镁合金应力腐蚀开裂行为研究进展
Research Progress on Stress Corrosion Cracking Behavior of Magnesium Alloys

查看参考文献65篇

王保杰 1   栾吉瑜 1   王士栋 2,3   许道奎 2,3 *  
文摘 系统总结了镁合金的应力腐蚀开裂行为及其微观失效机制的研究进展,重点介绍了阳极溶解、机械载荷、氢脆效应等对裂纹开裂模式的影响和作用规律,以及提高镁合金抗应力腐蚀开裂能力的处理方法及其作用机制;指出目前研究中存在的问题,并提出未来的研究重点和发展方向。
其他语种文摘 In this paper, the stress corrosion cracking (SCC) behavior of Mg-alloys and the relevant failure mechanism were systematically summarized. Moreover, the effect of anodic dissolution, mechanical loading and hydrogen embrittlement on the SCC cracking modes was described. The measures for improving the SCC resistance of Mg-alloys were also introduced. Finally, the existing problems in the current study, the research emphasis and direction in the future are also pointed out.
来源 中国腐蚀与防护学报 ,2019,39(2):89-95 【核心库】
DOI 10.11902/1005.4537.2018.186
关键词 镁合金 ; 应力腐蚀开裂 ; 局部腐蚀 ; 氢致开裂 ; 腐蚀机制
地址

1. 沈阳理工大学环境与化学工程学院, 沈阳, 110159  

2. 中国科学院金属研究所, 中国科学院核用材料与安全评价重点实验室, 沈阳, 110016  

3. 中国科学院金属研究所环境腐蚀研究中心, 沈阳, 110016

语种 中文
文献类型 研究性论文
ISSN 1005-4537
学科 金属学与金属工艺
基金 国家自然科学基金 ;  沈阳理工大学博士后启动基金
文献收藏号 CSCD:6491509

参考文献 共 65 共4页

1.  褚武扬. 氢脆和应力腐蚀,2013 被引 24    
2.  Choudhary L. Mechanical integrity of magnesium alloys for biomedical applications. Surface Modification of Magnesium and its Alloys for Biomedical Applications. Volume 1: Biological Interactions, Mechanical Properties and Testing,2015:179 被引 1    
3.  Winzer N. A critical review of the stress corrosion cracking (SCC) of magnesium alloys. Adv. Eng. Mater,2005,7:659 被引 19    
4.  Sieradzki K. Brittle behavior of ductile metals during stress-corrosion cracking. Philos. Mag. A,1985,51:95 被引 11    
5.  Parkins R N. Predictive approaches to stress corrosion cracking failure. Corros. Sci,1980,20:147 被引 32    
6.  Winzer N. Characterisation of stress corrosion cracking (SCC) of Mg-Al alloys. Mater. Sci. Eng. A,2008,488:339 被引 10    
7.  Winzer N. Comparison of the linearly increasing stress test and the constant extension rate test in the evaluation of transgranular stress corrosion cracking of magnesium. Mater. Sci. Eng. A,2008,472:97 被引 6    
8.  Winzer N. Fractography of stress corrosion cracking of Mg-Al alloys. Metall. Mater. Trans. A,2008,39:1157 被引 7    
9.  Ben-Hamu G. Stress corrosion cracking of new Mg-Zn-Mn wrought alloys containing Si. Corros. Sci,2008,50:1505 被引 1    
10.  Chen J. Stress corrosion cracking behaviors of AZ91 magnesium alloy in deicer solutions using constant load. Mater. Sci. Eng. A,2009,515:79 被引 5    
11.  Kannan M B. Stress corrosion cracking of rare-earth containing magnesium alloys ZE41, QE22 and Elektron 21 (EV31A) compared with AZ80. Mater. Sci. Eng. A,2008,480:529 被引 9    
12.  Ebtehaj K. The influence of chloride-chromate solution composition on the stress-corrosion cracking of a Mg-Al alloy. Corros. Sci,1988,28:811 被引 3    
13.  Stampella R S. Environmentally-induced cracking of magnesium. Corros. Sci,1984,24:325 被引 7    
14.  Wearmouth W R. Role of stress in the stress corrosion cracking of a Mg-Al alloy. Corrosion,1973,29:251 被引 2    
15.  Chakrapani D G. Transgranular SCC of a Mg-Al alloy: Crystallographic, fractographic and acoustic-emission studies. Metall. Trans. A,1975,6:1155 被引 1    
16.  Chakrapani D G. Hydrogen embrittlement in a Mg-Al alloy. Metall. Trans. A,1976,7:173 被引 2    
17.  Meletis E I. Crystallography of stress corrosion cracking in pure magnesium. Corrosion,1984,40:39 被引 6    
18.  Kannan M B. Pitting-induced hydrogen embrittlement of magnesium-aluminium alloy. Mater. Des,2012,42:321 被引 9    
19.  Curioni M. The behaviour of magnesium during free corrosion and potentiodynamic polarization investigated by real-time hydrogen measurement and optical imaging. Electrochim. Acta,2014,120:284 被引 19    
20.  Singh Raman R K. Corrosion fatigue fracture of magnesium alloys in bioimplant applications: A review. Eng. Fract. Mech,2015,137:97 被引 20    
引证文献 4

1 刘玉项 合金化对镁电化学腐蚀速率影响的研究进展 稀有金属材料与工程,2021,50(1):361-372
被引 9

2 李岩 微弧氧化工艺参数对镁合金表面水滑石复合膜层耐蚀性的影响 表面技术,2021,50(8):327-336
被引 3

显示所有4篇文献

论文科学数据集
PlumX Metrics
相关文献

 作者相关
 关键词相关
 参考文献相关

版权所有 ©2008 中国科学院文献情报中心 制作维护:中国科学院文献情报中心
地址:北京中关村北四环西路33号 邮政编码:100190 联系电话:(010)82627496 E-mail:cscd@mail.las.ac.cn 京ICP备05002861号-4 | 京公网安备11010802043238号