CU-10Ni-5Al三元合金在700℃～800℃,1×105 Pa氧气中的氧化
Oxidation of a Ternary Cu-10Ni-5Al Alloy in 1 × 105 Pa Pure O2 at 700℃～800℃
查看参考文献10篇
|
文摘
|
研究了三元Cu-10Ni-5Al合金在700℃～800℃纯氧气中的氧化行为.合金在2种温度下的氧化行为较为类似,经过初始阶段的快速氧化反应之后,在锈层底部开始形成连续完整的保护性A12O3薄层,防止了铝的内氧化和其它组元的进一步氧化,因此合金的腐蚀速率与初始阶段相比极大地降低了.与相应的Cu-5Al二元合金相比,10at%Ni的存在使得活泼组元Al由内氧化向外氧化转变更为困难. |
|
其他语种文摘
|
The oxidation of Cu-10Ni-5Al has been studied at 70O'C~8OO-C in pure O2. The oxidation behavior of the alloy at both temperatures is similar. After an initial stage of fast reaction, this alloy is able to develop a continuous layer of alumina at the base of the scale, which prevents preceding with oxidation of aluminum and other components, thus the oxidation rate was greatly reduced as compared with the initial oxidation stage. The presence of 10 at% Ni makes the transition of aluminum from internal to external oxidation more difficult in contrast with the corresponding Cu-5A1 binary alloy. |
|
来源
|
稀有金属材料与工程
,2004,33(10):1104-1107 【核心库】
|
|
关键词
|
Cu-10Ni-5Al
;
高温氧化
;
镍效应
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-185X |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:1689473
|
参考文献 共
10
共1页
|
|
1.
Croll J F.
Oxid Met,1969,1:55
|
CSCD被引
4
次
|
|
|
|
|
2.
潘学民. 液态CuAlNi合金的微观不均匀性.
稀有金属材料与工程,2003,32:494
|
CSCD被引
3
次
|
|
|
|
|
3.
Hausgrud R.
Oxid Met,1998,50:189
|
CSCD被引
3
次
|
|
|
|
|
4.
Dennison J P.
JInst Metals,1952,81:229
|
CSCD被引
1
次
|
|
|
|
|
5.
Pettit F S.
Trans Met Soc AIME,1967,239:1296
|
CSCD被引
2
次
|
|
|
|
|
6.
Hindam H M.
J Electrochem Soc,1980,127:1622
|
CSCD被引
5
次
|
|
|
|
|
7.
Pastorek R L.
Trans Met Soc AIME,1969,245:1711
|
CSCD被引
1
次
|
|
|
|
|
8.
Rhines F N.
Trans Met Soc AIME,1938,128:185
|
CSCD被引
1
次
|
|
|
|
|
9.
Gesmundo F.
Oxid Met,2003,60:347
|
CSCD被引
3
次
|
|
|
|
|
10.
Kirkaldy J.
Diffusion in the Condensed State,1987:27
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问