羟基亚乙基二膦酸对20SiMn钢在含Cl~-混凝土模拟孔隙液中的缓蚀行为
Corrosion Inhibition Behavior of 1-Hydroxyethylidene-1, 1-Diphosphonic Acid on 20SiMn Steel in Simulated Concrete Pore Solution Containing Cl~-

查看参考文献36篇

曹凤婷 1,2   魏洁 1   董俊华 1 *   柯伟 1   王铁钢 2   范其香 2  
文摘 采用电化学技术(动电位极化曲线、自腐蚀电位、EIS以及Mott-Schottky曲线)和表面分析方法(SEM、 XPS)研究了羟基亚乙基二膦酸(HEDP)对空冷20SiMn低合金钢在含Cl~-的高碱性混凝土模拟孔隙液中的缓蚀作用及机理。结果表明,HEDP对20SiMn钢在含1 mol/L NaCl饱和Ca(OH)2溶液中的缓蚀效果随HEDP浓度的升高存在极值,最佳浓度为1.441×10~(-4) mol/L。在此浓度下HEDP将20SiMn钢的钝性保持时间从6 h延长至9 h,缓蚀效率达到46.45%~59.78%。在发生点蚀的情况下,HEDP对点蚀的发展亦有显著的抑制作用,缓蚀效率超过93%。电化学和表面分析结果表明,HEDP优先吸附在钝化膜表面,通过竞争吸附机制屏蔽了侵蚀性Cl~-向钝化膜表面的附着,从而对其产生保护作用。
其他语种文摘 The corrosion of steel rebar in concrete will be induced once the passive film is destroyed by chlorides or carbonation. Several techniques have been employed to reduce the corrosion so far. Among them, adding inhibitors is effective one because of its advantages, such as high efficiency and easy handling. 1-hydroxyethylidene-1,1-diphosphonic acid (HEDP), a typical organic phosphonic acid, is a low toxic corrosion inhibitor for steel and iron in neutral aerobic environment. This compound was first used as scale inhibitor in water treatment industry, such as cooling water circulation system. The molecule of HEDP has two phosphate groups, making it a powerful chelating ability with metallic ions. However, most of the current studies of HEDP focus on neutral or near-neutral systems, and there are few reports on the corrosion inhibition of steel reinforcement in alkaline environment. Therefore, it is not clear whether HEDP can play the role of corrosion inhibitor by protecting the passive film and resist foreign corrosive Cl~-. In this work, the inhibition effect of HEDP towards 20SiMn steel was investigated in simulated concrete pore solution contaminated by Cl– (Sat.Ca(OH)2+1 mol/L NaCl) by electrochemical methods (corrosion potential, potentiodynamic polarization curves, EIS and Mott-Schottcky curves) and surface analysis techniques (SEM, XPS). The results showed that HEDP was a mixed inhibitor and its inhibition efficiency increased first and then decreased with the increase of concentration, the optimal concentration is 1.441×10~(-4) mol/L. At the optimal concentration, HEDP could obviously enlarge the passive region, prolong the passive period of 20SiMn steel from 6 h to 9 h, and improve the charge-transfer resistance significantly with the inhibition efficiency around 46.45%~59.78%. When pitting corrosion occurs, HEDP could hinder its development with the inhibition efficiency over 93%. The inhibition mechanism was the preferential adsorption of HEDP over Cl~- by forming a complete adsorption film outside the passive film of the steel.
来源 金属学报 ,2020,56(6):898-908 【核心库】
DOI 10.11900/0412.1961.2019.00382
关键词 羟基亚乙基二膦酸 ; 腐蚀 ; 缓蚀剂 ; 吸附 ; 混凝土模拟孔隙液
地址

1. 中国科学院金属研究所, 沈阳材料科学国家研究中心, 沈阳, 110016  

2. 天津职业技术师范大学机械工程学院, 天津市高速切削与精密加工重点实验室, 天津, 300222

语种 中文
文献类型 研究性论文
ISSN 0412-1961
学科 金属学与金属工艺
基金 国家自然科学基金项目
文献收藏号 CSCD:6729615

参考文献 共 36 共2页

1.  Biezma M V. Methodology to study cost of corrosion. Corros. Eng. Sci. Technol,2005,40:344 被引 6    
2.  Page C L. Aspects of the electrochemistry of steel in concrete. Nature,1982,297:109 被引 17    
3.  Jones S. Simulation studies of methods to delay corrosion and increase service life for cracked concrete exposed to chlorides. Cem. Concr. Compos,2015,58:59 被引 5    
4.  曹凤婷. 20SiMn钢在恒定pH值的碳酸盐溶液中的腐蚀行为. 金属学报,2014,50:674 被引 4    
5.  Andrade C. Pore solution chemistry and corrosion in hydrated cement systems containing chloride salts: A study of cation specific effects. Br. Corros. J,1986,21:49 被引 1    
6.  Pourbaix M. Some applications of potential-pH diagrams to the study of localized corrosion. J. Electrochem. Soc,1976,123:C25 被引 2    
7.  Abd El Haleem S M. Environmental factors affecting the corrosion behaviour of reinforcing steel. VI. Benzotriazole and its derivatives as corrosion inhibitors of steel. Corros. Sci,2014,87:321 被引 4    
8.  Zhou X. Investigation on the inhibition behavior of a pentaerythritol glycoside for carbon steel in 3.5% NaCl saturated Ca(OH)_2 solution. Corros. Sci,2012,54:193 被引 8    
9.  Felhosi I. Effects of bivalent cations on corrosion inhibition of steel by 1-hydroxyethane-1, 1-diphosphonic acid. J. Electrochem. Soc,1999,146:961 被引 3    
10.  Karman F H. The role of oxide layer formation during corrosion inhibition of mild steel in neutral aqueous media. Electrochim. Acta,1998,43:69 被引 4    
11.  Akrout H. Adsorption of corrosion inhibitors (SA, HEDP) using EQCM: Chloride effect and synergic behavior. J. Mater. Sci,2012,47:8085 被引 1    
12.  Awad H S. Role of complexes in inhibition of mild steel by zinc-1-hydroxyethylidene-1, 1-diphosphonic acid mixtures. Br. Corros. J,2002,37:147 被引 2    
13.  Kolodynska D. Cu(II), Zn(II), Ni(II), and Cd(II) complexes with HEDP removal from industrial effluents on different ion exchangers. Ind. Eng. Chem. Res,2010,49:2388 被引 1    
14.  Wang Z L. A study on electroplating of zinc nickel alloy with HEDP plating bath. Russ. J. Electrochem,2006,42:22 被引 2    
15.  Lacour S. Influence of carbonate and calcium ions on the phosphonate complexation with Cu, Zn, Cd and Ni in fresh waters: An evaluation of thermodynamic constants and a chemical model. Environ. Technol,1999,20:249 被引 1    
16.  Pu S M. Zirconium ions integrated in 1-hydroxyethylidene-1,1-diphosphonic acid (HEDP) as a metalorganic-like complex coating on biodegradable magnesium for corrosion control. Corros. Sci,2018,144:277 被引 2    
17.  Sekine I. Effect of 1-hydroxyethylidene-1, 1-diphosphonic acid on the corrosion of SS 41 steel in 0.3% sodium chloride solution. Corrosion,1986,42:272 被引 22    
18.  Mohammedi D. Synergistic or additive corrosion inhibition of mild steel by a mixture of HEDP and metasilicate at pH 7 and 11. Mater. Corros,2004,55:837 被引 1    
19.  Awad H S. The effect of zinc-to-HEDP molar ratio on the effectiveness of zinc-1, hydroxyethylidene-1, 1 diphosphonic acid in inhibiting corrosion of carbon steel in neutral solutions. Anti-Corros. Method Mater,2005,52:22 被引 1    
20.  魏洁. 化学冷却工艺提高热轧螺纹钢耐蚀性的研究,2009 被引 1    
引证文献 5

1 唐荣茂 十二烷基苯磺酸钠在模拟混凝土孔隙液中对Q235钢缓蚀及吸附行为研究 中国腐蚀与防护学报,2021,41(6):857-863
被引 2

2 靳文章 电化学高级氧化对HEDP的降解效能研究 化工学报,2022,73(9):4062-4069
被引 0 次

显示所有5篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号