退火工艺对钨丝／错基非晶合金复合材料动态力学性能及断裂模式的影响
Influence of annealing on dynamic mechanical characteristics and fracture modes of W fiber/Zr - based amorphous matrix composites

查看参考文献4篇

孙明 1   王鲁 1   程焕武 1   姚佳浩 1   王富耻 1   李树硅 1   张海峰 2   王宏民 2  
文摘 研究了体积含量为60％的钨丝／锆基复合材料在经过退火处理后，材料的应力-应变响应和动态断裂特征以及断口形貌。利用Hopkingson压杆冲击加载装置和扫描电镜（SEM）以及X射线衍射仪（XRD），对Φ5mm*5mm的圆柱形试样进行了相关研究。研究表明，钨丝体积含量为60％的钨丝／锆基复合材料在经过退火处理后，非晶基体出现了明显的晶化现象；材料在退火后动态压缩强度比退火前有明显降低；退火后非晶基体断口形貌由退火前的完全的脉络花样转变为河流花样和脉络花样混合模式；经过动态冲击后，钨丝的断裂模式在退火前后变化大.
其他语种文摘 After the W fiber/Zr - based amorphous matrix composites whose W fiber volumetric fraction is 60% are an-nealed, the influence of annealing on the stress - strain response, dynamic fracture characteristic and fractographic pattern are examined. The samples are 5mm in diameter with a length to diameter ratio of 1. They are tested by using Hopkinson pressure bar,Scanning Electron Microscopy(SEM) and XRD. The experiment shows that, after being annealed, the amorphous matrix is crystallized and the compressive strength of the material decreases obviously. The fracture mode of W fiber does not change after annealing.
来源 兵器材料科学与工程 ,2004,27(3):4-8 【核心库】
关键词 W丝/Zr基非晶合金复合材料 ; 动态性能 ; 退火 ; 动态断裂
地址

1. 北京理工大学材料科学与工程学院, 北京, 100081  

2. 中国科学院金属研究所, 辽宁, 沈阳, 110015

语种 中文
文献类型 研究性论文
ISSN 1004-244X
学科 一般工业技术
文献收藏号 CSCD:1593420

参考文献 共 4 共1页

1.  Conner R D. Acta Mater,1998,46(17):6089-6102 CSCD被引 81 次    
2.  Johnson W L. Mater Sci Forum,1996,225-227:35-49 CSCD被引 33 次    
3.  Dandliker R B. J Mater Res,1998,13(10):2896-2901 CSCD被引 44 次    
4.  边赞. Zr_(52.5)Cu_(17.9)Ni_(14.6)Al_(10)Ti_5块体非晶退火后的力学性能. 金属学报,2000(7):693-696 CSCD被引 4 次    
引证文献 1 篇

1 张晓立 钨丝增强块体非晶复合材料的研究进展 稀有金属材料与工程,2008,37(8):1323-1328
CSCD被引 2 次

显示所有1篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号