硅溶胶添加对氧化铝多孔陶瓷烧结性能的影响
Effect of silica sol addition on sintering properties of porous alumina ceramics
查看参考文献17篇
|
文摘
|
以煅烧α-Al_2O_3粉末为原料,硅溶胶为高温结合剂,羧甲基纤维素钠为成型黏结剂,通过混料、困料、模压成型、高温烧结等工序制备氧化铝多孔陶瓷,利用SEM和XRD对多孔陶瓷微观形貌和晶体结构进行测试,并对多孔陶瓷的线收缩率、体积密度、显气孔率和抗弯强度进行表征,系统地研究硅溶胶添加对氧化铝多孔陶瓷高温烧结特性的影响。结果表明:低温下硅溶胶的热解产物石英型SiO_2将氧化铝颗粒黏结起来,形成物理黏结,能提高多孔陶瓷的力学性能;烧结温度达1500℃时,SiO_2开始与氧化铝反应形成莫来石,莫来石结合相的生成使得氧化铝多孔陶瓷趋于致密,力学性能优异,抗弯强度可达(105.5±8.0)MPa;随烧结温度的升高莫来石生成量增多,导致氧化铝多孔陶瓷的体积膨胀,进而使得孔隙率增大,力学性能降低。烧结温度介于1400~1500℃之间时,可以得到微观结构合理、力学性能优异、孔隙率适中的氧化铝多孔陶瓷。 |
|
其他语种文摘
|
Porous alumina ceramics were prepared by using calcinedα-Al_2O_3as raw material,nano silica sol as high temperature binder and carboxymethy cellulose as molding binder with processes of mixing,aging,molding and sintering.The effect of silica sol addition on sintering properties was investigated by test method of SEM and XRD.The linear shrinkage,volume density,porosity and flexural strength were also tested.The results show that the quartz silicon dioxide which is pyrolysed product from silica sol could bond the alumina particles together to form porous ceramics and improve the mechanical properties.The essence of silica sol bonding is physical bonding.The silicon dioxide in the sol begins to react with alumina to form mullite when the sintering temperature reaches 1500℃,and the porous ceramics tend to be compact with excellence mechanical properties.The flexural strength is about(105.5±8.0)MPa.The content of mullite phase increases with sintering temperature.However,with much higher content of mullite generation,the porosity increases and the mechanical performance degrades.The porous alumina ceramics with excellence performance can be obtained when the sintering temperature is between 1400℃and 1500℃. |
|
来源
|
材料工程
,2021,49(5):151-156 【核心库】
|
|
DOI
|
10.11868/j.issn.1001-4381.2019.000971
|
|
关键词
|
硅溶胶
;
氧化铝多孔陶瓷
;
莫来石
;
烧结特性
|
|
地址
|
贵州师范大学材料与建筑工程学院, 贵阳, 550025
|
|
语种
|
中文 |
|
文献类型
|
研究性论文 |
|
ISSN
|
1001-4381 |
|
学科
|
化学工业 |
|
基金
|
贵州师范大学创新训练项目
;
贵州省自然科学基金
;
贵阳市科技局计划项目
|
|
文献收藏号
|
CSCD:6973174
|
参考文献 共
17
共1页
|
|
1.
Wu P. A review of preparation techniques of porous ceramic membranes.
Journal of Ceramic Processing Research,2015,16(1):102-106
|
被引
5
次
|
|
|
|
|
2.
Nie Z G. Fabrication of porous alumina ceramics using hollow microspheres as the pore-forming agent.
Journal of the Korean Society of Manufacturing Technology Engineers,2015,24(4):368-373
|
被引
1
次
|
|
|
|
|
3.
Juettner T. Structure of kaoline-alumina based foam ceramics for high temperature applications.
Journal of the European Ceramic Society,2007,27(2/3):1435-1441
|
被引
12
次
|
|
|
|
|
4.
Ahmad R. Particle-stabilized ultra-low density zirconia toughened alumina foams.
Journal of the European Ceramic Society,2013,33(13/14):2559-2564
|
被引
10
次
|
|
|
|
|
5.
黄坤模. Al_2O_3多孔陶瓷的制备及性能.
中国陶瓷,2018,54(5):11-15
|
被引
2
次
|
|
|
|
|
6.
黎阳. 低温制备氧化铝多孔陶瓷.
中国陶瓷,2014,50(5):47-50
|
被引
5
次
|
|
|
|
|
7.
孔德玉. 硅溶胶分散氧化铝浆料的免脱气注凝成型工艺.
硅酸盐学报,2005,33(9):1070-1074
|
被引
3
次
|
|
|
|
|
8.
蔡艳芝. 硅溶胶对莫来石结合刚玉质耐火材料力学性能的影响.
硅酸盐学报,2007,35(5):664-670
|
被引
7
次
|
|
|
|
|
9.
朱新文. 氧化铝粉体在硅溶胶中分散行为的研究.
硅酸盐学报,2001,29(3):263-266
|
被引
10
次
|
|
|
|
|
10.
Liden E. Silica sols as refractory fibre binders.
Journal of the European Ceramic Society,2001,21(6):795-808
|
被引
3
次
|
|
|
|
|
11.
Simendic B. Low temperature transformation of alumino-silicate gels.
Ceramics International,1998,24(7):553-557
|
被引
3
次
|
|
|
|
|
12.
Kong D. Gel-casting without de-airing process using silica sol as a binder.
Ceramics International,2007,33(2):133-139
|
被引
6
次
|
|
|
|
|
13.
Ivankovic H. Correlation of the precursor type with densification behavior and microstructure of sintered mullite ceramics.
Journal of the European Ceramic Society,2003,23(2):283-292
|
被引
2
次
|
|
|
|
|
14.
马红萍. 硅溶胶的凝胶化包覆对氧化铝烧结性能的影响.
稀有金属材料与工程,2010,39(增刊2):463-466
|
被引
1
次
|
|
|
|
|
15.
赵惠忠. 纳米莫来石粉体的合成及其表征.
硅酸盐学报,2003,31(12):1216-1220
|
被引
7
次
|
|
|
|
|
16.
陈照峰. 硅溶胶强化辅助制备C纤维增韧氧化铝结合莫来石陶瓷基复合材料.
航空材料学报,2001,21(4):28-32,37
|
被引
2
次
|
|
|
|
|
17.
Behnam A. Simultaneous effects of salted water and water flow on asphalt concrete pavement deterioration under freeze-thaw cycle.
International Journal of Pavement Engineering,2014,15(5):383-391
|
被引
5
次
|
|
|
|
|
了解气象卫星更多信息，请访问