次

2 刘征 电子束快速成形制备TC4合金的组织和拉伸性能分析 金属学报,2019,55(6):692-700
CSCD被引 4 次

显示所有5篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号