(MCrAlY+AlSiY)复合涂层的高温氧化行为
HIGH TEMPERATURE OXIDATION BEHAVIOR OF A (MCrAlY+AlSiY) COMPOSITE COATING
查看参考文献14篇
|
文摘
|
采用电弧离子镀技术在镍基高温合金K465上制备了(MCrAlY+AlSiY)复合涂层,分析了复合涂层的组织及结构,对比研究了NiCoCrAlYSiB单一涂层及(NiCoCrAlYSiB+AlSiY)复合涂层分别在1000及1100℃时的恒温氧化行为和从1000℃到室温的循环氧化行为.结果表明:退火后复合涂层外层主要由β-(Ni,Co)Al相及少量σ-NiCoCr和Cr_3Si相组成,内层主要是富Cr相及少量β-(Ni,Co)Al相.氧化过程中由于Al的消耗,单一涂层表面生成了尖晶石和NiO,而复合涂层中的β-(Ni,Co)Al相退化成γ/γ'相,提供Al源支持表面Al_2O_3膜的形成和修复,从而提高了抗高温氧化性能. |
|
其他语种文摘
|
A composite coating (MCrAlY+AlSiY) was prepared on a Ni-based superalloy K465 by arc ion plating technique. The oxidation behaviors of the composite coating and the reference coating NiCoCrAlYSiB were investigated. The results show that the outer layer of composite coating consists of β-(Ni, Co)Al and dispersed σ-NiCoCr and Cr_3Si, and the inner layer of composite coating consists of Cr-rich phases and minor β-(Ni, Co)Al after vacuum annealing at 1050 ℃ Because of the excessive consumption of Al, the spinels and NiO are formed on the surface of the reference coating. For the composite coating, the protective alumina scale is continuous and dense. The enhanced oxidation resistance of the composite coating is related to the gradient distributions of Al-enriched outer layer and Cr-enriched inner layer. |
|
来源
|
金属学报
,2009,45(3):378-384 【核心库】
|
|
关键词
|
NiCoCrAlYSiB
;
AlSiY
;
复合涂层
;
电弧离子镀
;
高温氧化
|
|
地址
|
1.
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 辽宁, 沈阳, 110016
2.
中国航空工业第一集团公司沈阳黎明航空发动机(集团)有限责任公司, 辽宁, 沈阳, 110043
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
0412-1961 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:3530521
|
参考文献 共
14
共1页
|
|
1.
Nicholls J R.
MRS Bulletin,2003,28:1
|
CSCD被引
2
次
|
|
|
|
|
2.
Goward G W.
Surface and Coatings Technology,1998,68:73
|
CSCD被引
111
次
|
|
|
|
|
3.
Jeanine T D.
Surface and Coatings Technology,1994,68:1
|
CSCD被引
35
次
|
|
|
|
|
4.
Padture N P.
Science,2002,296:280
|
CSCD被引
596
次
|
|
|
|
|
5.
Tang F.
Oxidation of Metals,2004,61:219
|
CSCD被引
15
次
|
|
|
|
|
6.
Nicholls J R.
Surface and Coatings Technology,2002,149:236
|
CSCD被引
33
次
|
|
|
|
|
7.
Guo M H.
Surface and Coatings Technology,2006,200:3942
|
CSCD被引
16
次
|
|
|
|
|
8.
Guo M H.
Corrosion Science,2006,48:2750
|
CSCD被引
15
次
|
|
|
|
|
9.
Wang Q M.
Surface and Coatings Technology,2004,186:389
|
CSCD被引
20
次
|
|
|
|
|
10.
Wu Y N.
Surface and Coatings Technology,2006,200:2857
|
CSCD被引
9
次
|
|
|
|
|
11.
Brumm M W.
Corrosion Science,1992,33:1677
|
CSCD被引
34
次
|
|
|
|
|
12.
Rybicki G C.
Oxidation of Metals,1989,31:275
|
CSCD被引
31
次
|
|
|
|
|
13.
Gale W F.
Surface and Coatings Technology,1992,54/55:8
|
CSCD被引
4
次
|
|
|
|
|
14.
Rnsovic N.
Physical Status Solidi A,1977,44:609
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问