小角度晶界对DD5镍基单晶高温合金中、高温条件下力学性能的影响
Effect of low angle grain boundaries on mechanical properties of DD5single crystal Ni-base superalloy at medium temperature and high temperature
查看参考文献21篇
|
文摘
|
采用双籽晶制备第二代镍基单晶高温合金DD5合金双晶试板并加工成力学试样,研究小角度晶界对DD5合金中、高温条件下拉伸、持久性能的影响。结果表明:在760℃拉伸条件下,晶界角度小于14.8°时,试样抗拉强度大于1100MPa,伸长率大于8%,断面收缩率大于14%,晶界角度大于14.8°后,抗拉强度、伸长率以及断面收缩率随着晶界角度的增大而下降,屈服强度则没有显著变化;在980℃拉伸中,晶界角度小于19.4°时,试样抗拉强度大于760MPa,屈服强度大于630MPa,伸长率以及断面收缩率则随晶界角度的增大而快速下降,至19.4°时,伸长率下降至1.4%,断面收缩率下降至2.8%;在870℃/551MPa持久条件下,当晶界角度小于7.8°时,试样持久寿命大于110h,伸长率大于19.8%,断面收缩率大于23.1%,当晶界角度大于7.8°后,试样持久寿命、伸长率以及断面收缩率随晶界角度的增大而快速下降。 |
|
其他语种文摘
|
The effects of low angle grain boundaries on the tensile properties and stress rupture properties of second generation single crystal superalloy DD5at medium temperature and high temperature were investigated.The test plates were prepared by using seeds and processed into mechanical samples.The results show that the tensile strength at 760℃is higher than 1100MPa,the elongation is higher than 8%and the percentage reduction of area is higher than 14% when the angle is below 14.8°.The tensile strength,elongation and percentage reduction of area are decreased when the angle is above 14.8°.But the yield strength shows no difference.The tensile strength at 980℃is higher than 760 MPa,the yield strength is higher than 630 MPa,the elongation and percentage reduction of area are decreased quickly when the angle is below 19.4°.The elongation is 1.4%,the percentage reduction of area is 2.8% when the angle is 19.4°.The rupture life at 870℃/551MPa is higher than 110h,the elongation is higher than 19.8%and the percentage reduction of area is higher than 23.1% when the angle is below 7.8°.But they are decreased quickly when the angle is above 7.8°. |
|
来源
|
材料工程
,2020,48(10):114-122 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2020.000002
|
|
关键词
|
高温合金
;
小角度晶界
;
持久寿命
;
拉伸性能
|
|
地址
|
中国航发北京航空材料研究院, 先进高温结构材料国防科技重点实验室, 北京, 100095
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:6839808
|
参考文献 共
21
共2页
|
|
1.
Gell M. The development of single crystal superalloy turbine blades.
Superalloys 1980,1980:205-214
|
CSCD被引
20
次
|
|
|
|
|
2.
Broomfield R W. Development and turbine engine performance of three advanced rhenium containing superalloys for single crystal and directionally solidified blades and vanes.
Transactions of the ASME,1998,120(3):596-608
|
CSCD被引
9
次
|
|
|
|
|
3.
Walston W S. ReneN6: Third generation single crystal superalloy.
Superalloys 1996,1996:27-34
|
CSCD被引
44
次
|
|
|
|
|
4.
Harris K. Development of the rhenium containing superalloys CMSX-4 &CM186LC for single crystal blade and directionally solidified vane applications in advanced turbine engines.
Superalloys 1992,1992:297-306
|
CSCD被引
18
次
|
|
|
|
|
5.
Harris K. Improved single crystal superalloys CMSX-4(SLS)[La+Y]and CMSX-486.
Superalloys 2004,2004:45-52
|
CSCD被引
12
次
|
|
|
|
|
6.
陈荣章. 铸造高温合金发展的回顾与展望.
航空材料学报,2000,20(1):55-61
|
CSCD被引
33
次
|
|
|
|
|
7.
Koizumi Y. Development of next-generation Ni-base single crystal superalloy.
Superalloys 2004,2004:35-43
|
CSCD被引
21
次
|
|
|
|
|
8.
Pollock T M. Grain defect formation during directional solidification of nickel base single crystals.
Superalloys 1992,1992:125-134
|
CSCD被引
21
次
|
|
|
|
|
9.
Chen Q Z. The grain boundary microstructures of the base and modified RR2072bicrystal superalloys and their effects on the creep properties.
Materials Science and Engineering,2004,385(1/2):402-418
|
CSCD被引
27
次
|
|
|
|
|
10.
Ross E W. Rene N4:a first generation single crystal turbine airfoil alloy with improved oxidation resistance, low angle boundary strength and superior long time rupture strength.
Superalloys 1996,1996:19-25
|
CSCD被引
19
次
|
|
|
|
|
11.
史振学. DD6单晶高温合金扭转小角度晶界的拉伸性能.
航空材料学报,2009,29(3):88-92
|
CSCD被引
4
次
|
|
|
|
|
12.
赵金乾. 小角度晶界对单晶高温合金DD6拉伸性能的影响.
材料工程,2008(8):73-76
|
CSCD被引
5
次
|
|
|
|
|
13.
Cui R J. Microstructual evolution and stability of second generation single crystal nickel-based superalloy DD5.
Transactions of Nonferrous Metals Society of China,2016,26(8):2079-2085
|
CSCD被引
14
次
|
|
|
|
|
14.
崔仁杰. 980℃长期时效对第二代镍基单晶高温合金DD5组织与性能的影响.
材料热处理学报,2016,37(6):78-83
|
CSCD被引
2
次
|
|
|
|
|
15.
曹亮. 晶界角度对一种镍基双晶高温合金持久性能的影响.
金属学报,2014,50(1):11-18
|
CSCD被引
10
次
|
|
|
|
|
16.
秦健朝. 小角度晶界对DD5镍基单晶高温合金力学性能的影响.
航空材料学报,2017,37(3):24-29
|
CSCD被引
6
次
|
|
|
|
|
17.
刘志义. DD8镍基高温合金单晶制备中的杂晶长大机制.
金属学报,2000,36(1):1-6
|
CSCD被引
7
次
|
|
|
|
|
18.
周亦胄. 双晶镍基高温合金定向凝固过程的结构演化.
金属学报,2010,46(11):1327-1334
|
CSCD被引
18
次
|
|
|
|
|
19.
Goldschmidt D. Porosity clusters and recrystallization in single-crystal components.
Superalloys 1992,1992:155-164
|
CSCD被引
14
次
|
|
|
|
|
20.
Liu L R. Microstructural evolution of a single crystal nickel-base superalloy during thermal exposure.
Materials Letters,2003,57(29):4540-4546
|
CSCD被引
14
次
|
|
|
|
|
了解气象卫星更多信息，请访问