热处理对TiAl/Ti_2AlNb放电等离子扩散焊接头微观组织与力学性能的影响
Effect of heat treatment on microstructure and mechanical properties of TiAl/Ti_2AlNb joint by spark plasma diffusion bonding
查看参考文献17篇
|
文摘
|
采用放电等离子扩散连接方法,实现了TiAl/Ti_2AlNb合金扩散连接,对焊后的接头进行不同温度的热处理,分析热处理后接头显微组织,并检测接头抗拉强度和显微硬度。结果表明:热处理后Ti_2AlNb母材、TiAl母材和界面处显微形貌无明显变化;Ti_2AlNb热影响区发生B2相向O相转变,由于针状O相的析出,热影响区的显微硬度较焊态显著增加。随着热处理温度的升高,Ti_2AlNb热影响区的显微硬度逐渐减小,接头的室温抗拉强度逐渐增加。当热处理温度为900℃时,接头抗拉强度最大为376MPa。热处理后接头的断裂方式为脆性断裂。 |
|
其他语种文摘
|
TiAl/Ti_2AlNb dissimilar alloys were successfully bonded together by spark plasma diffusion bonding.The joints were subjected to post-weld heat treatment at different temperatures.The microstructure of the welded joint was analyzed and the tensile strength and microhardness of the joint were tested.The results indicate that after heat treatment,the microstructure of Ti_2AlNb base metal, TiAl base metal and interface has no obvious change.In the Ti_2AlNb heat affected zone(HAZ),most B2phase gradually turns into O phase,due to the precipitation of acicular O phase,the microhardness increases significantly compared to as welded condition. With the increase of heat treatment temperature,the microhardness of the Ti_2AlNb HAZ gradually decreases,meanwhile,the tensile strength of the joint at room temperature shows an evident increase compared to as welded.The maximum tensile strength of the joint reaches 376MPa at heat treatment temperature of 900℃.After heat treatment,the fracture mode of the joint is brittle fracture. |
|
来源
|
材料工程
,2021,49(9):87-93 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2019.000866
|
|
关键词
|
放电等离子扩散焊
;
TiAl
;
Ti_2AlNb
;
抗拉强度
;
显微硬度
|
|
地址
|
1.
中国航空制造技术研究院, 航空焊接与连接技术航空科技重点实验室, 北京, 100024
2.
大连交通大学材料科学与工程学院, 辽宁, 大连, 116028
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
金属学与金属工艺 |
|
基金
|
国家自然科学基金
|
|
文献收藏号
|
CSCD:7073079
|
参考文献 共
17
共1页
|
|
1.
Loria E A. Gamma titanium aluminides as prospective structural materials.
Intermetallics,2000,8(9/11):1339-1345
|
被引
104
次
|
|
|
|
|
2.
Wei H E. Microstructure and tensile properties of containerless near-isothermally forged TiAl alloys.
Transactions of Nonferrous Metals Society of China,2011,21(12):2605-2609
|
被引
1
次
|
|
|
|
|
3.
Kong F. High temperature deformation behavior of Ti-46Al-2Cr-4Nb-0.2Yalloy.
Materials Science and Engineering:A,2012,539(2):107-114
|
被引
3
次
|
|
|
|
|
4.
司玉锋. Ti2AlNb基合金的研究进展.
宇航材料工艺,2006,36(3):10-13
|
被引
32
次
|
|
|
|
|
5.
Wang Y H. Microstructure and mechanical properties of high Nb containing TiAl alloys by reactive hot pressing.
Journal of Alloys and Compounds,2008,461(1/2):367-372
|
被引
10
次
|
|
|
|
|
6.
Wang Y H. Microstructures and mechanical properties of Ti-45Al-8.5Nb-(W,B,Y)alloy by SPS-HIP route.
Materials Science and Engineering:A,2008,489(1):55-61
|
被引
8
次
|
|
|
|
|
7.
Zhang S Z. Phase transformation and microstructure evolution of differently processed Ti-45Al-9Nb-Y alloy.
Intermetallics,2012,31(4):208-216
|
被引
10
次
|
|
|
|
|
8.
静永娟. Ti_3Al基合金TLP扩散连接界面的组织演变.
焊接学报,2013,34(2):71-74
|
被引
4
次
|
|
|
|
|
9.
刘加奇.
TiAl/Ti2AlNb合金钎焊工艺与机理研究,2016
|
被引
2
次
|
|
|
|
|
10.
Cao J. Relationship between microstructure and mechanical properties of TiAl/Ti2AlNb joint brazed using Ti-27Co eutectic filler metal.
Materials & Design,2017,121:176-184
|
被引
10
次
|
|
|
|
|
11.
任海水. 以Ti-Zr-Cu-Ni-Fe合金为中间层的Ti_3 Al/TiAI瞬间液相扩散连接.
焊接学报,2016,37(3):106-110
|
被引
4
次
|
|
|
|
|
12.
Ren H S. Microstructures and mechanical properties of transient liquid-phase diffusion-bonded Ti_3Al/TiAl joints with Ti-Zr-Cu-Ni interlayer.
Metallurgical and Materials Transactions A,2016,47(4):1668-1676
|
被引
4
次
|
|
|
|
|
13.
吕彦龙. TiAl/Ti_2AlNb放电等离子扩散接头的组织性能研究.
热加工工艺,2018,47(19):72-76
|
被引
2
次
|
|
|
|
|
14.
吴波. Ti-22Al-27Nb合金平衡相结构预测.
稀有金属,2002,26(1):12-14
|
被引
7
次
|
|
|
|
|
15.
张永刚.
金属间化合物结构材料,2001:795-797
|
被引
2
次
|
|
|
|
|
16.
Chen X. Microstructure evolution and mechanical properties of linear friction welded Ti2AlNb alloy.
Journal of Alloys and Compounds,2015,646:490-496
|
被引
23
次
|
|
|
|
|
17.
Wang W. Quantitative analysis of the effect of heat treatment on microstructural evolution and microhardness of an isothermally forged Ti-22Al-25Nb(at.%)orthorhombic alloy.
Intermetallics,2014,45:29-37
|
被引
17
次
|
|
|
|
|
了解气象卫星更多信息，请访问