纯Al在3种典型沿海、工业和乡村大气中2的腐蚀行为
Characterization of Corrosion Products on Pure Al Exposed in Atmospheres at Typical Rural, Industrial and Coastal Areas in China
查看参考文献19篇
|
文摘
|
纯Al在沿海、工业以及乡村大气环境中暴露12个月之后,利用电化学阻抗谱技术(EIS)以及扫描电镜(SEM)研究腐蚀产物对纯Al大气腐蚀过程的影响。结果表明,纯Al在沿海环境中腐蚀最为严重,在工业环境2中次之,在乡村环境中最轻。在沿海与工业环境中,纯Al表面形成了不同厚度的腐蚀产物层;在乡村环境中,2只有少量腐蚀产物分散存在,未形成连续的腐蚀产物层。纯Al大气腐蚀的速率控制步骤在沿海环境中为扩散2过程;在工业与乡村环境中为电荷转移过程。 |
|
其他语种文摘
|
Pure Al plates were exposed in different atmospheres for 12 months at three typical test sites respectively: i.e. a rural site at Xishuangbanna of Yunnan province, an industrial site at Jiangjin of Sichuan province and a coastal site at Wanning of Hainan province. Then the corroded Al plates were characterized by means of EIS technique and SEM. The results indicate that the corrosion resistance of pure Al is the worst in the coastal atmosphere, the best in the rural atmosphere and the middle in the industrial atmosphere. Different thick layers of corrosion products were formed on Al surface in the rural and industrial atmosphere. In the contrast, a few corrosion products were formed dispersedly in the coastal atmosphere. The rate controlling step may be the diffusion of corrosive ions for the corrosion process in the coastal atmosphere, while the charge transfer for those in the rural and industrial atmospheres. |
|
来源
|
中国腐蚀与防护学报
,2016,36(1):47-51 【核心库】
|
|
DOI
|
10.11902/1005.4537.2015.018
|
|
关键词
|
大气腐蚀
;
Al EIS
;
腐蚀产物
|
|
地址
|
中国科学院金属研究所, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1005-4537 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
国防技术基础项目
|
|
文献收藏号
|
CSCD:5646048
|
参考文献 共
19
共1页
|
|
1.
Wang B B. Atmospheric corrosion of aluminium alloy 2024-T3 exposed to salt lake environment in western China.
Corros. Sci,2012,59:63
|
CSCD被引
31
次
|
|
|
|
|
2.
王振尧. 3种有色金属在沈阳地区的大气腐蚀规律.
中国有色金属学报,2003,13(2):372
|
CSCD被引
1
次
|
|
|
|
|
3.
孙霜青. LY12铝合金的长期大气腐蚀行为.
中国腐蚀与防护学报,2009,29(6):442
|
CSCD被引
7
次
|
|
|
|
|
4.
Sun S Q. Long-term atmospheric corrosion behaviour of aluminium alloys 2024 and 7075 in urban, coastal and industrial environments.
Corros. Sci,2009,51(4):719
|
CSCD被引
44
次
|
|
|
|
|
5.
Sun S Q. Exfoliation corrosion of extruded 2024- T4 in the coastal environments in China.
Corros. Sci,2011,53(8):2527
|
CSCD被引
17
次
|
|
|
|
|
6.
Sun S Q. Atmospheric corrosion of aluminium in the northern Taklamakan desert environment.
Mater. Corros,2010,61(10):852
|
CSCD被引
5
次
|
|
|
|
|
7.
Li T. Characterization of atmospheric corrosion of 2A12 aluminum alloy in tropical marine environment.
J. Mater. Eng. Perform,2010,19(4):591
|
CSCD被引
21
次
|
|
|
|
|
8.
Vilchf J R. A survey of Argentinean atmospheric corrosion I-Aluminium and zinc samples.
Corros. Sci,1995,37(6):941
|
CSCD被引
9
次
|
|
|
|
|
9.
Vera R. Effect of atmospheric pollutants on the corrosion of high power electrical conductors: Part 1. Aluminium and AA6201 alloy.
Corros. Sci,2006,48(10):2882
|
CSCD被引
28
次
|
|
|
|
|
10.
Dan Z. Applicability of constant dew point corrosion tests for evaluating atmospheric corrosion of aluminium alloys.
Corros. Sci,2011,53(5):2006
|
CSCD被引
13
次
|
|
|
|
|
11.
Natesan M. Kinetics of atmospheric corrosion of mild steel, zinc, galvanized iron and aluminium at 10 exposure stations in India.
Corros. Sci,2006,48(11):3584
|
CSCD被引
39
次
|
|
|
|
|
12.
.
GB/T 16545-1996.金属和合金的腐蚀腐蚀试样上腐蚀产物的清除
|
CSCD被引
1
次
|
|
|
|
|
13.
Vargel C.
Corrosion of Aluminium,2004
|
CSCD被引
10
次
|
|
|
|
|
14.
Chung S C. Application of EIS to the initial stages of atmospheric zinc corrosion.
J. Appl. Electrochem,2000,30:607
|
CSCD被引
7
次
|
|
|
|
|
15.
De la Fuente D. Studies of long-term weathering of aluminium in the atmosphere.
Corros. Sci,2007,49(7):3134
|
CSCD被引
30
次
|
|
|
|
|
16.
Yan M C. Corrosion inhibition performance of polypyrrole Al flake composite coatings for Al alloys.
Corros. Sci,2013,70:37
|
CSCD被引
9
次
|
|
|
|
|
17.
Liu C. EIS comparison on corrosion performance of PVD TiN and CrN coated mild steel in 0.5 N NaCl aqueous solution.
Corros. Sci,2001,43:1953
|
CSCD被引
27
次
|
|
|
|
|
18.
Hsu C H. Concerning the conversion of the constant phase element parameter Y_0 into a capacitance.
Corrosion,2001,57:2
|
CSCD被引
1
次
|
|
|
|
|
19.
曹楚南.
腐蚀电化学原理,2008:184
|
CSCD被引
4
次
|
|
|
|
|
了解气象卫星更多信息，请访问