文摘	以Cu(NO_3)_2 ·3H_2O和Ce(NO_3)_3 ·6H_2O为改性剂,采用溶胶-凝胶法制备Cu-Ce/TiO_2。探讨Cu-Ce负载量、 Cu与Ce摩尔比和煅烧温度对Cu-Ce/TiO_2性能的影响。利用SEM,LPSA,BET和UV-Vis测试Cu-Ce/TiO_2的表面形貌、粒度分布、孔结构和光学性能。结果表明:Cu-Ce负载量3%、Cu与Ce摩尔比1∶1、煅烧温度500℃时,制备的Cu-Ce/TiO_2具有良好的光催化性能与湿性能。Cu-Ce/TiO_2呈近似球体,具有较好的均匀化和分散性,其粒径分布为1202.98~5364.48nm,其中d_(50)为2437.57nm。Cu-Ce/TiO_2具有狭小瓶颈的“墨水瓶”型孔结构,其比表面积为105.55m~2/g,孔体积为0.1200~0.1246mL/g,平均孔直径为3.44~4.02nm。Cu-Ce掺杂促使Cu-Ce/TiO_2内部形成新的能级,提高捕获e-和h+的能力,增强光子的利用效率,促使吸收边带发生红移。
其他语种文摘	Cu(NO_3)_2·3H_2O and Ce(NO_3)_3·6H_2O were used as modifier to make Cu-Ce/TiO_2by solgel method.The influences of Cu-Ce loading capacity,Cu and Ce molar ratio,sintering temperature on Cu-Ce/TiO_2performance were explored.Then,surface morphology,particle size distribution, pore structure and optical property of Cu-Ce/TiO_2 were characterized by SEM,LPSA,BET and UVVis, respectively.The results show that:prepared Cu-Ce/TiO_2shows good photocatalytic-moisture performance when Cu-Ce loading capacity is 3%,Cu and Ce molar ratio is 1∶1and sintering temperature is at 500℃.Cu-Ce/TiO_2presents approximate sphere,with better uniformity and dispersibility and the particle size distribution is 1202.98-5364.48nm,with d_(50)2437.57nm.Cu-Ce/TiO_2has pore structure,approximate to an “ink bottle”with a narrow bottleneck,with the specific surface area 105.55m~2/g,hole size 0.1200-0.1246mL/g,and average pore diameter 3.44-4.02nm.Cu-Ce doping promotes to form a new energy level inside Cu-Ce/fiO_2so as to improve the ability to capture e-and h+,enhance the efficiency of photon utilization,and promote red shift of absorption sideband.
来源	材料工程 ,2018,46(1):114-118 【核心库】
DOI	10.11868/j.issn.1001-4381.2016.001100
关键词	Cu-Ce掺杂 ; 光-湿性能 ; TiO_2 ; 湿性能 ; 光催化性能
地址	安徽工业大学建筑工程学院, 安徽, 马鞍山, 243032
语种	中文
文献类型	研究性论文
ISSN	1001-4381
学科	环境污染及其防治
基金	国家自然科学基金青年基金资助项目 ; 高等学校优秀青年人才基金项目
文献收藏号	CSCD:6162172