固溶和时效温度对TC6钛合金显微组织与力学性能的影响
Effects of Solution-Treatment and Aging Temperature on Microstructure and Mechanical Properties of TC6 Titanium Alloy

查看参考文献16篇

文摘 研究了不同温度的固溶和时效工艺对TC6钛合金显微组织和性能的影响。结果表明:800~840 ℃固溶后,合金由初生α相和亚稳β相组成,两相随着温度升高而长大,合金强度和塑性略有上升;880 ℃固溶后,亚稳β相依然保留到室温,然而在拉伸过程中出现应力诱变斜方马氏体α″相,导致双屈服现象;920~960 ℃固溶后,初生α相减少,大量的细针状斜方马氏体α″相在亚稳β相上析出,强度上升塑性下降;当超过β相变点固溶后,主要由粗大针状六方马氏体α'相组成,强度下降同时拉伸为脆性断裂。对于固溶样品经过不同温度时效处理,主要变化过程是亚稳β相分解为次生α相及其长大,300 ℃时效后,相比固溶态强度上升但塑性下降,亚稳β相中弥散析出次生α相及少量的ω相;当时效温度升高到400 ℃,强度继续上升接近最大值但塑性最差;500 ℃时效后,强度最高然而合金元素充分扩散,塑性得到提升;550 ℃时效后,强度有所下降但塑性明显提升,此时具有较佳的强塑性匹配;600~700 ℃时效后,初生 α相聚集长大并且含量增加,次生α相在β基体上析出且逐渐长大为层片状,强度下降塑性进一步提升。
其他语种文摘 Effects of solution-treatment and aging temperature on microstructure and mechanical properties of TC6 titanium alloy were investigated.The results show that when specimens are solution-treated is at 800~840 °C,primary α and metastable β phases are form and they grow up with the increase of the temperature,which result in the slight increase of the strength and ductility.The metastable β phase is also retained after solution-treatment at 880 °C though its stability is weakened,while at this moment double yield phenomenon is observed,which is attributed to stress-induced α″ orthorhombic martensite in the metastable β phase.When specimens are solution-treated at 920~960 °C,primary α phase dissolves,and a large amount of fine acicular α″ orthorhombic martensite precipitate from the metastable β phase;the strength increases and the ductility decreases,.The alloy is almost composed of coarse α' hexagonal martensite after solution treatment above the β transus,which lead to the decrease in strength and the brittle fracture during tensile test.In terms of different aging temperatures for solution-treated specimens (880 °C/1.5 h/WQ),the main microstructural changes are the precipitation of secondary α phase from the metastable β phase and its growth.Compared with solution-treated specimens,the specimens aged at 300 °C exhibit higher strength and lower ductility,and it can be seen that some secondary α phase and ω phase have precipitated from the β matrix.As the aging temperature increases to 400 °C,the maximum strength as well as minimum ductility is obtained.The specimens aged at 500 °C maintain the maximum strength,while the ductility is improved due to the sufficient diffusion of alloying elements.When the specimens are aged at 550 °C,they possess the optimum balance of strength and ductility.The primary α phase gradually gathers to grow up and the lamellar secondary α phase apparently disperses in the β matrix after aging at 600~700 °C,which lead to the decrease in strength and the increase in ductility.
来源 稀有金属材料与工程 ,2020,49(3):1038-1044 【核心库】
关键词 TC6钛合金 ; 固溶和时效 ; 显微组织 ; 力学性能
地址

中国科学院金属研究所, 辽宁, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1002-185X
学科 金属学与金属工艺
文献收藏号 CSCD:6688022

参考文献 共 16 共1页

1.  Lutjering G. Titanium,2007:23 被引 2    
2.  Banerjee D. Acta Mater,2013,61:844 被引 271    
3.  Li M Q. Mater Charact,2002,49:203 被引 7    
4.  张翥. 钛的金属学和热处理,2009:72 被引 1    
5.  Balasundar I. Mater Sci Eng. A,2017,684:135 被引 7    
6.  Lei X F. Metals,2017,7(4):131 被引 1    
7.  Fujii H. Mater Sci Eng. A,1998,243:103 被引 5    
8.  朱知寿. TC6钛合金棒材热处理工艺研究. 航空材料学报,2004,24:15 被引 6    
9.  陈勋. TC6钛合金加热和冷却过程中的相转变研究. 稀有金属材料与工程,2012,41(12):2123 被引 3    
10.  Tarin P. Materials Science and Engineering A,2008,481:559 被引 3    
11.  李兴无. 淬火温度对Ti-3Al-4.5V-5Mo钛合金形变诱发马氏体的影响. 材料工程,2007(9):3 被引 4    
12.  李兴无. 具有α″马氏体组织的Ti-3Al-4.5V-5Mo钛合金拉伸变形行为. 航空材料学报,2008,28:82 被引 2    
13.  Huang L J. Mater Sci Eng. A,2008,489:330 被引 10    
14.  He D. Mater Des,2014,56:937 被引 9    
15.  Stella P. J Alloy Compd,2013,567:134 被引 4    
16.  赵永庆. 钛合金相变及热处理,2012:106 被引 1    
引证文献 2

1 周璇 固溶和时效对Ti2041合金组织与硬度的影响 稀有金属材料与工程,2021,50(6):2155-2162
被引 0 次

2 海敏娜 热处理对深海耐压壳用Ti542222钛合金厚板组织性能影响研究 稀有金属,2023,47(3):365-372
被引 0 次

显示所有2篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号