H_(Sn)70-1B铜管在碱性NaCl溶液中的腐蚀行为
Corrosion behavior of H_(Sn)70-1B tube in alkaline sodium chloride solution
查看参考文献12篇
|
文摘
|
利用表面分析技术和电化学方法研究了H_(Sn)70-1B铜管在碱性NaCl溶液中的腐蚀行为。在自腐蚀状态下，H_(Sn)70-1B铜管表面生成以Cu_2O为主的表面膜；在阳极极化电位下表面CuCl的生成反应为一级反应，电极表面形成CuCl膜后，存在极限电流密度；电化学阻抗频谱（EIS）有2个容抗弧，随Cl~-含量的增加，容抗弧逐渐收缩，弥散性增大。 |
|
其他语种文摘
|
Corrosion behavior of H_(Sn)70-1B tube in alkaline sodium chloride solution has been investigated by electrochemical methods and surface analysis techniques. By free corrosion, Cu_2O film is observed on the surface of H_(Sn)70-1B tube. The anodic polarization curves exhibit that there exists rapid growth of anodic dissolution current and diffusion process control reactions on the electrode surface. Two semicircles are found in electrochemical impedance spectroscopy, and with the growth of content of chloride the semicircle's diameter decrease gradually. |
|
来源
|
腐蚀科学与防护技术
,2002,14(2):67-72 【核心库】
|
|
关键词
|
H_(Sn)70-1B铜管
;
极化
;
阻抗谱
;
扩散
|
|
地址
|
中国科学院金属研究所, 金属腐蚀与防护国家重点实验室, 沈阳, 110016
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1002-6495 |
|
学科
|
金属学与金属工艺 |
|
文献收藏号
|
CSCD:983717
|
参考文献 共
12
共1页
|
|
1.
Pickering H W.
Electrochem. Soc.,1967,114:698
|
被引
11
次
|
|
|
|
|
2.
Newman R C.
Corros. Sci.,1988,28:873
|
被引
1
次
|
|
|
|
|
3.
Scully J C.
Met. Sci.,1978,12:290
|
被引
1
次
|
|
|
|
|
4.
Hardie D.
Br. Corros. J.,1987,22:202
|
被引
1
次
|
|
|
|
|
5.
Verink E D Jr.
Corrosion,1970,26:5
|
被引
2
次
|
|
|
|
|
6.
Heidersbach R.
Corrosion,1968,24:38
|
被引
2
次
|
|
|
|
|
7.
周业蓉.
腐蚀科学与防护技术,1989,1:28
|
被引
1
次
|
|
|
|
|
8.
孙理. 硼对70/30黄铜腐蚀性能的影响.
中国腐蚀与防护学报,1990,10(4):371
|
被引
11
次
|
|
|
|
|
9.
Boukamp B A.
Solide State Ionics,1986,18/19:136
|
被引
3
次
|
|
|
|
|
10.
Mansfeld F.
162nd Meeting, the Electrochem. Soc. Abstract,1982:64
|
被引
1
次
|
|
|
|
|
11.
王佳. 孔蚀发展期的电极阻抗频谱特征.
中国腐蚀与防护学报,1989,9(4):271
|
被引
38
次
|
|
|
|
|
12.
曹楚南.
腐蚀电化学,1994:91
|
被引
8
次
|
|
|
|
|
|
了解气象卫星更多信息，请访问