蠕墨铸铁激光合金化熔覆的界面组织及性能
Microstructure and mechanical properties of NiCoCrAlY coating on compacted graphite iron by laser cladding
查看参考文献14篇
|
文摘
|
针对铸铁激光熔覆涂层结合界面淬火硬化、裂纹倾向大的问题,提出激光合金化与激光熔覆相结合的工艺在蠕墨铸铁表面制备NiCoCrAlY合金涂层。通过光学显微镜、扫描电子显微镜、X射线衍射仪、维氏硬度计研究了激光合金化熔覆中熔覆层稀释率、组织、显微硬度的演化规律,通过三点弯曲试验考察了熔覆层的结合特性及力学性能。结果表明:激光合金化熔覆工艺方法将热影响区由马氏体组织转变为回火索氏体组织,降低了淬硬层深度,改善了熔覆层结合特性与塑性,抗弯强度提高到891MPa。断口显示,熔覆层与基体结合良好,断裂机制是脆性解理断裂与韧窝断裂混合机制。 |
|
其他语种文摘
|
Considering the problem of quench hardening and cracking at the interface of laser cladding coating on the cast iron,a method combined laser alloy and laser cladding was proposed to produce NiCoCrAlY coating on compacted graphite iron.The dilution, microstructure and microhardness of the coating were investigated by means of optical microscope,scanning electron microscopy,X-ray diffractometer,Vickers hardness tester.The bonding characteristics and mechanical properties of the layer were evaluated by three-point bending test.The results show that martensite turns to tempered sorbite in heat affected zone by the laser alloy cladding method,thus the depth of hardening layer decreases.Simultaneously,the bonding characteristics and plasticity are improved,and the bending strength is raised to 891 MPa.The fracture morphology shows a good bonding between coating and substrate,and also a combination of cleavage fracture and dimple fracture. |
|
来源
|
材料热处理学报
,2015,36(3):171-176 【核心库】
|
|
DOI
|
10.13289/j.issn.1009-6264.2015.03.031
|
|
关键词
|
蠕墨铸铁
;
激光熔覆
;
稀释率
;
显微组织
;
抗弯强度
|
|
地址
|
中国科学院力学研究所, 中国科学院先进制造工艺力学重点实验室, 北京, 100190
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1009-6264 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
;
江苏高校优势学科建设工程
|
|
文献收藏号
|
CSCD:5407649
|
参考文献 共
14
共1页
|
|
1.
Ehsan Toyserkani.
Laser Cladding,2005
|
CSCD被引
15
次
|
|
|
|
|
2.
钟敏霖. 国际激光材料加工研究的主导领域与热点.
中国激光,2008,35(11):1653-1659
|
CSCD被引
43
次
|
|
|
|
|
3.
Dubourg L. Technological and scientific landscape of laser cladding process in 2007.
Sur Coat Tech,2008,202(24):5863-5869
|
CSCD被引
23
次
|
|
|
|
|
4.
Bekir S Y.
Laser Surface Processing and Model Studies,2013
|
CSCD被引
1
次
|
|
|
|
|
5.
Dawson S. Practical applications for compacted graphite iron.
AFS Transactions,2004,71(1):1211-1216
|
CSCD被引
1
次
|
|
|
|
|
6.
聂树真.
强度分布整形激光束加载模拟热负荷温度场的实验研究,2011:2-14
|
CSCD被引
1
次
|
|
|
|
|
7.
周振峰.
铸铁焊接冶金与工艺,2001
|
CSCD被引
1
次
|
|
|
|
|
8.
董世运. 铸铁件激光熔覆NiCuFeBSi合金组织及力学性能.
中国激光,2012,39(12):67-73
|
CSCD被引
7
次
|
|
|
|
|
9.
Lestan Z. Laser deposition of Metco 15E,Colmony 88 and VIM CRU 20 powders on cast iron and low carbon steel.
International Journal of Advanced Manufacturing Technology,2013,66(9/12):2023-2028
|
CSCD被引
4
次
|
|
|
|
|
10.
谭真.
工程合金热物性,1994
|
CSCD被引
84
次
|
|
|
|
|
11.
Zhang X. Modeling of the residual stresses in plasma-spraying functionally graded ZrO2 /NiCoCrAlY coatings using finite elements method.
Materials & design,2006,27(4):308-315
|
CSCD被引
1
次
|
|
|
|
|
12.
乔虹. 激光熔覆工艺参数对Fe-Cr-B合金涂层组织和硬度的影响.
材料热处理学报,2014,35(2):164-168
|
CSCD被引
12
次
|
|
|
|
|
13.
刘秀波. 等离子熔覆γ/Cr_7C_3复合材料涂层组织与耐磨性研究.
材料热处理学报,2006,27(6):114-117
|
CSCD被引
6
次
|
|
|
|
|
14.
Li Z Y. Fatigue crack propagation in laser alloyed ductile cast iron surface.
Journal of Laser Applications,2013,25(1):012003
|
CSCD被引
1
次
|
|
|
|
|
了解气象卫星更多信息，请访问