Anisotropic Stress Rupture Properties of a 3rd-Generation Nickel-Based Single-Crystal Superalloy at 1100 °C/150 MPa

查看参考文献41篇

Li Yifei 1,2   Wang Li 1   Zhang Gong 1   Qi Dongqing 1   Du Kui 1   Lou Langhong 1  
文摘 The influence of orientation on the stress rupture behaviors of a 3rd-generation nickel-based single-crystal superalloy was investigated at 1100 °C/150 MPa.It is found that the stress rupture anisotropy is shown at 1100 °C, but not so obvious compared with that at intermediate temperatures.The [001] specimens display the longest rupture life, [111] specimens show the shortest rupture life, and [011] specimens exhibit the intermediate life.Detailed observations show that the final fracture is caused by crack initiation and propagation, and the anisotropy of three oriented specimens is related to the fracture modes, γ / γ ʹ microstructures, interfacial dislocation networks and cutting mechanisms in γ ʹ phase.For [001] specimens,N -type rafted structures are formed which can well hinder the slip and climb of dislocations.Besides, the regular interfacial dislocation networks can prevent dislocations from cutting into γ ʹ phase, leading to the improvement of the creep resistance.For [011] specimens, ± 45° rafted structures and irregular networks result in less strain hardening.For [111] specimens, a large number of crack propagation paths and inhomogeneous deformations caused by irregular rafted structures deteriorate the property and result in the shortest life.Furthermore, a [100] superdislocations with low mobility are widely formed in [001] and [011] specimens which suggests the low creep strain rate during steady creep stage, whereas superdislocations in [111] specimens possess high mobility, which indicates the high strain rate and corresponding poor stress rupture property.
来源 Acta Metallurgica Sinica(English Letters) ,2020,33(3):446-458 【核心库】
DOI 10.1007/s40195-019-00931-1
关键词 Single-crystal superalloy ; Stress rupture ; Anisotropy ; Microstructure ; Dislocation
地址

1. Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016  

2. School of Materials Science and Engineering, University of Science and Technology of China, Hefei, 230026

语种 英文
文献类型 研究性论文
ISSN 1006-7191
学科 金属学与金属工艺
基金 国家自然科学基金 ;  国家科技攻关计划项目
文献收藏号 CSCD:6667168

参考文献 共 41 共3页

1.  Reed R C. The Superalloys: Fundaments and Applications,2006 被引 5 次    
2.  Hillier G S. Doctoral Thesis,1984 被引 1 次    
3.  Pollock T M. Acta Metall. Mater,1992,40:1 被引 94 次    
4.  Long H B. J. Alloys Compd,2018,743:203 被引 23 次    
5.  Han J C. Int. J. Rotating Mach,2004,10:443 被引 4 次    
6.  Mackay R A. Metall. Trans. A,1982,13:1747 被引 33 次    
7.  Segersall M. Superalloys,2012:215 被引 1 次    
8.  Chen Q Z. Mater. Sci. Eng., A,2003,356:352 被引 15 次    
9.  Sass V. Acta Mater,1996,44:1967 被引 38 次    
10.  Sass V. Mater. Sci. Eng., A,1998,245:19 被引 27 次    
11.  Liu J L. Mater. Sci. Eng., A,2008,479:277 被引 13 次    
12.  Gabb T P. Mater. Sci. Eng., A,1989,118:59 被引 20 次    
13.  Reed R C. Acta Mater,1999,47:3367 被引 24 次    
14.  Epishin A. Acta Mater,2001,49:4017 被引 14 次    
15.  Zhang J X. Scr. Mater,2003,48:287 被引 42 次    
16.  Zhang J X. Acta Mater,2005,53:4623 被引 70 次    
17.  Epishin A. Philos. Mag,2004,84:1979 被引 18 次    
18.  Zhang J X. Acta Mater,2003,51:5073 被引 25 次    
19.  Sarosi P M. Acta Mater,2007,55:2509 被引 8 次    
20.  Link T. Mater. Sci. Eng., A,2005,405:254 被引 11 次    
引证文献 4 篇

1 史振学 DD15单晶高温合金持久性能各向异性 钢铁研究学报,2021,33(2):168-174
被引 2 次

2 史振学 晶体取向对第四代单晶高温合金DD15高周疲劳性能的影响 航空制造技术,2021,64(1/2):51-56,61
被引 1 次

显示所有4篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护：中国科学院文献情报中心
地址：北京中关村北四环西路33号 邮政编码：100190 联系电话：(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号